Abstract
Medium Mn steels, one of the most promising 3rd generation advanced high strength steels (AHSS), achieve an encouraging trade-off between the outstanding mechanical property and the production cost. As a typical medium Mn steel, 7Mn steels have superior mechanical property but their poor cross-tension property becomes the Achilles' heel, hindering the application in the automotive industry. The current study focuses on the cross-tension property of the resistance spot weld of 7Mn steel. Generally, martensite is produced in the nugget during the resistance spot welding (RSW). However, the microstructure in the weld nugget can be correspondingly tuned by directly optimizing the welding parameters. With post-weld pulses, in situ tempering occurs, which can decrease the segregation of Mn existing along martensite lath boundaries and facilitate the microstructure transition from martensite to tempered martensite. The tuning on the nugget microstructure facilitates the increase of cross-tension strength (CTS) from 1.5 to 3.7 kN. Although both cases fail in an interfacial fracture mode, a partial ductile fracture is demonstrated in the specimen with post-weld treatment, which is attributed to the occurrence of low-carbon α phase and second phase particles. This study elucidates that the decrease of segregation and the microstructure transition in the nugget are the dominant factor determining the CTS. It is therefore demonstrated that the reduction of Mn segregation and the formation of tempered martensite can increase the weldability of RSW joints of the medium Mn steels.
Similar content being viewed by others
References
Aydin, H., Essadiqi, E., Jung, I. H., & Yue, S. (2013). Development of 3rd generation AHSS with medium Mn content alloying compositions. Materials Science and Engineering: A, 564, 501–508.
Baltazar Hernandez, V. H., Nayak, S. S., & Zhou, Y. (2011). Tempering of martensite in dual-phase steels and its effects on softening behavior. Metallurgical and Materials Transactions A, 42(10), 3115–3129.
Chang, Y., Wang, C. Y., Zhao, K. M., Dong, H., & Yan, J. W. (2016). An introduction to medium-Mn steel: Metallurgy, mechanical properties and warm stamping process. Materials & Design, 94, 424–432.
Chao, Y. J. (2003). Ultimate strength and failure mechanism of resistance spot weld subjected to tensile, shear, or combined tensile/shear loads. Journal of Engineering Materials and Technology, 125(2), 125–132.
Chen, S., Rana, R., Haldar, A., & Ray, R. K. (2017). Current state of Fe-Mn-Al-C low density steels. Progress in Materials Science, 89, 345–391.
Gao, G., Gao, B., Gui, X., Hu, J., He, J., Tan, Z., & Bai, B. (2019a). Correlation between microstructure and yield strength of as-quenched and Q&P steels with different carbon content (0.06–0.42 wt%C). Materials Science and Engineering: A, 753, 1–10.
Gao, Y., Zhao, B., Vlassak, J. J., & Schick, C. (2019b). Nanocalorimetry: Door opened for in situ material characterization under extreme non-equilibrium conditions. Progress in Materials Science, 104, 53–137.
Gould, J. E., Khurana, S. P., & Li, T. (2006). Predictions of microstructures when welding automotive advanced high-strength steels. Welding Journal, 85(5), 111–116.
Han, D. T., Xu, Y. B., Peng, F., Zou, Y., & Misra, R. D. K. (2020). The determining role of pre-annealing on Mn partitioning behavior in medium-Mn-TRIP steel: experimental and numerical simulation. Journal of Materials Science, 55(10), 4437–4452.
Kujanpää, V. P., & David, S. A. (1986). Microsegregation in high-molybdenum austenitic stainless steel laser beam and gas tungsten arc welds. International Congress on Applications of Lasers & Electro-Optics, 1986(S2), 63–69.
Kurz, W., Giovanola, B., & Trivedi, R. (1986). Theory of microstructural development during rapid solidification. Acta Metallurgica, 34(5), 823–830.
Kuziak, R., Kawalla, R., & Waengler, S. (2008). Advanced high strength steels for automotive industry. Archives of Civil and Mechanical Engineering, 8(2), 103–117.
Lee, Y. K., & Han, J. (2015). Current opinion in medium manganese steel. Materials Science and Technology, 31(7), 843–856.
Lesch, C., Kwiaton, N., & Klose, F. B. (2017). Advanced high strength steels (AHSS) for automotive applications-tailored properties by smart microstructural adjustments. Steel Research International, 88(10), 1700210.
Li, S., Yang, S., Lu, Q., Luo, H., & Tao, W. (2019). A novel shim-assisted resistance spot welding process to improve weldability of medium-Mn transformation-induced plasticity steel. Metallurgical and Materials Transactions B, 50(1), 1–9.
Li, Y., Li, W., Liu, W., Wang, X., Hua, X., Liu, H., & Jin, X. (2018). The austenite reversion and co-precipitation behavior of an ultra-low carbon medium manganese quenching-partitioning-tempering steel. Acta Materialia, 146, 126–141.
Park, G., Kim, K., Uhm, S., & Lee, C. (2019). A comparison of cross-tension properties and fracture behavior between similar and dissimilar resistance spot-weldments in medium-Mn TRIP steel. Materials Science and Engineering: A, 752, 206–216.
Pouranvari, M., Aghajani, H., & Ghasemi, A. (2020). Enhanced mechanical properties of martensitic stainless steels resistance spot welds enabled by in situ rapid tempering. Science and Technology of Welding and Joining, 25(2), 119–126.
Pouranvari, M., Asgari, H. R., Mosavizadch, S. M., Marashi, P. H., & Goodarzi, M. (2007). Effect of weld nugget size on overload failure mode of resistance spot welds. Science and Technology of Welding and Joining, 12(3), 217–225.
Pouranvari, M., & Marashi, S. P. H. (2013). Critical review of automotive steels spot welding: Process, structure and properties. Science and Technology of Welding and Joining, 18(5), 361–403.
Pouranvari, M., Sobhani, S., & Goodarzi, F. (2018). Resistance spot welding of MS1200 martensitic advanced high strength steel: Microstructure-properties relationship. Journal of Manufacturing Processes, 31, 867–874.
Saha, D. C., Cho, Y., & Park, Y. D. (2013). Metallographic and fracture characteristics of resistance spot welded TWIP steels. Science and Technology of Welding and Joining, 18(8), 711–720.
Sajjadi-Nikoo, S., Pouranvari, M., Abedi, A., & Ghaderi, A. A. (2018). In situ postweld heat treatment of transformation induced plasticity steel resistance spot welds. Science and Technology of Welding and Joining, 23(1), 71–78.
Sawanishi, C., Ogura, T., Taniguchi, K., Ikeda, R., Oi, K., Yasuda, K., & Hirose, A. (2014). Mechanical properties and microstructures of resistance spot welded DP980 steel joints using pulsed current pattern. Science and Technology of Welding and Joining, 19(1), 52–59.
Seo, C. H., Kwon, K. H., Choi, K., Kim, K. H., Kwak, J. H., Lee, S., & Kim, N. J. (2012). Deformation behavior of ferrite-austenite duplex lightweight Fe-Mn-Al-C steel. Scripta Materialia, 66(8), 519–522.
Shirmohammadi, D., Movahedi, M., & Pouranvari, M. (2017). Resistance spot welding of martensitic stainless steel: Effect of initial base metal microstructure on weld microstructure and mechanical performance. Materials Science and Engineering: A, 703, 154–161.
Shterner, V., Molotnikov, A., Timokhina, I., Estrin, Y., & Beladi, H. (2014). A constitutive model of the deformation behaviour of twinning induced plasticity (TWIP) steel at different temperatures. Materials Science and Engineering: A, 613, 224–231.
Stadler, M., Gruber, M., Schnitzer, R., & Hofer, C. (2020). Microstructural characterization of a double pulse resistance spot welded 1200 MPa TBF steel. Welding in the World, 64(2), 335–343.
Uijl, N., Smith S., & Moolevliet, T. (2008). Failure modes of resistance spot welded advanced high strength steels (pp. 78–104).
Wang, Y., Ding, K., Zhao, B., Zhang, Y., Wu, G., Wei, T., Pan, H., & Gao, Y. (2020). Highly enhanced cross tensile strength of the resistance spot welded medium manganese steel by optimized post-heating pulse. In TMS 2020 149th annual meeting & exhibition supplemental proceedings (pp. 1871–1880).
Wei, P. S., & Wu, T. H. (2014). Electrode geometry effects on microstructure determined by heat transfer and solidification rate during resistance spot welding. International Journal of Heat and Mass Transfer, 79, 408–416.
Yang, F., Luo, H., Hu, C., Pu, E., & Dong, H. (2017). Effects of intercritical annealing process on microstructures and tensile properties of cold-rolled 7Mn steel. Materials Science and Engineering: A, 685, 115–122.
Zhao, C., Zhang, C., Cao, W., & Yang, Z. (2016). Variation in retained austenite content and mechanical properties of 0.2C–7Mn steel after intercritical annealing. International Journal of Minerals, Metallurgy, and Materials, 23(2), 161–167.
Zou, D. Q., Li, S. H., He, J., Gu, B., & Li, Y. F. (2018). The deformation induced martensitic transformation and mechanical behavior of quenching and partitioning steels under complex loading process. Materials Science and Engineering: A, 715, 243–256.
Acknowledgements
This work was supported by the National Natural Science Foundation of China (Grant no. U1760102), Independent Research Project of State Key Laboratory of Advanced Special Steel and Shanghai Key Laboratory of Advanced Ferrometallurgy (Shanghai University, Grant no. 19DZ2270200), the State Key Laboratory of Development and Application Technology of Automotive Steels (Baosteel Group, Grant no. Y17ECEQ05Y).
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
The authors declare that they have no conflict of interest.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Zhao, B., Wang, Y., Ding, K. et al. Enhanced Cross-Tension Property of the Resistance Spot Welded Medium-Mn Steel by In Situ Microstructure Tailoring. Int J Steel Struct 21, 666–675 (2021). https://doi.org/10.1007/s13296-021-00464-3
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13296-021-00464-3