Abstract
Thick high-strength low-alloy (HSLA) steel plates with excellent large heat input welding properties are increasingly demanded to build super-large container ships for the globally flourishing marine trade. This article describes the effect of Ca content on the TiN particles, microstructure and impact toughness of the simulated coarse-grained heat-affected zone (CGHAZ) in HSLA steels after large heat input welding at 400 kJ/cm. The quantitative analyses on TiN particles demonstrate that the number densities of the submicron- and nano-scale particles increase with increasing Ca content, but the particle sizes appear to be independent of the Ca content. The prior austenite grains in the CGHAZs of the HSLA steels are comparably coarse, including a small number of extremely large grains, except for 25Ca steel, whose grains are relatively fine and uniform. Moreover, only the impact toughness of the CGHAZ in 25Ca steel is satisfactorily improved with a small test variability, and this could be attributed to the improved precipitation of the submicron-scale TiN particles that effectively refine the grains. Based on the experimental and thermodynamic results, it is strongly recommended to increase the Ca content to > 0.0019 wt pct for the related HSLA steel system in the future steel optimization.
Similar content being viewed by others
References
H. Shirahata, T. Okawa, K. Nakashima, K. Yanagita, T. Inoue, A. Inami, K. Ishida, M. Minagawa, and Y. Funatsu: Nippon Steel & Sumitomo Metal Tech. Rep., 2015, vol. 110, pp. 25–29.
[2] R. Cao, J. Li, D.S. Liu, J.Y. Ma, J.H. Chen: Metall. Mater. Trans. A, 2015, vol. 46A, pp. 2999-3014.
[3] B. Hutchinson, J. Komenda, G.S. Rohrer, H. Beladi: Acta Mater., 2015, vol. 97, pp. 380-91.
[4] Z.H. Xiong, S.L. Liu, X.M. Wang, C.J. Shang, X.C. Li, R.D.K. Misra: Mater. Sci. Eng. A, 2015, vol. 636, pp. 117-23.
[5] L.Y. Xu, J. Yang, R.Z. Wang, Y.N. Wang, W.L. Wang: Metall. Mater. Trans. A, 2016, vol. 47A, pp. 3354-64.
[6] D. Loder, S.K. Michelic, A. Mayerhofer, C. Bernhard: Metall. Mater. Trans. B, 2017, vol. 48B, pp. 1992-2006.
[7] L.Y. Xu, J. Yang, R.Z. Wang, W.L. Wang, Y.N. Wang: J. Iron Steel Res. Int., 2018, vol. 25, pp. 433-41.
[8] L.Y. Xu, J. Yang, R.Z. Wang, W.L. Wang, Z.M. Ren: Steel Res. Int., 2017, vol. 88, pp. 1700157.
[9] C. Wang, R.D.K. Misra, M.H. Shi, P.Y. Zhang, Z.D. Wang, F.X. Zhu, G.D. Wang: Mater. Sci. Eng. A, 2014, vol. 594, pp. 218-28.
[10] K. Yamamoto, T. Hasegawa, J.-i. Takamura: ISIJ Int., 1996, vol. 36, pp. 80-86.
[11] Y. Kasamatsu, S. Takashima, T. Hosoya: Tetsu-to-Hagane, 1979, vol. 65, pp. 1232-41.
[12] S. Kanazawa, A. Nakashima, K. Okamoto, K. Kanaya: Tetsu-to-Hagane, 1975, vol. 61, pp. 2589-603.
[13] Y. Zhang, X.B. Li, H. Ma: Metall. Mater. Trans. B, 2016, vol. 47B, pp. 2148-56.
[14] K.-s. Bang, C. Park, S. Liu: J. Mater. Sci., 2006, vol. 41, pp. 5994-6000.
[15] Y. Kitani, R. Ikeda, K. Yasuda, K. Oi, K. Ichimiya: Weld. World, 2007, vol. 51, pp. 31-36.
T. Kato, S. Sato, H. Ohta, and T. Shiwaku: Kobelco Technol. Rev., 2011, vol. 30, pp. 76–79.
[17] M. Wang, H.Y. Sun, M.P. Phaniraj, H.N. Han, J. Jang, Z.J. Zhou: Mater. Sci. Eng. A, 2016, vol. 672, pp. 23-31.
[18] J. Moon, C. Lee, S. Uhm, J. Lee: Acta Mater., 2006, vol. 54, pp. 1053-61.
[19] P.A. Manohar, M. Ferry, T. Chandra: ISIJ Int., 1998, vol. 38, pp. 913-24.
[20] M. Chapa, S.F. Medina, V. López, B. Fernández: ISIJ Int., 2002, vol. 42, pp. 1288-96.
[21] Q.F. Wang, C.Y. Zhang, R.X. Li, J.Z. Gao, M.Z. Wang, F.C. Zhang: Mater. Sci. Eng. A, 2013, vol. 559, pp. 130-34.
[22] Y.H. Zhang, J. Yang, L.Y. Xu, Y.L. Qiu, G.G. Cheng, M.Y. Yao, J.X. Dong: Metals, 2019, vol. 9, pp. 1328.
[23] X.L. Wang, Z.Q. Wang, L.L. Dong, C.J. Shang, X.P. Ma, S.V. Subramanian: Mater. Sci. Eng. A, 2017, vol. 704, pp. 448-58.
Acknowledgments
This work was financially supported by the National Natural Science Foundation of China (Grant Nos. U1960202 and 51801118). The authors are grateful to X.F. Jiang, R.Z. Wang and Y.N. Wang for the assistance in steelmaking and TMCP treatment.
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Manuscript submitted July 27, 2020; Accepted November 5, 2020.
Rights and permissions
About this article
Cite this article
Zhang, Y., Yang, J., Liu, D. et al. Improvement of Impact Toughness of the Welding Heat-Affected Zone in High-Strength Low-Alloy Steels through Ca Deoxidation. Metall Mater Trans A 52, 668–679 (2021). https://doi.org/10.1007/s11661-020-06105-4
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11661-020-06105-4