High-Temperature Oxidation Behavior of a Cu-Bearing 17Cr Ferritic Stainless Steel

Zhang, Mengqi; Han, Ying; Zu, Guoqing; Sun, Jiapeng; Zhu, Weiwei; Chen, Hua; Ran, Xu

doi:https://doi.org/10.1155/2020/8847831

Scanning

On this page

Abstract Introduction Materials and Methods Results and Discussion Conclusions Data Availability Conflicts of Interest Acknowledgments References Copyright Related Articles

Special Issue

Characterization of the Corroding Interface using Scanning Techniques

View this Special Issue

Research Article | Open Access

Volume 2020 | Article ID 8847831 | https://doi.org/10.1155/2020/8847831

High-Temperature Oxidation Behavior of a Cu-Bearing 17Cr Ferritic Stainless Steel

Mengqi Zhang,¹Ying Han,¹Guoqing Zu,¹Jiapeng Sun,²Weiwei Zhu,¹Hua Chen,¹and Xu Ran¹

Academic Editor: Jian Chen

Received17 Sept 2020

Revised13 Nov 2020

Accepted25 Nov 2020

Published16 Dec 2020

Abstract

The isothermal oxidation behavior of 17Cr-0.85Si-0.5Nb-1.2Cu ferritic stainless steel in air was studied from 850°C to 1050°C by analyzing its weight gain after oxidation. The kinetic curves were plotted using the oxidation weight-gain data, and the structure, surface morphology, and element distribution of the oxide films were analyzed by XRD, SEM, and EDS. The results showed that the oxidation kinetics curves at 850°C and 950°C followed a parabolic law, and a continuous and dense oxide film composed of Cr₂O₃ and MnCr₂O₄, FeCr₂O₄, and Cu-Cr rich spinel was formed, which reveals that the steel displayed good oxidation resistance. When the temperature was increased to 1050°C, the oxidation kinetics curves gradually changed from parabolic to linear after 40 h exposure, which indicated that the oxidation resistance significantly worsened. A lower oxidation resistance was observed at 1050°C due to the formation of a large amount of Fe₂O₃ on the surface and the volatilization of the inner Cr₂O₃ layer.

1. Introduction

The materials used in automotive exhaust systems require high strength, good oxidation resistance, and satisfactory corrosion resistance because they are working in complex environments where includes cyclic oxidation and condensate corrosion [1–4]. Austenitic stainless steels are widely used to manufacture the hot-end parts of automobile exhaust systems, but in recent years, they have been gradually replaced by ferritic stainless steels due to their lower cost, smaller thermal expansion, and better high-temperature strength. Ferritic stainless steels have become one of the most promising candidates for use in exhaust manifolds [5–8].

As a relatively cheap alloying element, Cu added to Nb-bearing ferritic stainless steels are expected to greatly improve both strength and corrosion resistance; thus, Cu-Nb alloyed ferritic stainless steels have received great attention as a potential material for the hot-end parts of automotive exhaust systems [9–13]. For example, Kobayashi et al. [9, 10] investigated the effect of Nb addition on the aging precipitation behavior of 18%Cr-1.5%Cu ferritic stainless steel and proved that solute Nb atoms delayed the formation of Cu-rich regions and the coarsening of Cu particles in the steel. Ota et al. [11] studied the thermal fatigue properties of 15%-21% Cr ferritic stainless steel with various Cu and Nb contents. Guo et al. [12] reported that the combination of Cu and Nb improved the corrosion resistance of ferritic stainless steel in sulfuric acid solution.

High-temperature oxidation resistance is one of the important indicators for evaluating the performance of automotive exhaust pipe materials. Moreover, improving the oxidation property is significant to expand the application range for ferritic stainless steels after all. Sun et al. [14] studied the high-temperature cyclic oxidation behavior of 1Cr17 ferritic stainless steel in air and found the oxidation kinetic curves followed a parabolic law. Wei et al. [2] reported the influence of W and Ce on the oxidation behavior of ferritic stainless steel at 950-1100°C and indicated that the addition of W and Ce improved the density and adhesion of the oxide film, which increased the oxidation resistance. However, when the amount of W exceeded 1.0 wt.%, exfoliation of the oxide film was accelerated, leading to an increased oxidation rate. In addition, Chen et al. [15] investigated the oxidation of 441 ferritic stainless steel at 900-1050°C under a simulating automobile exhaust condition, and the results showed that the maximum service temperature is about 900°C, and the oxide film displayed a stratified structure comprised of a Mn-Cr spinel layer and a Cr₂O₃ layer. However, studies focusing on the oxidation mechanism of Cu-Nb alloyed ferritic stainless steel at high temperatures have not been reported yet. Thus, in this work, the high-temperature oxidation behavior of 17Cr-0.85Si-0.5Nb-1.2Cu ferritic stainless steel, a candidate material for automotive exhaust manifolds, was studied at 850°C, 950°C, and 1050°C in air, and the corresponding oxidation mechanism was proposed.

2. Materials and Methods

The material used in this work was 17Cr-0.85Si-0.5Nb-1.2Cu ferritic stainless steel, and the chemical composition is shown in Table 1. The steel was first hot-rolled to 10 mm and then annealed at 1100°C for 30 min, followed by water cooling. After that, specimens with sizes of for the oxidation experiments were polished with SiC water-abrasive papers up to 1200 grit, washed with ethanol, and dried in a vacuum drying oven at 150°C.

Specimens that calcined to a constant weight were placed in the alumina crucibles, respectively, and stood against the inner wall of the crucible at a certain angle to ensure complete contact with air during the experiment. A box-type resistance heating furnace was used to perform continuous isothermal oxidation tests at 850°C, 950°C, and 1050°C, for 5 h, 12 h, 20 h, 40 h, 70 h, 100 h, and 140 h. Cover each crucible with a pot immediately after taking it out to avoid errors that might cause by the oxide film falling out during the cooling process. Each crucible and specimen group was weighed after air cooling, and the weight changes and oxidation rates were calculated to plot the oxidation kinetics curves. The composition of the oxide film was analyzed by X-ray diffraction (XRD, D-MAXIIA), with a scanning range of 20°-100°, with a Cu K_a radiation source and parameters of 40 kV and 40 mA. The surface and cross-section morphology and elemental composition of the oxide scale were analyzed by scanning electron microscopy (SEM, Gemini supra40) equipped with energy-dispersive X-ray spectroscopy (EDS).

3. Results and Discussion

3.1. Microstructure of Specimens

An optical micrograph of the steel after annealing at 1100°C for 30 min is shown in Figure 1(a), which reveals a typical equiaxed ferritic structure. The average grain size was measured to be , and a small number of precipitated particles were observed in the grains and at the grain boundaries (Figure 1(b)). These precipitated particles were analyzed by EDS, and the results are shown in Figure 1(c). It indicates that these precipitates were residual Nb-containing compounds which have been reported by many references [16–21].

(a)

(b)

(c)

3.2. Oxidation Kinetics

Figure 2 shows the oxidation weight gain curves of the studied steel at different temperatures. The weight gain gradually increased as the test temperature increased. At 850°C and 950°C, the weight gain curves followed a parabolic law, which indicated that the oxidation reaction was mainly controlled by elemental diffusion [22, 23]. Generally, Equation (1) can be used to describe the parabolic oxidation kinetics and is defined as [24]: where is the oxidation weight gain in mg cm^-2, is the oxidation rate constant in mg² cm^-4 s^-1, and is the oxidation time in s. As we all know, the premise of the parabolic law is that there are no defects in the oxide film or at the oxide/matrix interface. However, after long-term oxidation during actual oxidation tests, cracks and other defects may form in the oxide scale, which will cause the oxidation kinetics law to deviate from the classic parabolic law. Therefore, the formula above can be modified as [16, 20]: where is the index of oxidation and the value of is determined by the mass gain per unit area and oxidation time. Generally, a larger value of indicates a higher growth rate of oxidation film [25–27]. The oxidation kinetics equations of the experimental steel at 850°C and 950°C obtained from Equation (2) are:

In these two equations, indicates the formation of a loose oxide film, while the thickness of the oxide film did not increase proportionally to the element diffusion [28]. However, the oxidation still followed a parabolic law, indicating that the oxide film was protective at this time. Since , the oxidation resistance of the steel at 850°C was better than at 950°C, and the average oxidation rates at these two temperatures were and , respectively.

At 1050°C, the oxidation weight gain curve of the studied steel was segmented, and the curve displayed a parabolic shape in the first 40 h and then became linear from 40 h to 140 h, which shows that the oxidation resistance of the steel decreased rapidly. The oxidation kinetics process can be expressed by Equation (5):

When the oxidation time was less than 40 h at 1050°C, the value was 0.19, which is 2.7 and 6.5 times higher than those obtained at 850°C and 950°C, respectively. Although the oxide film was still protective at this time, the overall oxidation resistance was significantly lowered compared to that at lower temperatures. When the oxidation time exceeded 40 h, the oxidation kinetics obeyed a linear law, and the oxidation rate was no longer controlled by diffusion processes in the oxide film but instead depended on the chemical reaction. At this stage, severe macroscopic peeling of the oxide film occurred, and the matrix was not completely covered, which sharply decreased the oxidation resistance of the steel [23, 29]. When the oxidation time reached 140 h at 1050°C, the weight gain was 3.16 mg/cm², and the average oxidation rate was .

3.3. Characterization and Analysis of Oxide Films

3.3.1. Morphology and Surface Composition of Oxide Films

The surface morphology of the studied steel after oxidation at 850°C for different times is shown in Figure 3, and the compositions of these oxides were further analyzed by EDS (Table 2). In the first 5 h (Figure 3(a)), surface scratches were apparent, indicating that the oxide film was very thin and the oxidation had just begun. At this time, the oxides were small cubes and bubble-like shapes (Figures 3(b) and 3(c)). The cubic oxides (A₁) contained Cr, O, and a small amount of Cu, region A₂ contained Cr, O, Fe, and Si, and the bubble-like particles in region A₄ were identified as Cr₂O₃. No scratches were observed on the surface after 20 h oxidation (Figure 3(d)), and the size and quantity of the bubbly oxides on the surface increased and widely covered the thin cubic oxide film. In some areas, the bubble-like Cr₂O₃ oxides gradually merged (A₄ in Figure 3(e)). Sparse large agglomerates and flocculent oxides (A₅ in Figure 3(f)) which contained Cr, Fe, and Cu were also observed. The oxide film was even and compact after 70 h oxidation at 850°C, and a dense spinel oxide layer formed (Figures 3(g) and 3(h)). In addition to the cubic and a low amount of bubbly oxides, thin needle-like oxides (A₈ in Figure 3(i)) also appeared. The cubic oxide films in these areas showed signs of fusion, and their geometric characteristics were not obvious. In Figure 3(h), two different oxides, A₆ and A₇, contained Cr, O, and Mn, and the cubic oxides (A₆) contained more Mn, indicating that they were a spinel phase that contained Cr and Mn [30]. Area A₈ mainly consisted of Cr, O, and a small quantity of Fe, Mn, and Cu. When the oxidation time was lengthened to 140 h (Figures 3(j) and 3(k)), the oxide film became rougher, and some areas collapsed after cooling. Many large spinel particles were produced (Figure 3(l)), with many granular oxides (A₁₀) between them which were composed of Cr₂O₃, while the large layered cubic spinel oxides (A₉) were mainly composed of Cr and Cu.

(a)

(b)

(c)

(d)

(e)

(f)

(g)

(h)

(i)

(j)

(k)

(l)

Figure 4 shows the surface morphology of the studied steel at 950°C and 1050°C after oxidation for 140 h in air. The surface oxide scales fell off to some degree when the time progressed to 140 h at both temperatures. It can be seen from Figure 4(a) that when the temperature was 950°C, the thickness of oxide scale was increased, and a pit-like morphology (mainly composed of Fe, Cr, Si, and O by EDS analysis) appeared in the area which experienced oxide film spallation. After oxidation at 1050°C, significant scale spalling was observed (Figure 4(b)). The remaining part of the oxide had a warped edge and was poorly attached to the substrate, indicating a significantly lower oxidation resistance. EDS results showed that the composition of the exfoliated area was oxides containing Mn, Cr, and Cu.

(a)

(b)

3.3.2. Phase Analysis of Oxide Films

Figure 5 presents the XRD patterns of the oxide films obtained at different temperatures for 140 h. The oxidation products were similar and were mainly composed of Fe-Cr, Cr₂O₃, Fe₂O₃, Mn₃O₄, MnCr₂O₄, and FeCr₂O₄. But the intensities were different, indicating different phase content and/or thickness. The peaks of spinel Cu-Cr were not detected in the patterns, because their content was too low to be detected. At 1050°C, CuMn₂O₄ and more Fe₂O₃ appeared, compared to that at lower temperatures. The above results are both consistent with the EDS analysis. In addition, it can be found that as the temperature increased, the Cr₂O₃ content continued to decrease due to the further oxidation of Cr₂O₃ at high temperatures, which resulted in the formation of volatile CrO₃. According to a previous report [31], this reaction proceeds very rapidly above 950°C, which is why Cr₂O₃ showed a low peak intensity at 1050°C. The XRD patterns also showed that the Fe-Cr peaks were heightened at higher temperatures, which could be due to severe peeling of the oxide film, which exposed more of the matrix.

3.3.3. The Cross-Sectional Morphology of Oxide Scales

The cross-sectional morphology of the studied steel oxidized at 950°C and 1050°C for different times is shown in Figures 6 and 7, respectively. The changes in the distribution and concentration of O, Cr, Fe, Cu, Si, Nb, and Mn were detected. It can be seen from the figures that the oxygen content increased from the surface of the oxide film to the alloy substrate, and this indicated that the film at the interface of the substrate was denser than the surface oxide [1].

(a)

(b)

(a)

(b)

It can be seen from Figure 6(a) that when oxidized at 950°C for 12 h, the oxide film was still in the preliminary formation stage with a thickness of about 13.74 μm. Mn was evenly distributed throughout the entire oxide layer, but the Cr content was greater at the oxide/steel interface. A tiny amount of Cu was observed in the outer oxide layer, while nearly no Fe and Nb were detected. Moreover, some Si-rich oxides distributed sporadically near the scale/steel interface. When the oxidation time was prolonged to 100 h (Figure 6(b)), the thickness of the oxide film increased to 19.28 μm. Meanwhile, Fe began to gather near the oxide/metal interface, but Fe-rich oxides were not formed continuously or densely. A small amount of Cu was observed near the outermost side of the oxide scale, which may be related to the formation of Cu-Cr spinel oxide.

The cross-sectional element distribution of the oxide films after different oxidation times at 1050°C is shown in Figure 7. As the temperature increased, the oxide film gradually thickened and reached 18.75 μm after 12 h (Figure 7(a)), and the elemental distribution was significantly different from the specimen exposed at 950°C. Si-rich oxides were distributed near the matrix continuously, while some Nb accumulation was scattered around them. A Fe-rich oxide layer was formed above the original Cr-rich scale, and the Cr-rich layer was thinner compared with that at 950°C. The concentration of Fe throughout the entire oxide film was significantly higher than that at 950°C, indicating that Fe diffused through the oxide film and reacted with oxygen. Mn was distributed evenly throughout the oxide film, and its concentration decreased further away from the outer layer. When the exposure time reached 100 h (Figure 7(b)), the outermost layer was a thick Fe-rich oxide, and the layer underneath was a Cr-rich oxide which was thicker than the one formed at 12 h. Large cavities also appeared in the inner Cr-rich layer, which might have resulted in the outward diffusion and oxidation of Fe at the scale surface. Therefore, it can be inferred that after being oxidized at 1050°C for 100 h, the oxide film was stratiform, and the outer layer of the scale was composed of Fe₂O₃ and a tiny amount of discrete CuMn₂O₄. The middle layer was composed of Cr₂O₃ together with Mn-rich spinel oxides, and the innermost layer was SiO₂.

3.4. Oxidation Mechanism

3.4.1. Oxidation Mechanism at 850°C and 950°C

According to thermodynamic theory, the affinity between oxygen and other elements in an alloy follows the order of Si > Nb > Mn > Cr > Fe > Cu [2, 25, 28, 32]. During the initial oxidation stage, Si and Nb are supposed to be first oxidized at the oxide/steel interface due to their higher diffusion coefficient and oxygen affinity in steel. However, there was a strong competition between Si and Nb for the interfacial oxidation [32]. Also, since the supply amount of Si atoms was much greater than that of Nb, NbO₂ was difficult to form. This result corresponds to the result of X-ray diffraction, that is, no NbO₂ was detected. The formed SiO₂ layer was thin, porous, and discontinuous at this temperature; therefore, Cr and Mn began to diffuse outward through the SiO₂ layer to generate Cr₂O₃ and MnO, respectively. As the oxidation time increased, a denser and more continuous protective Cr₂O₃ layer was formed, while Fe began to diffuse from the metal to the middle oxide layer to form FeO. However, the protective Cr₂O₃ layer acted as a barrier to Fe diffusion to the surface of the oxide film, and FeO and MnO reacted with Cr₂O₃, respectively, under the Cr₂O₃ layer and at the outermost oxide film surface to generate spinel oxides through the following reactions:

In addition, a small amount of Cu migrated to the out layer of the oxide scale and reacted with Cr to form spinel oxides after longer exposure times. These spinel oxides formed on the surface were a compact barrier for the inward diffusion of O, reducing the growth of the oxide scale and acting as protective layers against oxidation [23, 33, 34].

3.4.2. Oxidation Mechanism at 1050°C

The oxidation rate of the studied steel increased significantly with increasing temperature. Si and Nb were oxidized during the initial oxidation period at 1050°C. And there are some differences from the low-temperature oxidation at 850°C −950°C. First of all, some sporadic Nb accumulation could be found. This is consistent with the finding of previous study, that is, when the content of Si in the steel is more than 0.5 wt.%, no Nb oxide aggregation layer will be formed [35]. Ali-Löytty et al. [16] also believed that the Nb-rich intermetallic precipitates remove free Nb from the alloy solution and thus made it difficult to form Nb-rich oxide layer. Therefore, based on the previous research conclusions and the phenomena observed in this experiment, we speculate that when the Si content is 0.85 wt.%, the oxidation of Nb has been severely suppressed, so the influence of Nb oxides will not be discussed here. Secondly, Si formed a continuous and dense thin oxide layer at the oxide/metal interface. It is known that Si-rich oxides are stable and protective at high temperatures [27, 36], yet a previous study [37] also found that it does not provide the highest oxidation resistance when a continuous Si oxide layer is formed at the steel/chromium interface. In contrast, it is better to obtain good oxidation resistance when a discontinuous Si oxide layer is formed at and below the interface with silica particles because Si does not act as a barrier for Cr diffusion to the chromium layer but rather prevents the diffusion of Cr from the matrix to the interface. Cr₂O₃ is also unstable at high temperatures, especially above 950°C, and easily reacts with oxygen to form volatile CrO₃, which leads to the depletion of protective chromium oxides via the following reaction [25, 31, 38, 39]:

When the average Cr content of the steel was lower than the critical concentration, the matrix Fe began to oxidize. Nodular oxides formed when Fe began to diffuse along the oxide layers and oxidized outward, which made the Cr₂O₃ film unstable, thereby causing more severe oxidation [40]. From Figure 7, it can be seen that Fe rapidly diffused through the inner scale, and oxidation occurred in the upper and middle oxide layers which were originally Cr₂O₃. Once the Fe-rich oxides which had faster oxidation rate began to form, no more dense protective chromium-rich oxide scale will be formed on the outermost surface. However, the Fe-rich oxide layer was loose and not protective, which provided more paths for the diffusion of Fe, O, Cr, and Mn [31]. It can also be observed in Figure 7(a) that the Fe-rich oxide had a bilayer structure whose outer layer was Fe₂O₃, and the inner was Fe-Cr oxides, but they were not dense enough to impede the outward diffusion of ions. Moreover, due to the different Pilling-Bedworth ratios of these oxides, cracks also formed due to growth stress [41, 42]. The above reasons eventually led to the failure of the oxide scale at 1050°C. Some Cu-rich and Mn-rich oxides were also distributed on the outermost side of the oxide film when the exposure time was extended to 100 h. It was estimated that few CuMn₂O₄ and MnFe₂O₄ spinel oxides were formed. Previous studies have shown that when a Cu-rich phase segregates at the scale-matrix interface, it can hinder the inward diffusion of oxygen, thereby improving the oxidation resistance [43], but this phenomenon was not observed in this study. In addition, another research showed that Cu-Mn spinel oxides are good barrier to the diffusion of Cr [44–46]. However, since the nonprotective Fe₂O₃ dominated the outermost film, spinel oxides did not form a strong protective continuous dense layer, and the oxidation rate of the experimental steel increased linearly.

4. Conclusions

The isothermal oxidation behavior of 17Cr-0.85Si-0.5Nb-1.2Cu ferritic stainless steel at 850°C, 950°C, and 1050°C in air was studied, and the following conclusions were obtained: (1)The oxidation rate increased with the increasing temperature. The oxidation kinetics curves conformed to the parabolic law at 850°C and 950°C, while the kinetics curve followed a parabolic-linear rule at 1050°C(2)At 850°C and 950°C, a small amount of oxide film peeled off. The oxide film was composed of a small amount of SiO₂ and continuous and dense Cr₂O₃, FeCr₂O₄, and Cr-Mn spinel oxides. The composition of the oxide film was sufficiently stable to protect the matrix from further acute oxidation(3)The spallation of the oxide scale became more severe when the exposure time increased to 40 h at 1050°C. The severe volatilization of Cr₂O₃ and the enrichment of nonprotective Fe-rich oxides on the surface rapidly decrease the oxidation resistance at this high temperature

Data Availability

The raw/processed data required to reproduce these findings cannot be shared at this time as the data also forms part of an ongoing study.

Conflicts of Interest

The authors declare that they have no conflicts of interest.

Acknowledgments

This work is supported by the National Natural Science Foundation of China (No. 51604034 and 51974032), the Science and Technology Project of Jilin Education Department in 13th Five–Year (No. JJKH20181008KJ), and the Science and Technology Development Program of Jilin Province (No. 20190302003GX).

References

L. L. Wei, “An investigation on high temperature oxidation resistance of medium-chromium alloyed ferritic stainless steel,” Tech. Rep., Northeastern Univ. Tech. Thesis, 2016.
View at: Google Scholar
L. L. Wei, J. H. Zheng, L. Q. Chen, and R. D. K. Misra, “High temperature oxidation behavior of ferritic stainless steel containing W and Ce,” Corrosion Science, vol. 142, pp. 79–92, 2018.
View at: Publisher Site | Google Scholar
G. M. Sim, J. C. Ahn, S. C. Hong, K. J. Lee, and K. S. Lee, “Effect of Nb precipitate coarsening on the high temperature strength in Nb containing ferritic stainless steels,” Materials Science and Engineering, vol. 396, no. 1-2, pp. 159–165, 2005.
View at: Publisher Site | Google Scholar
Y. Qiao, Z. Tian, X. Cai et al., “Cavitation erosion behaviors of a nickel-free high-nitrogen stainless steel,” Tribology Letters, vol. 67, no. 1, 2018.
View at: Google Scholar
Y. Inoue and M. Kikuchi, “Present and future trends of stainless steel for automotive exhaust system,” Nippon Steel Technical Report, vol. 88, pp. 62–69, 2003.
View at: Google Scholar
A. M. Huntz, A. Reckmann, C. Haut et al., “Oxidation of AISI 304 and AISI 439 stainless steels,” Materials Science and Engineering, vol. 447, no. 1-2, pp. 266–276, 2007.
View at: Publisher Site | Google Scholar
Y. Han, J. Q. Sun, Y. Sun, J. P. Sun, and X. Ran, “Tensile properties and microstructural evolution of an Al-bearing ferritic stainless steel at elevated temperatures,” Metals, vol. 10, no. 1, p. 86, 2020.
View at: Publisher Site | Google Scholar
Y. M. L. Y. Shao and C. X. Liu, “Annealing process optimization of high frequency longitudinal resistance welded low-carbon ferritic stainless steel pipe,” Acta Metallurgica Sinica, vol. 55, no. 11, pp. 1367–1378, 2019.
View at: Google Scholar
S. Kobayashi, T. Takeda, N. Kanno, Y. Inoue, K. Nakai, and T. Sakamoto, “Effect of Nb addition on the growth and coarsening of Cu-particles in ferritic stainless steel,” ISIJ International, vol. 54, no. 7, pp. 1697–1704, 2014.
View at: Publisher Site | Google Scholar
S. Kobayashi, T. Takeda, K. Nakai, N. Kanno, and T. Sakamoto, “Effect of Nb addition on Cu precipitation in ferritic stainless steel,” ISIJ International, vol. 51, no. 4, pp. 657–662, 2011.
View at: Google Scholar
H. Ota, T. Nakamura, and K. Maruyama, “Effect of solute atoms on thermal fatigue properties in ferritic stainless steels,” Materials Science and Engineering, vol. 586, pp. 133–141, 2013.
View at: Publisher Site | Google Scholar
J. J. Guo and M. S. N. Sato, “Electrochemical behavior and surface composition of ferritic stainless steels containing Cu and Nb in sulfuric acid solution,” Journal of Chinese Society for Corrosion and Protection, vol. 10, no. 3, pp. 239–244, 1990.
View at: Google Scholar
X. Li, L. Shi, Y. Liu, K. Gan, and C. Liu, “Achieving a desirable combination of mechanical properties in HSLA steel through step quenching,” Materials Science and Engineering: A, vol. 772, article 138683, 2020.
View at: Publisher Site | Google Scholar
B. Sun, S. R. Wang, and Y. J. Wang, “Cyclic oxidation behavior of ferrite stainless steel at high temperature,” Hot Working Technology, vol. 41, no. 4, pp. 43–48, 2012.
View at: Google Scholar
Y. S. Chen, “High temperature oxidation behavior of ferritic stainless steel for hot end of exhaust system,” Tech. Rep., Shanghai Univ. Tech. Thesis, 2019.
View at: Google Scholar
H. Ali-Löytty, P. Jussila, and M. Valden, “Optimization of the electrical properties of Ti–Nb stabilized ferritic stainless steel SOFC interconnect alloy upon high-temperature oxidation: the role of excess Nb on the interfacial oxidation at the oxide–metal interface,” International Journal of Hydrogen Energy, vol. 38, no. 2, pp. 1039–1051, 2013.
View at: Publisher Site | Google Scholar
H. Ali-Löytty, P. Jussila, T. Juuti, L. P. Karjalainen, A. A. Zakharov, and M. Valden, “Influence of precipitation on initial high-temperature oxidation of Ti–Nb stabilized ferritic stainless steel SOFC interconnect alloy,” International Journal of Hydrogen Energy, vol. 37, no. 19, pp. 14528–14535, 2012.
View at: Publisher Site | Google Scholar
H. S. Seo, D. W. Yun, and K. Y. Kim, “Oxidation behavior of ferritic stainless steel containing Nb, Nb–Si and Nb–Ti for SOFC interconnect,” International Journal of Hydrogen Energy, vol. 38, no. 5, pp. 2432–2442, 2013.
View at: Publisher Site | Google Scholar
P. D. Jablonski, C. J. Cowen, and J. S. Sears, “Exploration of alloy 441 chemistry for solid oxide fuel cell interconnect application,” Journal of Power Sources, vol. 195, no. 3, pp. 813–820, 2010.
View at: Publisher Site | Google Scholar
A. Safikhani, M. Esmailian, T. Tinatiseresht, and G. B. Darband, “High temperature cyclic oxidation behavior of ferritic stainless steel with addition of alloying elements Nb and Ti for use in SOFCs interconnect,” International Journal of Hydrogen Energy, vol. 41, no. 14, pp. 6045–6052, 2016.
View at: Publisher Site | Google Scholar
L. Niewolak, A. Savenko, D. Grüner, H. Hattendorf, U. Breuer, and W. J. Quadakkers, “Temperature dependence of laves phase composition in Nb, W and Si-alloyed high chromium ferritic steels for SOFC interconnect applications,” Journal of Phase Equilibria and Diffusion, vol. 36, no. 5, pp. 471–484, 2015.
View at: Publisher Site | Google Scholar
Y. Inoue, N. Hiraide, A. Hayashi, and K. Ushioda, “Effect of Mn addition on scale structure of Nb containing ferritic stainless steel,” ISIJ International, vol. 58, no. 10, pp. 1850–1859, 2018.
View at: Google Scholar
D. N. Zou, Y. Q. Zhou, X. Zhang, W. Zhang, and Y. Han, “High temperature oxidation behavior of a high Al-containing ferritic heat-resistant stainless steel,” Materials Characterization, vol. 136, pp. 435–443, 2018.
View at: Google Scholar
W. J. Qu, “Research on microstructure and high-temperature oxidation property of Al-Si coatings on 1Cr11MoNiW1VNbN stainless steel,” Tech. Rep., Harbin Engineering Univ. Tech. Thesis, 2011.
View at: Google Scholar
X. W. Cheng, Z. Y. Jiang, B. J. Monaghan, D. B. Wei, R. J. Longbottom, and J. W. Zhao, “Breakaway oxidation behaviour of ferritic stainless steels at 1150°C in humid air,” Corrosion Science, vol. 108, pp. 11–22, 2016.
View at: Publisher Site | Google Scholar
M. Peruzzo, T. D. Beux, M. F. C. Ordoñez, R. M. Souza, and M. C. M. Farias, “High-temperature oxidation of sintered austenitic stainless steel containing boron or yttria,” Corrosion Science, vol. 129, pp. 26–37, 2017.
View at: Google Scholar
H. H. Mao, X. Qi, J. Cao, L. C. An, and Y. T. Yang, “Effect of Si on high temperature oxidation of 30Cr13 stainless steel,” Journal of Iron and Steel Research, International, vol. 24, no. 5, pp. 561–568, 2017.
View at: Google Scholar
T. F. Li, “High temperature oxidation and thermal corrosion of metals,” Tech. Rep., Beijing: Chemical Industry Press, 2003.
View at: Google Scholar
H. B. Li, B. B. Zhang, Z. H. Jiang, S. C. Zhang, and H. Feng, “A new insight into high-temperature oxidation mechanism of super-austenitic stainless steel S32654 in air,” Journal of Alloys and Compounds, vol. 686, pp. 326–338, 2016.
View at: Google Scholar
D. S. Li, Q. X. Dai, X. N. Cheng, R. R. Wang, and Y. Huang, “High-temperature oxidation resistance of austenitic stainless steel Cr18Ni₁₁Cu₃Al₃MnNb,” Journal of Iron and Steel Research, International, vol. 19, no. 5, pp. 74–78, 2012.
View at: Publisher Site | Google Scholar
M. S. Li, High-Temperature Corrosion of Metal, Metallurgical Industry Press, Beijing, 2001.
Y. Kondo, “Behavior of copper and nickel during high temperature oxidation of steel containing them,” Materials Science Forum, vol. 522-523, pp. 53–60, 2006.
View at: Google Scholar
G. R. Holcomb and D. E. Alman, “Effect of manganese addition on reactive evaporation of chromium in Ni-Cr alloys,” Journal of Materials Engineering and Performance, vol. 15, no. 4, pp. 394–398, 2006.
View at: Publisher Site | Google Scholar
H. Ebrahimifar and M. Zandrahimi, “Mn coating on AISI 430 ferritic stainless steel by pack cementation method for SOFC interconnect applications,” Solid State Ionics, vol. 183, no. 1, pp. 71–79, 2011.
View at: Publisher Site | Google Scholar
Y. Inoue, N. Hiraide, and K. Ushioda, “Effect of Si addition on oxidation behavior of Nb containing ferritic stainless steel,” ISIJ International, vol. 58, no. 6, pp. 1117–1125, 2018.
View at: Publisher Site | Google Scholar
D. T. Hoelzer, B. A. Pint, and I. G. Wright, “A microstructural study of the oxide scale formation on ODS Fe-13Cr steel,” Journal of Nuclear Materials, vol. 283-287, pp. 1306–1310, 2000.
View at: Publisher Site | Google Scholar
G. Bamba, Y. Wouters, A. Galerie, F. Charlot, and A. Dellali, “Thermal oxidation kinetics and oxide scale adhesion of Fe–15Cr alloys as a function of their silicon content,” Acta Materialia, vol. 54, no. 15, pp. 3917–3922, 2006.
View at: Publisher Site | Google Scholar
J. H. Kim, B. K. Kim, D. I. Kim, and P. P. Choi, “The role of grain boundaries in the initial oxidation behavior of austenitic stainless steel containing alloyed Cu at 700 °C for advanced thermal power plant applications,” Corrosion Science, vol. 96, pp. 52–66, 2015.
View at: Google Scholar
Y. Qiao, J. Huang, D. Huang, J. Chen, W. Liu, and Z. Wang, “Effects of laser scanning speed on microstructure, microhardness, and corrosion behavior of laser cladding Ni45 coatings,” Journal of Chemistry, vol. 2020, Article ID 1438473, 11 pages, 2020.
View at: Publisher Site | Google Scholar
J. G. Peng, M. C. Li, and S. Z. Luo, “Oxidation characteristic of B443NT at high temperature,” Bao Steel Technology, vol. 5, pp. 22–31, 2013.
View at: Google Scholar
Y. S. Chen, J. M. Zhan, Q. Z. Ni, and M. C. Li, “Oxidation behavior of type 441 ferritic stainless steel in synthetic exhaust gas,” Corrosion Science and Protection Technology, vol. 31, no. 2, pp. 174–180, 2019.
View at: Google Scholar
Y. Qiao, D. Xu, S. Wang et al., “Effect of hydrogen charging on microstructural evolution and corrosion behavior of Ti-4Al-2V-1Mo-1Fe alloy,” Journal of Materials Science & Technology, vol. 60, pp. 168–176, 2021.
View at: Google Scholar
S. Swaminathan, Y. S. Lee, and D. I. Kim, “Long term high temperature oxidation characteristics of La and Cu alloyed ferritic stainless steels for solid oxide fuel cell interconnects,” Journal of Power Sources, vol. 327, pp. 104–118, 2016.
View at: Google Scholar
M. R. Bateni, P. Wei, X. H. Deng, and A. Petric, “Spinel coatings for UNS 430 stainless steel interconnects,” Surface and Coatings Technology, vol. 201, no. 8, pp. 4677–4684, 2007.
View at: Publisher Site | Google Scholar
N. Hosseini, M. H. Abbasi, F. Karimzadeh, and G. M. Choi, “Development of Cu_1.3Mn_1.7O₄ spinel coating on ferritic stainless steel for solid oxide fuel cell interconnects,” Journal of Power Sources, vol. 273, pp. 1073–1083, 2015.
View at: Publisher Site | Google Scholar
Z. Ranjbar-Nouri and S. Rastegari, “Applying the protective CuMn₂O₄ spinel coating on AISI-430 ferritic stainless steel used as solid oxide fuel cell interconnects,” Surface & Coatings Technology, vol. 34, pp. 365–372, 2018.
View at: Google Scholar

Copyright

Copyright © 2020 Mengqi Zhang et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

769

Downloads

858

Citations