We analyze the influence of model stratal water with low acidity on the cyclic crack resistance of 20N2M steel of a pump rod after operation for 5.5 yr. The state of the metal of a pump rod head is conventionally regarded as the reference state. We revealed insignificant differences between the basic mechanical properties and the characteristics of cyclic crack-growth resistance of steel in air for different states of the material. However, under the action of corrosive media, the fatigue crack-growth rate for the exploited steel is much higher than for steel in the reference state. This means that the in-service degradation of the rod steel manifests itself mainly in its sensitivity to the action of corrosive media.
Similar content being viewed by others
References
N. Kar, Y. Hu, E. Barjasteh, and S. Nutt, “Tension-tension fatigue of hybrid composite rods,” Composites Рart B. Eng., 43, No. 5, 2115–2124 (2012).
B. V., Kopei, A. B. Stefanyshyn, and T. P. Venhrynyuk, “Fatigue strength of hybrid pump rods,” Fiz.-Khim. Mekh. Mater., 54, No. 5, 117–120. (2018); English translation: Mater. Sci., 54, No. 5, 739–742 (2019).
B. V. Kopei, V. B. Kopei, and I. B. Kopei, Pump Rods of Well Units for the Extraction of Oil [in Ukrainian], Ivano-Frankivsk National Technical University of Oil and Gas, Ivano-Frankivsk (2009).
H. Ding, A.B. Zhang, D. T. Qi, H. B. Li, P. L. Ge, G. Q. Qi, N. Ding, Z. Q. Bai, and L. Fan, “Failure analysis of a sucker rod fracture in an oil-field,” Eng. Failure Anal., 109, article No. 104300 (2020).
B. V. Kopei, O. I. Zvirko, T. P. Venhrynyuk, Z. V. Slobodyan, and I. P. Shtoiko, “Elevation of the fatigue strength of pump rods as a result of treatment with a special medium,” Fiz.-Khim. Mekh. Mater., 56, No. 1, 118–123 (2020)); English translation: Mater. Sci., 56, No. 1, 125–131 (2020).
Yu. Ya. Meshkov, A. V. Shyyan, and O. І. Zvirko, “Evaluation of the in-service degradation of steels of gas pipelines according to the criterion of mechanical stability,” Fiz.-Khim. Mekh. Mater., 50, No. 6, 55–59 (2014); English translation: Mater. Sci., 50, No. 6, 830–835 (2015).
P. Maruschak, R. Bishchak, I. Konovalenko, A. Menou, and J. Brezinová, “Effect of long term operation on the degradation of material of main gas pipelines,” Mater. Sci. Forum, 782, 279–283 (2014).
E. V. Kharchenko, L. K. Polishchuk, and O. І. Zvirko, “Estimation of the in-service degradation of steel shapes for the boom of a clamp-forming machine,” Fiz.-Khim. Mekh. Mater., 49, No. 4, 77–82 (2013); English translation: Mater. Sci., 49, No. 4, 501–507 (2014).
I. Shtoyko, J. Toribio, V. Kharin, and M. Hredil, “Prediction of the residual lifetime of gas pipelines considering the effect of soil corrosion and material degradation,” Proc. Struct. Integrity, 16, 148–152 (2019).
H. V. Krechkovs’ka, O. T. Tsyrul’nyk, and O. Z. Student, “In-service degradation of mechanical characteristics of pipe steels in gas mains,” Strength Mater., 51, No. 3, 406–417 (2019).
H. M. Nykyforchyn and O. Z. Student, “Influence of hydrogen of the formation of fatigue thresholds in structural steels,” Fiz.-Khim. Mekh. Mater., 37, No. 2, 97–106 (2001); English translation: Mater. Sci., 37, No. 2, 252–263 (2001).
L. K. Polishchuk, H. V. Kharchenko, and O. І. Zvirko, “Corrosion-fatigue crack-growth resistance of steel of the boom of a clamp-forming machine,” Fiz.-Khim. Mekh. Mater., 51, No. 2, 77–82 (2015); English translation: Mater. Sci., 51, No. 2, 229–234 (2015).
O. O. Nemchuk, “Specific features of the diagnostics of technical state of steels of the port reloading equipment,” Fiz.-Khim. Mekh. Mater., 53, No. 6, 116–118 (2017); English translation: Mater. Sci., 53, No. 6, 875–878 (2018).
M. Kage, K. J. Miller, and R. A. Smith, “Fatigue crack initiation and propagation in a low-carbon steel of two different grain sizes,” Fatigue Fract. Eng. Mat. Struct., 15, No. 8, 763–774 (1992).
O. T. Tsyrulnyk, N. V. Kret, V. A. Voloshyn, and O. I. Zvirko, “A procedure of laboratory degradation of structural steels,” Fiz.-Khim. Mekh. Mater., 53, No. 5, 85–93 (2017); English translation: Mater. Sci., 53, No. 5, 674–683 (2018).
Z. T. Nazarchuk and H. M. Nykyforchyn, “Structural and corrosion fracture mechanics as components of the physicochemical mechanics of materials,” Fiz.-Khim. Mekh. Mater., 54, No. 1, 17–30 (2018); English translation: Mater. Sci., 54, No. 1, 7–21 (2018).
Author information
Authors and Affiliations
Corresponding author
Additional information
Translated from Fizyko-Khimichna Mekhanika Materialiv, Vol. 56, No. 2, pp. 130–134, March–April, 2020.
Rights and permissions
About this article
Cite this article
Kret, N.V., Svirska, L.M. & Venhrynyuk, T.P. Corrosion-Fatigue Crack Propagation in Exploited Pump Rods Made of 20N2M Steel. Mater Sci 56, 279–283 (2020). https://doi.org/10.1007/s11003-020-00426-w
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11003-020-00426-w