Abstract
The Van der Waals (vdWs) hetero-structures consist of two-dimensional materials have received extensive attention, which is due to its attractive electrical and optoelectronic properties. In this paper, the high-quality large-size graphene film was first prepared by the chemical vapor deposition (CVD) method; then, graphene film was transferred to SiO2/Si substrate; next, the graphene/WS2 and graphene/MoS2 hetero-structures were prepared by the atmospheric pressure chemical vapor deposition method, which can be achieved by directly growing WS2 and MoS2 material on graphene/SiO2/Si substrate. Finally, the test characterization of graphene/TMDs hetero-structures was performed by AFM, SEM, EDX, Raman and PL spectroscopy to obtain and grasp the morphology and luminescence laws. The test results show that graphene/TMDs vdWs hetero-structures have the very excellent film quality and spectral characteristics. There is the built-in electric field at the interface of graphene/TMDs heterojunction, which can lead to the effective separation of photo-generated electron–hole pairs. Monolayer WS2 and MoS2 material have the strong broadband absorption capabilities, the photo-generated electrons from WS2 can transfer to the underlying p-type graphene when graphene/WS2 hetero-structures material is exposed to the light, and the remaining holes can induced the light gate effect, which is contrast to the ordinary semiconductor photoconductors. The research on spectral characteristics of graphene/TMDs hetero-structures can pave the way for the application of novel optoelectronic devices.
Introduction
The size of traditional silicon-based metal oxide semiconductor (CMOS) transistors become smaller with increase in the chip integration, and the preparation processes of device become much more complicated, so researchers have begun to focus on the ultra-thin hetero-structure-based optoelectronics [1, 2]. The two-dimensional (2D) hetero-structures can be combined by the weak van der Waals (vdWs) force between the layers and the strong covalent bond of the layer. The layers can be separated by breaking the weak van der Waals bond and then easily transferred to other substrates [3]. The formation of new atomic-level 2D vdWs hetero-structures can be achieved by stacking the different 2D materials, and the synergistic effects of 2D hetero-structures become very important. Meanwhile, there are charge rearrangements and structural changes between adjacent crystals in hetero-structures, which can be regulated by adjusting the relative orientation of each element material. The different hetero-structures can not only maintain the properties of single material, but also produce the new physical characteristics under the synergy effect [4,5,6]. The vdWs hetero-structures are the material guarantee for exploring the new physical phenomena and laws, which can provide more possibilities for the nano-electronic devices with excellent photoelectric properties.
Since the 2D-crystalline materials have the strong interactions against a light, they have attracted extensive attentions as photosensitive materials [7]. Graphene is the atomic-level 2D material with excellent electrical, optical and mechanical properties, which has the wide application in the optoelectronics field [8,9,10]. However, the defect of zero band gap limits the application and development of graphene. The structure of 2D transition metal dichalcogenide (TMDs) materials is similar to that of graphene, and its band gap width changes with the layer number and thickness [11, 12]. The TMDs and graphene materials with complementary advantages are superimposed together, which can promote the application of graphene and TMDs materials in the photoelectric detection field [13,14,15]. The high mobility of graphene can ensure the rapid response of device, and the Van Hof singularity in electronic state density of TMDs materials ensures the strong interaction between light and materials, which can effectively enhance the absorption of light and the generation of electron–hole pairs [16, 17]. The 2D hetero-structures were widely used in the new electronic and optoelectronic devices, which is due to its transport characteristics of charge tunneling or charge accumulation, flexible energy band engineering and unique interlayer exciton characteristics. Therefore, the interlayer synergy interaction between graphene and TMDs materials can effectively control the band structure, magnetic properties and the exciton properties of hetero-structures. The graphene/TMDs hetero-structures have the high photosensitivity and light response performance, which is due to the strong quantum confinement effect [18, 19]. At present, there are the few studies on the controllable preparation methods of the large-area, large-size and high-quality graphene/TMDs hetero-structures. And the preparation processes of hetero-structures are complicated, which is still a big challenge in terms of repeatability and controllability [20, 21]. In addition, it is difficult to understand and grasp the spectral characteristics of graphene/TMDs hetero-structures, which largely hinder the application of graphene/TMDs hetero-structures in future optoelectronic devices [22].
In this paper, graphene/WS2 and graphene/MoS2 hetero-structures were composed of three kinds of semiconductor materials with different dielectric constant, band gap width and absorption coefficient. The 2D materials were directly grown on the single crystal graphene film of SiO2/Si substrate to form the graphene/TMDs hetero-structures, which can ensure the clean interface and atomic level transition of hetero-structures. The structure of graphene, MoS2 and WS2 can be analyzed by the AFM, SEM, EDX, Raman and photoluminescence spectroscopy to master the spectral characteristics of graphene/TMDs hetero-structures, which can be used to prepare the high-speed electron mobility transistors (HEMT) and photoelectric detectors [23,24,25].
Methods
Preparation and Movement of Graphene
The large-area, high-quality graphene film was prepared by CVD system, which is composed of the tube furnace, gas mixing system and vacuum machine. First, the copper foil with a size of 10 cm × 10 cm was placed into 1 mol/L hydrochloric acid solution for the 3 min ultrasonic cleaning. Then, it was washed with water and ethanol in turn. Subsequently, it was dried by blowing argon gas. Finally, it was inserted in the middle of the quartz tube, and we installed the system and corrected the air pressure [26] (Fig. 1).
As we all know, polycrystalline copper foil would affect the quality of graphene, it is necessary to anneal the copper foil substrate before the growth experiment of graphene. The specific conditions of the annealing processes at stage 1 were the following: the annealing temperature, time and the flow rate of hydrogen (H2) gas were 1000 °C, 20 min and 30 sccm, respectively. At this time, the surface of copper foil would form the large area single crystal domain, and H2 gas can reduce copper oxide, which can obtain the high-purity copper substrate. The growth temperature remains constant while entering stage 2, the flow rate of H2 gas was adjusted to 10 sccm, meanwhile 35 sccm methane (CH4) gas was also introduced, the growth time and growth pressure were, respectively, maintained for 10 min and 1.08 Torr, and the growth rate of graphene was approximately 16 μm/s in our CVD experiment, which would ensure the preparation of relatively uniform monolayer graphene film [27, 28]. Finally, the tube furnace was quenched to room temperature at a certain rate, which can avoid damaging the surface of substrate.
The following describes the transfer-specific processes of monolayer graphene material to SiO2/Si substrate [29]. First, PMMA solution with a mass fraction of 4% was uniformly spin-coated on the surface of monolayer graphene material with a size of 1 cm × 1 cm, the rotation speed and time were 3000 R/min and 1 min, respectively. Next, the copper foil substrate was etched by the (NH4)2(SO4)2 solution with a mass fraction of 3%, and the treatment time was 3–4 h. Then, the PMMA/graphene by the glass slide was rinsed repeatedly in deionized water 2–3 times, and PMMA/graphene was removed to the 50 °C constant temperature table by SiO2/Si substrate, which can remove the water vapor between monolayer graphene material and SiO2/Si substrate, and the monolayer graphene material can be better attached to SiO2/Si substrate. In this step, SiO2/Si substrate with a size of 1 × 1 cm2 was ultrasonically cleaned with acetone, ethanol and water for 15 min, and the surface of SiO2/Si substrate is very clean and uniform, which is conducive to the growth of graphene/TMDs hetero-structures. Finally, PMMA/graphene/SiO2/Si was put in acetone solution for 3–4 h to dissolve PMMA and repeatedly wash it with alcohol and deionized water to ensure that monolayer graphene film can be transferred to SiO2/Si substrate.
The Preparation of Graphene/TMDs Hetero-structures
In CVD dual temperature zone tube furnace, the graphene/SiO2/Si substrate was used for the growth of MoS2 and WS2 material. The MoO3, WO3 and sulfur powders were used as the growth molybdenum source, tungsten source and sulfur source, respectively. The high-purity Ar gas was also used to prepare the graphene/MoS2 and graphene/WS2 hetero-structures, respectively. First, the quartz boat with 100 mg sulfur powder was placed at the upstream of tube furnace. Then, 2 mg MoO3 powder (or WO3 powder) was filled in another quartz boat, and the graphene/SiO2/Si substrate was flipped upside down on MoO3 powder (or WO3 powder). And then, the quartz boat equipped with the graphene/SiO2/Si substrate and MoO3 powder (or WO3 powder) was inserted into the high temperature area of tube furnace. The heating belt was wound on the quartz tube to heat the sulfur powder, which would ensure that sulfur powder was well controlled and uniformly evaporated, as shown in Fig. 2a. Next, the high-purity Ar gas with a flow rate of 50 sccm was used as carrier gas, the evaporation temperature of sulfur powder was controlled at 150 °C, the growth temperature and growth time of MoS2 and WS2 were 750 °C, 920 °C and 10 min, respectively. Meanwhile, the first-stage temperature was maintained at 100 °C for 10 min, which can remove the water vapor of tube furnace. The specific temperature change diagram is shown in Fig. 2b. Subsequently, sulfur powder began to sublimate to the sulfur vapor, and the sulfur vapor reaches the high temperature area of tube furnace, which can be driven by Ar gas. It can be fully reacted with MoO3 and WO3 powder, and the product was deposited on graphene/SiO2/Si substrate. Therefore, the growth rate of graphene/TMDs hetero-structures was consistent with that of TMDs materials [30]. After the growth of MoS2 and WS2 material, the tube furnace was naturally cooled to room temperature, and the color of substrate becomes light yellow.
The Test Characterization of Graphene/TMDs Hetero-structures
In this paper, the test and characterization methods of graphene/TMDs hetero-structures mainly include the optical microscope (OM), Raman and photoluminescence (PL) spectroscopy, field emission scanning electron microscope (FESEM), energy-dispersive X-ray spectroscopy (EDX) and atomic force microscope (AFM). First, the surface morphology of graphene/TMDs hetero-structures can be observed by optical microscope, SEM and AFM. The layer number of hetero-structures can be judged according to the different contrast of hetero-structure sample. Then, the spectral characteristics of graphene/TMDs hetero-structures were tested and characterized. The growth morphology, growth pattern and growth mechanism of TMDs materials on graphene surface were analyzed and speculated based on the characterization results [31]. Next, Raman spectroscopy has the advantages of quickness, high efficiency and low destructiveness in terms of characterizing 2D materials. It can directly observe the interaction of electron phonons on the sample surface, which has a very wide range of applications in 2D materials. The layer number and crystal quality of 2D materials can be effectively judged by analyzing the characteristic peak position of Raman spectra, the characteristic peak position wave number difference and other characteristics of graphene/TMDs hetero-structures. Finally, the PL spectra were also an important method for characterizing and analyzing 2D materials. When the bulk material is thinned to monolayer material, the band gap width of TMDs material changes from the indirect band gap semiconductor to the direct band gap semiconductor. Meanwhile, the fluorescence effect was significantly enhanced, and there are the obvious characteristic peaks in the PL spectra. However, if the crystal quality of graphene/TMDs hetero-structures was not high, the characteristic peak intensity of PL spectra would be small even if the sample has few layers or monolayer. Therefore, the layer thickness and crystal quality of sample can also be judged by PL spectra. In addition, the distribution, element type and concentration percentage of graphene/TMDs hetero-structures films can be obtained by FESEM and EDX. Meanwhile, the AFM test was also used to grasp the surface cleanliness, roughness and material thickness of hetero-structures film samples.
Both the PL and Raman spectra were collected by the LabRAM HR Evolution high-resolution Raman spectrometer, which was produced by HORIBA Jobin Yvon (French company) [32, 33]. The range of Raman and PL spectra was 300 cm−1–3000 cm−1 and 550–800 nm, respectively. And the Raman and PL spectra were 10% power and 5% power, respectively. The following were the specific test conditions, spectral resolution ≤ 0.65 cm−1; spatial resolution: horizontal ≤ 1 μm, vertical ≤ 2 μm; 532 nm laser, 50× objective lens (beam spot diameter is 1.25 μm, and 100% laser power equivalent to 7500 μw/cm2); scan time 15 s, and the cumulative number is 2.
Results and Discussion
The Optical Micrograph and Characterization of Graphene/WS2 Hetero-structure
The morphology of hetero-structures can be distinguished by the high-resolution microscope of Raman spectrometer. Figure 3a shows the optical microscope images of graphene/WS2 hetero-structure under the different locations of SiO2/Si substrate. Since the color of graphene film transferred to SiO2/Si substrate was not much different, the graphene film is relatively uniform and complete. The surface of graphene/SiO2/Si substrate was clean except for a small amount of particles, which indicates the presence of better quality graphene film. Meanwhile, the nucleation density of WS2 became maximum when the gas concentration is sufficient in the growth experiment of WS2. And the WS2 grown on graphene/SiO2/Si substrate was the triangular structure grain with the uniform grain surface and a side length about 120 μm. The shape of WS2 was regular and complete, and the thickness was uniform, which is much larger than the size of mechanical peeling sample [34]. In Fig. 3b, since the fluorescence intensity of WS2 sample is highly uniformly distributed, the triangular monolayer WS2 film has the higher quality and lower defects. It can be seen from Fig. 3c, d that the morphology of WS2 film sample is triangle, and the thickness of WS2 film is 0.83 nm, which indicates the preparation of monolayer WS2 film. In addition, SEM was also used to analyze the morphology of WS2 sample film, and the morphology was the regular triangular with uniform thickness, as shown in Fig. 3e. In Fig. 3f, the dock element, sulfur element and carbon element are shown in EDX spectrum, which shows that graphene/WS2 hetero-structure material is successfully transferred and prepared.
The molecular vibration and rotation information of material can be obtained by Raman spectroscopy, which are the fingerprint vibration spectra for identifying the material structure. The layer number and crystal quality of WS2 sample can be effectively judged by the characteristic peak position and wave number difference of Raman spectra. Figure 4a shows the Raman spectra of WS2 sample at different positions, the E12g and A1g characteristic peaks were located at 350.4 cm−1 and 416.1 cm−1, respectively. When the bulk WS2 changes to monolayer material, E12g and A1g characteristic peaks appear the blue-shifted and red-shifted, respectively. Therefore, the layer number can be judged by the wave numbers difference between two characteristic peaks, and the wavenumber difference was 65.7 cm−1, so the triangular WS2 grains were monolayer material. In Fig. 4b, the strongest luminescence peak was located at 626 nm, and the corresponding band gap was 1.98 eV, which is consistent with the band gap width of monolayer WS2. As we all know, the PL intensity of 2D material is related to the crystal quality and layer number. The 2D material has the fewer defect and layer number, and the luminous intensity is higher, which indicates that the crystal quality is better [35]. The variable power characterization can be performed at the nW level to prevent the laser irradiation from damaging the sample. It can be found by observing Fig. 4c that the peak position of E12g plane vibration mode remains basically unchanged with increase in the excitation power, and the A1g vibration mode between the planes moves to the short wave number direction. This is because the A1g vibration mode has the great relationship with electron concentration, and the increase in electron concentration would lead to the reformation of band gap. As shown in Fig. 4d, the PL spectra intensity of WS2 increases with the laser power increases, and there exists the fluorescence quenching phenomenon, which is due to the reformation of band gap and the interlayer interaction of hetero-structures. At the same time, it can also be found that the local temperature of material did nearly not change with increase in the laser power. This is because WS2 is the atomic layer-level nanomaterial.
The layer number characterization and quality information of graphene material can be obtained by Raman spectroscopy. In Fig. 5a, the Raman diffraction spectra of graphene at different positions has the three main characteristic peaks, D peak, G peak and 2D peak, were, respectively, located at 1330 cm−1, 1583 cm−1 and 2674 cm−1. The D peak is related to the disorder of graphene lattice structure, and the position of D peak was blue-shifted when graphene material has more lattice defects, which can reflect the defects and impurity content of crystal. The 2D peak is the two-phonon second-order resonance Raman peak, which can indicate the carbon atoms arrangement of graphene material. Besides, the G peak is caused by the E2g mode of first Brillouin zone center, the peak height increases almost linearly with the layers number of graphene, and the G peak intensity is related to the doping of graphene to a certain extent. The relative ratio of 2D peak and G peak can be used to roughly determine the layers number of graphene, and the ratio of D peak to G peak would decrease when the defect density is increased. The weak D peak appears in the Raman spectra of graphene when the growth of MoS2 (or WS2) material was completed, which indicates that the graphene domain still maintains the high quality. The 2D peak intensity of exposed graphene area weakened, which is affected by the high-temperature growth process. The full width at half maxima (FWHM) of graphene 2D peak gradually increases with increase in the layers number, and the peak position of 2D peak is blue-shifted, which may be related to the energy band relationship of graphene material. The electronic energy band structure splits with increase in the layers number, and a variety of phonon resonance scattering processes would occur. The exciton peak would be excited by absorbing more energy, which would lead to the blue shift of 2D peak position. The peak intensity of G peak at Point C and E is significantly higher than that of 2D peak. The I2D/IG ratio decreases with increase in the thickness, and the transferred graphene in this experiment was not very uniform, which is within the allowable range. Figure 5b shows the power Raman spectra of monolayer graphene. The G and 2D peak intensity of graphene is gradually increasing with increase in the laser power and temperature, and there is basically no change of the peak position and FWHM. The G peak and 2D peak were, respectively, located at 1581 cm−1 and 2672 cm−1, and the intensity of two characteristic peaks differs greatly. Due to the interaction change between graphene and underlying SiO2, the characteristic peak ratio of I2D/IG is decreased. Meanwhile, there were no D defect peak of Raman spectra, which indicate that the selected graphene region has a high quality and the carbon atoms are highly ordered.
Raman spectroscopy was used to characterize and analyze the graphene/WS2 hetero-structure material, and there were two spectra of 300 cm−1 ≤ ω ≤ 500 cm−1 and 1400 cm−1 ≤ ω ≤ 3000 cm−1, which were fitted by the Lorentz function. There were the E12g and A1g modes characteristic peaks of WS2 in the range of 300 cm−1 ≤ ω ≤ 500 cm−1. The E12g phonon mode is the in-plane displacement of sulfur and tungsten atoms, while the A1g phonon mode is the out-of-plane displacement of sulfur atoms, the above phonon mode locations and intervals vary with the layers number. The G and 2D peaks of graphene appear in the spectra region of 1400 cm−1 ≤ ω ≤ 3000 cm−1, and the layer number and crystal quality information of graphene can be obtained according to the intensity ratio and the peak position of characteristic peaks.
The frequency difference of two different Davydov splitting peaks can reflect the interaction magnitude of vdWs hetero-structures. Therefore, the intra-layer vibrating phonon mode frequency of multilayer 2D material also depends on the interlayer coupling and layers number. Figure 6a shows the Raman spectra test characterization of graphene/WS2 hetero-structure at different points under the 532 nm laser. It can be found that the intensity of E12g characteristic peak was higher than that of A1g characteristic peak intensity, and the E12g and A1g characteristic peaks were located at 349.3 cm−1 and 417.1 cm−1, respectively. The Raman spectra 2D and G peaks of graphene/WS2 hetero-structure were, respectively, at 1591.5 cm−1 and 2680.9 cm−1, and the peak position of 2D and G peaks rise compared with pure graphene, which may be related to the effective interlayer coupling of WS2 nano-sheets and the strain effect generated by the high temperature heating during CVD growth. The Raman spectra of graphene/WS2 hetero-structure material is only the sum of the individual separated WS2 and graphene spectra, which can confirm the formation of vdWs heterojunction interface. The PL spectra intensity is related to the crystal quality and layer number. Raman spectroscopy focuses on the influence of hetero-structures formation on the vibration modes, and the electronic band structure of TMDs hetero-structures material can be mainly obtained by PL spectra. Figure 6b shows the PL spectra of graphene/WS2 hetero-structure at different points. The strongest luminescence peak was located at 624 nm, and the corresponding band gap was 1.99 eV, which is consistent with the band gap width of monolayer WS2. The graphene/WS2 hetero-structure material at different positions has the different intensity and shape of PL spectra, and the crystal quality is not very good. Therefore, the preparation processes of hetero-structure need to be further improved. The PL spectra intensity of graphene/WS2 hetero-structure is weaker than that of WS2. This is because the inter-layer coupling of graphene/WS2 hetero-structure changes the exciton fluorescence of hetero-structures region, which would lead to the separation of electron–hole pairs and the reduction in fluorescence. Meanwhile, the peak position shifts when the graphene/WS2 hetero-structure is formed, and the transfer of charge can cause the shift of Fermi surface, which can make the free excitons change into the charged excitons. Figure 6c shows the power Raman spectra of graphene/WS2 hetero-structure. The in-plane phonon mode E12g characteristic peak and the out-of-plane phonon mode A1g characteristic peak were, respectively, at 356 cm−1 and 418 cm−1, where the above characteristic peak is increased with increase in the laser power. The peak position and shape of characteristic peak were uniform within single crystal, and the electronic characteristics of WS2 on graphene/SiO2/Si substrate were uniform. The thickness of WS2 sheet can be determined according to the frequency difference between A1g and E12g characteristic peaks, and the average distance was 62 ± 0.2 cm−1, which is consistent with the thickness of monolayer WS2. Compared to the peak positions of intrinsic graphene, the G peak and 2D peak positions of graphene/WS2 hetero-structure from 1578.7 cm−1 and 2685.8 cm−1 change to 1582.2 cm−1 and 2689.5 cm−1, respectively. Besides, the intensity of G peak becomes stronger than that of 2D peak with increase in the laser power, and decrease in the I2D/IG ratio, which is caused by the interaction change between graphene and SiO2/Si substrate [36, 37]. It can be found by observing Fig. 6d that the PL intensity of graphene/WS2 hetero-structure is increased with increase in the laser power, the FWHM of PL spectra also increasing, and the shape of PL spectra is changed. The reason is that the test temperature around hetero-structure is increased, and there is also the strong interlayer coupling at the interface of graphene/WS2 heterojunction.
The Raman spectra of graphene/WS2 hetero-structure were significantly different from that of exposed graphene region, as shown in Fig. 7a. First, the spectral background rises when wavenumber increases, and the background comes from the PL spectra of WS2, which confirms the presence of graphene/WS2 hetero-structure. Next, WS2 material can suppress the 2D characteristic peak intensity of graphene. Finally, both G peak and 2D peak of graphene/WS2 hetero-structure shift upward compared with the spectra of bare graphene material. Due to the interlayer coupling between graphene and WS2, the 2D peak would also shift up, and the mechanical strain also has the impact on the Raman shift of graphene. The enhancement factor (EF) is the ratio of the maximum peak intensity of graphene/WS2 hetero-structure divided by the maximum peak intensity of graphene. The maximum peak intensity of G peak increases from 460 to 830, and the maximum peak intensity of 2D peak increases from 340 to 1460, and the corresponding EF were 1.8 and 4.3, respectively. The D peak signal is significantly enhanced when the graphene/TMDs hetero-structures is formed. Therefore, the ID/IG ratio of monolayer graphene is weaker than that of graphene/WS2 hetero-structure. This is because the extrusion of WS2 on graphene has the effect on the structure of graphene, which would result in the appearance of a small number of defects. In Fig. 7b, the PL intensity of graphene/WS2 hetero-structure is higher than that of bare graphene, which may be related to the effective interlayer coupling and the strain effect. Meanwhile, the maximum intensity of PL spectra is increased from 270 to 1410, and the corresponding EF is 5.23. The intensity enhancement of characteristic peak can be attributed to the coupling of graphene/WS2 hetero-structure.
Raman spectroscopy can be used to evaluate the crystal quality and film thickness of 2D materials. The Raman spectra comparison of WS2 and graphene/WS2 hetero-structure is shown in Fig. 8a. Compared to the Raman spectra of WS2, the A1g mode characteristic peak position of graphene/WS2 hetero-structure was blue-shifted, and the intensity of E12g mode and A1g mode characteristic peaks was higher than those of WS2, and the graphene/WS2 hetero-structure film has the excellent crystallinity. The reason is that the coupling between layers can be enhanced when the two materials are stacked to form the hetero-structure, which would generate the interlayer interaction forces. The maximum E12g and Alg characteristic peak intensity increases from 3400 and 1100 to 6500 and 2950, respectively. And the enhancement factors (EF) are 1.9 and 2.7, respectively. In addition, monolayer WS2 and multilayer WS2 are the direct band gap semiconductor and indirect semiconductor materials, respectively. Therefore, the PL spectroscopy can be used to identify the layer number of WS2 sample. In Fig. 8b, the above two materials show that the strongest PL emission was around 626 nm, and that the band gap was approximately at 1.98 eV, which is consistent with band gap of the mechanically peeled monolayer WS2. The PL intensity of graphene/WS2 hetero-structure was stronger than that of monolayer WS2. The reasons are the following: First, the work function between graphene and WS2 does not match. Second, the internal field was formed. Third, the photoelectrons from WS2 can transfer to graphene. Forth, the WS2 material retains holes. The maximum intensity of strongest peak increases from 7450 to 19,320, and the EF of PL spectra are 2.6. The increase in peak intensity is due to the coupling between graphene and WS2 materials.
Optical Micrograph and Characterization of Graphene/MoS2 Hetero-structure
The optical microscope pictures of graphene/MoS2 hetero-structure on SiO2/Si substrate are shown in Fig. 9a. We found that the color of the graphene transferred to SiO2/Si substrate was not much different from the original one. The surface was relatively clean except for a few particles in some areas. These results indicate that the graphene film is uniformly and completely formed. The MoS2 thin film covers graphene/SiO2/Si substrate, which can be connected into the continuous graphene thin film across the grain boundaries. The prepared graphene/MoS2 hetero-structure was continuous and intact, and the sample surface was relatively clean, which has the good surface uniformity. The local fluorescence intensity distribution is not uniform when there are many defects. Figure 9b shows the in-plane fluorescence intensity distribution of triangular monolayer MoS2 film. The crystal lattice of sample has the fewer defects. In Fig. 9c, d, the surface condition of the material is observed by AFM, and the height difference between the edge of the material and the graphene/SiO2/Si substrate is measured to judge the material thickness, the thickness of monolayer MoS2 material is about 0.81 nm. It can be found by the SEM test result that the morphology of MoS2 film sample is the triangular flake, as shown in Fig. 9e. It can be found by observing Fig. 9f that the molybdenum, sulfur and carbon elements are uniformly distributed in the EDX spectrum, which indicates that the graphene/MoS2 hetero-structure has been successfully prepared.
The interlayer interaction weakens with decrease in the film thickness. The A1g mode characteristic peak is red-shifted, whereas the characteristic peak of E12g mode is blue-shifted. As a result, the frequency distance between A1g and E12g vibration modes becomes smaller, which can be used to identify the thickness of 2D materials. Figure 10a shows the Raman spectra of MoS2 at different positions. The characteristic peaks of E12g mode and A1g mode were at 381.2 cm−1 and 400.5 cm−1, respectively. And the peak spacing was 19.3 cm−1, which indicates the presence of monolayer MoS2. Due to the Van der Waals force between the layers, the frequencies of two vibration modes moving in the same or opposite directions between adjacent atoms in the layers are slightly different. The PL spectra are used to obtain the light emission characteristics of MoS2 film, as shown in Fig. 10b. As we all know, the luminous intensity of monolayer MoS2 was much greater than that of multilayer, and the electronic band structure changed from indirect band gap to direct band gap when the layer number of MoS2 material changed from multilayer to single layer. Therefore, there was only the strong emission peak of monolayer MoS2. In addition, the strongest PL peak was at 678.5 nm, and the corresponding direct band gap was 1.83 eV, which is close to the band gap value of mechanically peeling MoS2 film. It can be found by observing Fig. 10c that the characteristic peak intensity of Raman spectra is increased with increase in the laser power and that the peak positions of E12g and A1g mode characteristic peak were blue-shifted. This is because the Raman peak line would have a certain frequency shift with increase in the temperature and laser power. Figure 10d shows the power PL spectra of MoS2, the luminous intensity increasing accordingly with increase in the laser power, and the strongest PL peak position was blue-shifted.
A high-frequency layer vibrating phonon mode of monolayer 2D material would split into the N corresponding high-frequency modes in an N-layer 2D material, which would lead to the Davydov splitting. Figure 11a shows the Raman spectra of graphene/MoS2 hetero-structure, and there were the G, 2D peaks of graphene and the E12g and A1g peaks of MoS2, which indicates the formation of layered graphene/MoS2 hetero-structure material. The E12g and A1g Raman characteristic peaks of MoS2 were located at 375.5 cm−1 and 394.4 cm−1, respectively. And the peak spacing was 18.9 cm−1. Compared with intrinsic graphene, the G peak and 2D peak positions of graphene/MoS2 hetero-structure shift to large wavenumbers, and G peak and 2D peak move from 1581 and 2672 cm−1 to 1587 and 2674 cm−1, respectively. In addition, the intensity of G peak is stronger than that of 2D peak. The rise of the 2D and G peaks position is related to the effective interlayer coupling and the strain effect. Compared with the Raman spectra of MoS2 material, the spectra of graphene/MoS2 hetero-structure material are significantly shifted due to the enhancement of interlayer atomic interaction, and the peak intensity can also be significantly enhanced. It can be found from Fig. 11b that the graphene/MoS2 hetero-structure has two absorption peaks at 621 nm and 683 nm and that the corresponding band gaps were 1.99 eV and 1.82 eV according to the conversion relationship between wavelength and electron volt. The luminous intensity of graphene/MoS2 hetero-structure was lower than that of intrinsic MoS2. The reasons of these phenomena are that the graphene material has the weakening effect on the fluorescence of MoS2 material and that the electronic energy band and electronic distribution can be changed due to the interlayer coupling, which can greatly change the PL and Raman spectra.
Figure 11c shows the power Raman spectra of graphene/MoS2 hetero-structure, the Raman peaks intensity of G, 2D, E12g, and A1g increasing with increase in the laser power. The peak position difference between E12g and A1g is gradually enhanced with increase in the layer number of MoS2 material. The characteristic peak positions of E12g and A1g were 377.2 cm−1 and 396.7 cm−1, respectively. And the peak position difference was 19.5 cm−1, which can be judged that MoS2 material is the monolayer. Meanwhile, the G and 2D peaks of graphene were red-shifted and blue-shifted, respectively. This is because graphene material is doped with MoS2. It can be found by observing Fig. 11d that there were two PL peaks of graphene/MoS2 hetero-structure. These PL peak corresponding to the compound transition of A and B excitons, wherein the light emission corresponding to the direct band gap exciton recombination was 1.84 eV, whereas the peak corresponding to the indirect band gap exciton recombination was at 2.0 eV. The luminous intensity of strongest peak is increased with increase in the laser power, and the peak position of the strongest PL spectra is red-shifted. This is due to the p-type conductivity of the graphene and the change of band structure when graphene and MoS2 materials were stacked. In addition, the arrangement of energy bands at the interface allows the electrons from electron-rich MoS2 to transfer to p-type graphene material.
Conclusion
Graphene/TMDs-based hetero-structures, where WS2 and MoS2 were used as TMDs material, were successfully synthesized directly on graphene films by using APCVD. The morphology, spectral characteristics and luminescence law of hetero-structures can be obtained by AFM, SEM, EDX, Raman and PL spectroscopy, and the hetero-structures show the excellent photosensitivity. Compared with intrinsic graphene material, the G and 2D peak positions of graphene/TMDs hetero-structures are the blue-shifted, the intensity of G peak is stronger than that of 2D peak with increase in the laser power and decrease in the I2D/IG ratio. Due to the presence of internal electric field, the photo-generated electron–hole pairs can be effectively separated at the interface of graphene/TMDs hetero-structures, which could greatly improve the light response. This research could effectively guide the preparation process improvement in large-area, high-quality hetero-structures, and it could also pave the way for the application of graphene/TMDs hetero-structures in the optoelectronic devices field.
Availability of data and materials
The experiment data supporting the conclusion of this manuscript have been given in this manuscript.
Abbreviations
- 2D TMDs:
-
Two-dimensional transition-metal dichalcogenides
- vdWs:
-
Van der Waals
- HEMT:
-
High-speed electron mobility transistors
- PMMA:
-
Polymethyl methacrylate
- MoS2 :
-
Molybdenum disulfide
- APCVD:
-
Atmospheric pressure chemical vapor deposition
- WO3 :
-
Molybdenum trioxide
- OM:
-
Optical microscopy
- PL:
-
Photoluminescence
- MoO3 :
-
Molybdenum trioxide
References
Sun D, Ye D, Liu P, Tang Y, Guo J, Wang L, Wang H (2018) MoS2/Graphenenanosheets from commercial bulky MoS2 and graphite as anode materials for high rate sodium-ion batteries. Adv Energy Mater 8(10):1702383
Thanh TD, Chuong ND, Van Hien H, Kshetri T, Kim NH, Lee JH (2018) Recent advances in two-dimensional transition metal dichalcogenides-graphene hetero-structuresd materials for electrochemical applications. Progress Mater Sci 96:51–85
Yuan L, Chung TF, Kuc A, Wan Y, Xu Y, Chen YP, Heine T, Huang L (2018) Photocarrier generation from interlayer charge-transfer transitions in WS2-graphene hetero-structures. SciAdv 4(2):e1700324
Tian H, Liu M, Zheng W (2018) Constructing 2D graphitic carbon nitride nanosheets/layered MoS2/graphene ternary nanojunction with enhanced photocatalytic activity. ApplCatal B Environ 225:468–476
Wang R, Wang S, Jin D, Zhang Y, Cai Y, Ma J, Zhang L (2017) Engineering layer structure of MoS2-graphene composites with robust and fast lithium storage for high-performance Li-ion capacitors. Energy Storage Mater 9:195–205
Yamaguchi T, Moriya R, Inoue Y, Morikawa S, Masubuchi S, Watanabe K, Taniguchi T, Machida T (2014) Tunneling transport in a few monolayer-thick WS2/graphene hetero-structures. ApplPhysLett 105(22):223109
Liu Q, Cook B, Gong M, Gong Y, Ewing D, Casper M, Wu J (2017) Printable transfer-free and wafer-size MoS2/graphene van der Waals hetero-structures for high-performance photodetection. ACS Appl Mater Interfaces 9(14):12728–12733
You B, Wang X, Mi W (2015) Prediction of spin–orbital coupling effects on the electronic structure of two dimensional van der Waals hetero-structures. PhysChemChemPhys 17(46):31253–31259
Murugadoss V, Wang N, Tadakamalla S, Wang B, Guo Z, Angaiah S (2017) In situ grown cobalt selenide/graphenenanocomposite counter electrodes for enhanced dye-sensitized solar cell performance. J Mater Chem A 5(28):14583–14594
Zhang D, Jia Y, Cheng J, Chen S, Chai J, Yang X, Han C (2018) High-performance microwave absorption materials based on MoS2-graphene isomorphic hetero-structures. J Alloys Compd 758:62–71
Liu M, Shi J, Li Y, Zhou X, Ma D, Qi Y, Zhang Y, Liu Z (2017) Temperature-triggered sulfur vacancy evolution in monolayer MoS2/graphene hetero-structures. Small 13(40):1602967
Kirubasankar B, Palanisamy P, Arunachalam S, Murugadoss V, Angaiah S (2019) 2D MoSe2-Ni (OH)2nanohybrid as an efficient electrode material with high rate capability for asymmetric supercapacitor applications. ChemEng J 355:881–890
Li C, Cao Q, Wang F, Xiao Y, Li Y, Delaunay JJ, Zhu H (2018) Engineering graphene and TMDs based van der Waals hetero-structures for photovoltaic and photoelectrochemical solar energy conversion. ChemSoc Rev 47(13):4981–5037
Xie Y, Chou TM, Yang W, He M, Zhao Y, Li N, Lin ZH (2017) Flexible thermoelectric nanogenerator based on the MoS2/graphenenanocomposite and its application for a self-powered temperature sensor. SemicondSciTechnol 32(4):044003
Kirubasankar B, Murugadoss V, Lin J, Ding T, Dong M, Liu H, Zhang J, Li T, Wang N, Guo Z, Angaiah S (2018) In situ grown nickel selenide on graphenenanohybrid electrodes for high energy density asymmetric supercapacitors. Nanoscale 10(43):20414–20425
Liu X, Gao J, Zhang G, Zhang YW (2017) MoS 2-graphene in-plane contact for high interfacial thermal conduction. Nano Res 10(9):2944–2953
Omar S, van Wees BJ (2017) Graphene-WS2 hetero-structures for tunable spin injection and spin transport. Phys Rev B 95(8):081404
Subasri A, Balakrishnan K, Nagarajan ER, Devadoss V, Subramania A (2018) Development of 2D La (OH)3/graphenenanohybrid by a facile solvothermal reduction process for high-performance supercapacitors. ElectrochimActa 281:329–337
Biroju RK, Pal S, Sharma R, Giri PK, Narayanan TN (2017) Stacking sequence dependent photo-electrocatalytic performance of CVD grown MoS2/graphene van der Waals solids. Nanotechnology 28(8):085101
Zhao Y, Zhang X, Wang C, Zhao Y, Zhou H, Li J, Jin H (2017) The synthesis of hierarchical nanostructured MoS2/graphene composites with enhanced visible-light photo-degradation property. Appl Surf Sci 412:207–213
O’Suilleabhain D, Vega-Mayoral V, Kelly AG, Harvey A, Coleman JN (2019) Percolation effects in electrolytically gated WS2/graphenenano: nano composites. ACS Appl Mater Interfaces 11(8):8545–8555
Song H, Wang B, Zhou Q, Xiao J, Jia X (2017) Preparation and tribological properties of MoS2/graphene oxide composites. Appl Surf Sci 419:24–34
Aeschlimann S, Rossi A, Chávez-Cervantes M, Krause R, Arnoldi B, Stadtmüller B, Aeschlimann M, Forti S, Fabbri F, Coletti C, Gierz I (2020) Direct evidence for efficient ultrafast charge separation in epitaxial WS2/graphene hetero-structures. Sci Adv 6(20):eaay0761
Du L, Yu H, Liao M, Wang S, Xie L, Lu X, Yang R (2017) Modulating PL and electronic structures of MoS2/graphene hetero-structures via interlayer twisting angle. ApplPhysLett 111(26):263106
Maurya DK, Balan B, Murugadoss V, Yan C, Angaiah S (2020) A fast Li-ion conducting Li7.1La3Sr0.05Zr1.95O12 embedded electrospun PVDF-HFP nanohybrid membrane electrolyte for all-solid-state Li-ion capacitors. Mater Today Commun 25:101497
O’Farrell ECT, Avsar A, Tan JY, Eda G, Ozyilmaz B (2015) Quantum transport detected by strong proximity interaction at a graphene-WS2 van der Waals interface. NanoLett 15(9):5682–5688
Antonova IV (2016) Vertical hetero-structures based on graphene and other 2D materials. Semiconductors 50(1):66–82
Kirubasankar B, Vijayan S, Angaiah S (2019) Sonochemical synthesis of a 2D–2D MoSe2/graphenenanohybrid electrode material for asymmetric supercapacitors. Sustain Energy Fuels 3(2):467–477
Kim YC, Nguyen VT, Lee S, Park JY, Ahn YH (2018) Evaluation of transport parameters in MoS2/graphene junction devices fabricated by chemical vapor deposition. ACS Appl Mater Interfaces 10(6):5771–5778
Meng X, Yu L, Ma C, Nan B, Si R, Tu Y, Bao X (2019) Three-dimensionally hierarchical MoS2/graphene architecture for high-performance hydrogen evolution reaction. Nano Energy 61:611–616
Murugadoss V, Panneerselvam P, Yan C, Guo Z, Angaiah S (2019) A simple one-step hydrothermal synthesis of cobaltnickelselenide/graphenenanohybrid as an advanced platinum free counter electrode for dye sensitized solar cell. ElectrochimActa 312:157–167
He J, Kumar N, Bellus MZ, Chiu HY, He D, Wang Y, Zhao H (2014) Electron transfer and coupling in graphene–tungsten disulfide van der Waals hetero-structures. Nat Commun 5(1):1–5
Horri A, Faez R, Pourfath M, Darvish G (2017) A computational study of vertical tunneling transistors based on graphene-WS2 hetero-structures. J ApplPhys 121(21):214503
Kirubasankar B, Murugadoss V, Angaiah S (2017) Hydrothermal assisted in situ growth of CoSe onto graphenenanosheets as a nanohybrid positive electrode for asymmetric supercapacitors. RSC Adv 7(10):5853–5862
Wang Y, Chen Y, Wu X, Zhang W, Luo C, Li J (2018) Fabrication of MoS2-graphene modified with Fe3O4 particles and its enhanced microwave absorption performance. Adv Powder Technol 29(3):744–750
Arunachalam S, Kirubasankar B, Murugadoss V, Vellasamy D, Angaiah S (2018) Facile synthesis of electrostatically anchored Nd (OH)3nanorods onto graphenenanosheets as a high capacitance electrode material for supercapacitors. New J Chem 42(4):2923–2932
Paradisanos I, McCreary KM, Adinehloo D, Mouchliadis L, Robinson JT, Chuang HJ, Kioseoglou G (2020) Prominent room temperature valley polarization in WS2/graphene hetero-structures grown by chemical vapor deposition. ApplPhysLett 116(20):203102
Acknowledgements
TH and KY are Ph.D. students in Xidian University. SpC is a doctor in Xidian University. SlW is an associate professor in Xidian University. HxL is a professor in Xidian University.
Funding
This research was funded by the National Natural Science Foundation of China (Grant No. U1866212), the Laboratory Open Fund of Beijing Smart-chip Microelectronics Technology Co., Ltd. (Grant No. SGITZXDDKJQT2002303), the Innovation Foundation of Radiation Application (Grant No. KFZC2018040206). This research was also supported by SixCarbon Technology Shenzhen.
Author information
Authors and Affiliations
Contributions
TH generated the research idea, analyzed the data, and wrote the paper. TH, KY and SC carried out experiments. TH and KY participated in the discussion. SW and HL have given the final approval of the version to be published. All authors read and approved the final manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare that they have no competing interests.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Han, T., Liu, H., Wang, S. et al. Research on the Preparation and Spectral Characteristics of Graphene/TMDs Hetero-structures. Nanoscale Res Lett 15, 219 (2020). https://doi.org/10.1186/s11671-020-03439-1
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-020-03439-1