Abstract
The machinability of 7055 aluminum alloy with wide temperature range is examined, with focus on the three cutting forces, surface quality and work hardening of the material under low, medium, and high temperatures. The results demonstrate that, under low temperature, the work hardening depth of 7055 aluminum alloy is almost insensitive to the cutting speed, whereas at a higher cutting speed, the work hardening degree of the material first decreases and then increases; both the work hardening degree and hardening depth are significantly positively correlative to the cutting depth: the work hardening degree is positively correlative, though not so significantly, to the feed rate, while the work hardening depth is insensitive to the feed rate and remains at 100 μm in all cases. Under high temperature, the work hardening degree of 7055 aluminum alloy is positively correlative to the cutting speed; at depths smaller than 80 μm below the machined surface, the work hardening degree is negatively correlative to the cutting depth; at depths larger than 80 μm below the cutting surface, the work hardening degree of the material becomes significantly positively correlative to the cutting depth. A mathematical model of three cutting forces in dry cutting with wide temperature range is established based on wide temperature-range dynamic impact experimental results and the orthogonal cutting model, and modified using the LMSE (least mean square error) principle. The errors between the predicted and experimental three cutting forces, after modification, are all smaller than 10%, which is within the permissible limit of error. This verifies that the modified three cutting force prediction model can predict cutting forces accurately.
Similar content being viewed by others
References
Sugihara T, Enomoto T (2012) Improving anti-adhesion in aluminum alloy cutting by micro stripe texture. Precis Eng 36(2):229–237
Davoodi B, Tazehkandi AH (2014) Experimental investigation and optimization of cutting parameters in dry and wet machining of aluminum alloy 5083 in order to remove cutting fluid. Journal of Cleaner Production 68(3):234–242
Paturi UMR, Narala SKR, Pundir RS (2014) Constitutive flow stress formulation, model validation and Fe cutting simulation for aa7075-t6 aluminum alloy. Materials Science & Engineering A 605(6):176–185
Lindstrm SB (2020) Continuous-time, high-cycle fatigue model for nonproportional stress with validation for 7075-t6 aluminum alloy. Int J Fatigue 140:105839
Wang Y, Su H, Dai J, Yang S (2019) A novel finite element method for the wear analysis of cemented carbide tool during high speed cutting ti6al4v process. Int J Adv Manuf Technol 103(2):2795–2807
Li W, Xu D, Xiong D, Ke Q (2019) Compression deformation in the primary zone during the high-speed cutting of titanium alloy ti-6al-4v. Int J Adv Manuf Technol
Tsao CC (2007) An experiment study of hard coating and cutting fluid effect in milling aluminum alloy. Int J Adv Manuf Technol 32(9–10):885–891
Wu Q, Li DP (2014) Analysis and X-ray measurements of cutting residual stresses in 7075 aluminum alloy in high speed machining. International Journal of Precision Engineering & Manufacturing 15(8):1499–1506
Dong G, Wang X, Gao S (2018) Molecular dynamics simulation and experiment research of cutting-tool wear mechanism for cutting aluminum alloy. International Journal of Advanced Manufacturing Technology 26:1–15
Chen C, Gao M, Zeng X (2016) Relationship between temperature at cut front edge and kerf quality in fiber laser cutting of Al–Cu aluminum alloy. Int J Mach Tool Manu 109:58–64
Huang Y, Wang J, Wan L, Meng X, Liu H, Li H (2016) Self-riveting friction stir lap welding of aluminum alloy to steel. Mater Lett 185:181–184
Frattini D, Accardo G, Moreno A, Yoon SP, Han JH, Nam SW (2017) A novel nickel-aluminum alloy with titanium for improved anode performance and properties in molten carbonate fuel cells. J Power Sources 352:90–98
Qi JL, Wang ZY, Lin JH, Zhang TQ, Zhang AT, Cao J et al (2016) Graphene-enhanced cu composite interlayer for contact reaction brazing aluminum alloy 6061. Vacuum 136:142–145
Tian W, Li S, Wang B, Liu J, Yu M (2016) Pitting corrosion of naturally aged aa 7075 aluminum alloys with bimodal grain size. Corros Sci 113:1–16
Xiao X, Mu Z, Pan H, Lou Y (2018) Effect of the lode parameter in predicting shear cracking of 2024-t351 aluminum alloy Taylor rods. International Journal of Impact Engineering 120:185–201
Li S, Dong H, Shi L, Li P, Ye F (2017) Corrosion behavior and mechanical properties of Al-Zn-Mg aluminum alloy weld. Corros Sci 126:265–271
Zhang T, Guo ZR, Yuan FP, Zhang HS (2018) Investigation on the plastic work-heat conversion coefficient of 7075-t651 aluminum alloy during an impact process based on infrared temperature measurement technology. Acta Mechanica Sinica 2:1–7
Zhang P et al (2020) Research on the large plastic deformation damage and shock resistance of 7055 aluminum alloy. JOM:1–8
Zhang H, Li JL, Wang CS, Xiong JT, Zhang FS (2017) Equal-strength precision diffusion bonding of aa6063 aluminum alloy with the surface passivated by a self-assembled monolayer. Int J Mater Res 108(7):571–577
Tiringer U, Kovač J, Milošev I (2017) Effects of mechanical and chemical pre-treatments on the morphology and composition of surfaces of aluminium alloys 7075-t6 and 2024-t3. Corros Sci 119:46–59
Zhang P, Li Y, Liu Y, Zhang Y, Liu J (2020) Analysis of the microhardness, mechanical properties and electrical conductivity of 7055 aluminum alloy. Vacuum 171:109005
Huang R, Riddle M, Graziano D, Warren J, Das S, Nimbalkar S (2016) Energy and emissions saving potential of additive manufacturing: the case of lightweight aircraft components. J Clean Prod 135:1559–1570
Kuwazuru O, Ode K, Yamada M, Kassab AJ, Divo E (2017) Experimental and boundary element method study on the effect of stress on the polarization curve of cast aluminum alloy in sodium chloride solution. Corros Sci 132
Sayğılı H, Güzel F (2016) High surface area mesoporous activated carbon from tomato processing solid waste by zinc chloride activation: process optimization, characterization and dyes adsorption. J Clean Prod 113:995–1004
Severo EA, Guimarães JCFD, Dorion ECH (2017) Cleaner production and environmental management as sustainable product innovation antecedents: a survey in Brazilian industries. Journal of Cleaner Production 142(part 1:87–97
Ping Z, Youqiang W, Wenhui L (2018) Finite element analysis of tc17 Ti alloy under high-speed cutting based on its friction model of deformation zone. The International Journal of Advanced Manufacturing Technology
Arrés MDM, Jiménez AE, Arias-Pardilla J, Martínez-Nicolás G, Bermúdez MD (2016) Electrochemical treatment of aluminium alloy 7075 in aqueous solutions of imidazolium phosphonate and phosphate ionic liquids and scratch resistance of the resultant materials. Tribol Int
Yong JY, Klemeš JJ, Varbanov PS, Huisingh D (2016) Cleaner energy for cleaner production: modelling, simulation, optimisation and waste management. J Clean Prod 111(8):1–1–16
Wu Q, Li DP (2014) Analysis and X-ray measurements of cutting residual stresses in 7075 aluminum alloy in high speed machining. Int J Precis Eng Manuf 15(8):1499–1506
Gao P, Wang X, Liang Z, Xiang J, Xie J (2019) Effects of WC grain size and Co content on microscale wear behavior of micro end mills in aluminum alloy 7075 machining. Int J Adv Manuf Technol 104(11–12):2401–2413
Zhang P, Wang Y, Yu X, Luo H (2019) The mechanical behaviors and energy absorption mechanisms of Al–Cu–Mn alloy under dynamic penetration at wide temperature ranges and large angles. Journal of Alloys and Compounds 152188. https://doi.org/10.1016/j.jallcom.2019.152188
Hao M, Xu D, Feng P (2019) Numerical and experimental investigation of the shear angle in high-speed cutting of al6061-t6. The International Journal of Advanced Manufacturing Technology 100
A QC, B WLA, A YR, A ZZ (2020) 3d Chatter stability of high-speed micromilling by considering nonlinear cutting coefficients, and process damping. J Manuf Process 57:552–565
Acknowledgments
The work was supported by the National Natural Science Foundation of China (Nos. 51705270 and 51575289), the Natural Science Foundation of Shandong Province (No. ZR2016EEP03), and the Technology Project of Higher Education Shandong Province Science (No. J17KA031).
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
All authors declare that there is no conflict of interest.
Additional information
Publisher’s note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Zhang, P., Cao, X., Zhang, X. et al. Machinability and cutting force modeling of 7055 aluminum alloy with wide temperature range based on dry cutting. Int J Adv Manuf Technol 111, 2787–2808 (2020). https://doi.org/10.1007/s00170-020-06177-x
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00170-020-06177-x