Abstract
Organometal halide perovskite semiconductors could potentially be used to create field-effect transistors (FETs) with high carrier mobilities. However, the performance of these transistors is currently limited by the migration of ionic surface defects. Here, we show that a surface cleaning and passivation technique, which is based on a sequence of three solution-based steps, can reduce the concentration of ionic surface defects in halide-based perovskites without perturbing the crystal lattice. The approach consists of an initial cleaning step using a polar/nonpolar solvent, a healing step to remove surface organic halide vacancies and a second cleaning step. The surface treatment is shown to restore clean, near hysteresis-free transistor operation, even if the perovskite films are formed under non-optimized conditions, and can improve room-temperature FET mobility by two to three orders of magnitude compared to untreated films. Our methylammonium lead iodide (MAPbI3) FETs exhibit high n- and p-type mobilities of 3.0 cm2 V−1 s−1 and 1.8 cm2 V−1 s−1, respectively, at 300 K, and higher values (9.2 cm2 V−1 s−1; n-type) at 80 K. We also show that the approach can be used to transform PbI2 single crystals into high-quality, two-dimensional perovskite single crystals.
This is a preview of subscription content, access via your institution
Access options
Access Nature and 54 other Nature Portfolio journals
Get Nature+, our best-value online-access subscription
$29.99 / 30 days
cancel any time
Subscribe to this journal
Receive 12 digital issues and online access to articles
$119.00 per year
only $9.92 per issue
Buy this article
- Purchase on Springer Link
- Instant access to full article PDF
Prices may be subject to local taxes which are calculated during checkout
Similar content being viewed by others
Data availability
The data supporting this paper are available at https://www.data.cam.ac.uk/repository.
References
Lee, M. M., Teuscher, J., Miyasaka, T., Murakami, T. N. & Snaith, H. J. Efficient hybrid solar cells based on meso-superstructured organometal halide perovskites. Science 338, 643–647 (2012).
Burschka, J. et al. Sequential deposition as a route to high-performance perovskite-sensitized solar cells. Nature 499, 316–319 (2013).
Liu, M., Johnston, M. B. & Snaith, H. J. Efficient planar heterojunction perovskite solar cells by vapour deposition. Nature 501, 395–398 (2013).
Zhou, H. et al. Interface engineering of highly efficient perovskite solar cells. Science 345, 542–546 (2014).
Arora, N. et al. Perovskite solar cells with CuSCN hole extraction layers yield stabilized efficiencies greater than 20%. Science 358, 768–771 (2017).
Han, Q. et al. High-performance perovskite/Cu(In,Ga)Se2 monolithic tandem solar cells. Science 361, 904–908 (2018).
Tan, Z. K. et al. Bright light-emitting diodes based on organometal halide perovskite. Nat. Nanotechnol. 9, 687–692 (2014).
Zhao, B. et al. High-efficiency perovskite-polymer bulk heterostructure light-emitting diodes. Nat. Photon. 12, 783–789 (2018).
Wang, N. et al. Perovskite light-emitting diodes based on solution-processed self-organized multiple quantum wells. Nat. Photon. 10, 699–704 (2016).
Dou, L. et al. Solution-processed hybrid perovskite photodetectors with high detectivity. Nat. Commun. 5, 5404 (2014).
Wei, H. et al. Sensitive X-ray detectors made of methylammonium lead tribromide perovskite single crystals. Nat. Photon. 10, 333–339 (2016).
Stranks, S. D. et al. Electron–hole diffusion lengths exceeding 1 micrometer in an organometal trihalide perovskite absorber. Science 342, 341–344 (2013).
Dong, Q. et al. Electron-hole diffusion lengths >175 µm in solution-grown CH3NH3PbI3 single crystals. Science 347, 967–970 (2015).
Xing, G. et al. Long-range balanced electron- and hole-transport lengths in organic–inorganic CH3NH3PbI3. Science 342, 344–347 (2013).
Shi, D. et al. Low trap-state density and long carrier diffusion in organolead trihalide perovskite single crystals. Science 347, 519–522 (2015).
Pazos-Outón, L. M. et al. Photon recycling in lead iodide perovskite solar cells. Science 351, 1430–1433 (2016).
Wang, Y., Zhang, Y., Zhang, P. & Zhang, W. High intrinsic carrier mobility and photon absorption in the perovskite CH3NH3PbI3. Phys. Chem. Chem. Phys. 17, 11516–11520 (2015).
Saidaminov, M. I. et al. High-quality bulk hybrid perovskite single crystals within minutes by inverse temperature crystallization. Nat. Commun. 6, 7586 (2015).
Chen, Y. et al. Extended carrier lifetimes and diffusion in hybrid perovskites revealed by Hall effect and photoconductivity measurements. Nat. Commun. 7, 12253 (2016).
Kim, H. et al. Direct observation of mode-specific phonon-band gap coupling in methylammonium lead halide perovskites. Nat. Commun. 8, 687 (2017).
Karakus, M. et al. Phonon–electron scattering limits free charge mobility in methylammonium lead iodide perovskites. J. Phys. Chem. Lett. 6, 4991–4996 (2015).
Luo, L. et al. Ultrafast terahertz snapshots of excitonic Rydberg states and electronic coherence in an organometal halide perovskite. Nat. Commun. 8, 15565 (2017).
Zhao, T., Shi, W., Xi, J., Wang, D. & Shuai, Z. Intrinsic and extrinsic charge transport in CH3NH3PbI3 perovskites predicted from first-principles. Sci. Rep. 6, 19968 (2016).
Kagan, C. R., Mitzi, D. B. & Dimitrakopoulos, C. D. Organic–inorganic hybrid materials as semiconducting channels in thin-film field-effect transistors. Science 286, 945–957 (1999).
Matsushima, T. et al. Solution-processed organic–inorganic perovskite field-effect transistors with high hold mobilities. Adv. Mater. 28, 10275–10281 (2016).
Gao, Y. et al. Highly stable lead-free perovskite field-effect transistors incorporating linear π-conjugated organic ligands. J. Am. Chem. Soc. 141, 15577–15585 (2019).
Chin, X. Y., Cortecchia, D., Yin, J., Bruno, A. & Soci, C. Lead iodide perovskite light-emitting field-effect transistor. Nat. Commun. 6, 7383 (2015).
Wang, G. et al. Wafer-scale growth of large arrays of perovskite microplate crystals for functional electronics and optoelectronics. Sci. Adv. 1, e1500613 (2015).
Li, D. et al. Size-dependent phase transition in methylammonium lead iodide perovskite microplate crystals. Nat. Commun. 7, 11330 (2016).
Senanayak, S. P. et al. Understanding charge transport in lead iodide perovskite thin-film field-effect transistors. Sci. Adv. 3, e1601935 (2017).
Li, F. et al. Ambipolar solution-processed hybrid perovskite phototransistors. Nat. Commun. 6, 8238 (2015).
Frost, J. M. & Walsh, A. What is moving in hybrid halide perovskite solar cells? Acc. Chem. Res. 49, 528–535 (2016).
Shao, Y. et al. Grain boundary dominated ion migration in polycrystalline organic–inorganic halide perovskite films. Energy Environ. Sci. 9, 1752–1759 (2016).
Yuan, Y. & Huang, J. Ion migration in organometal trihalide perovskite and its impact on photovoltaic efficiency and stability. Acc. Chem. Res. 49, 286–293 (2016).
Burgi, L., Sirringhaus, H. & Friend, R. H. Noncontact potentiometry of polymer field-effect transistors. Appl. Phys. Lett. 80, 2913 (2002).
Birkhold, S. T. et al. Direct observation and quantitative analysis of mobile Frenkel defects in metal halide perovskites using scanning Kelvin probe microscopy. J. Phys. Chem. C 122, 12633–12639 (2018).
Leijtens, T. et al. Mapping electric field-induced switchable poling and structural degradation in hybrid lead halide perovskite thin films. Adv. Energy Mater. 5, 1500962 (2015).
Zhu, X., Lee, J. & Lu, W. D. Iodine vacancy redistribution in organic–inorganic halide perovskite films and resistive switching effects. Adv. Mater. 29, 1700527 (2017).
Eames, C. et al. Ionic transport in hybrid lead iodide perovskite solar cells. Nat. Commun. 6, 7497 (2015).
Azpiroz, J. M., Mosconi, E., Bisquert, J. & Angelis, F. D. Defect migration in methylammonium lead iodide and its role in perovskite solar cell operation. Energy Environ. Sci. 8, 2118–2127 (2015).
Mosconi, E., Meggiolaro, D., Snaith, H. J., Stranks, S. D. & Angelis, F. D. Light-induced annihilation of Frenkel defects in organo-lead halide perovskites. Energy Environ. Sci. 9, 3180–3187 (2016).
Meloni, S. et al. Ionic polarization-induced current–voltage hysteresis in CH3NH3PbX3 perovskite solar cells. Nat. Commun. 7, 10334 (2016).
Choi, H. H., Cho, K., Frisbie, C. D., Sirringhaus, H. & Podzorov, V. Critical assessment of charge mobility extraction in FETs. Nat. Mater. 17, 2–7 (2018).
Wang, J. et al. Investigation of electrode electrochemical reactions in CH3NH3PbBr3 perovskite single-crystal field-effect transistors. Adv. Mater. 31, 1902618 (2019).
Saidaminov, M. I. et al. Suppression of atomic vacancies via incorporation of isovalent small ions to increase the stability of halide perovskite solar cells in ambient air. Nat. Energy 3, 648–654 (2018).
Brenner, T. M. et al. Conversion of single crystalline PbI2 to CH3NH3PbI3: structural relations and transformation dynamics. Chem. Mater. 28, 6501–6510 (2016).
She, X.-J. et al. A vertical organic transistor architecture for fast nonvolatile memory. Adv. Mater. 29, 1604769 (2017).
Zheng, X. et al. Defect passivation in hybrid perovskite solar cells using quaternary ammonium halide anions and cations. Nat. Energy 2, 17102 (2017).
Acknowledgements
X.-J.S. thanks the Cambridge Trust and China Scholarship Council for financial support. H.S. thanks the Engineering and Physical Sciences Research Council (EPSRC) for support through a programme grant (EP/M005143/1). L.C. and B.Z. were also supported by the EPSRC grant. We thank R. Chakalov and R. Beadle for technical support. X.-J.S. is grateful to R.D. Pietro for discussions on early-stage SKPM measurements, to N. Berdunov for resolving experimental problems with the SKPM set-up and to D. Venkateshvaran for LabVIEW programming discussions. J.F.O. acknowledges the EPSRC Nano Doctoral Training Centre (EP/L015978/1) for support.
Author information
Authors and Affiliations
Contributions
X.-J.S. conceived the idea, designed the measurements, conducted and led the majority of the research experiments. X.-J.S. and C.C. fabricated the SKPM samples and FET devices, with B.Z., W.X. and J.P. contributing to the optimization of perovskite fabrications and J.W. contributing to the investigations on electrode selection. Y.L. performed the atomic layer deposition growth. X.-J.S. performed the SKPM and FET studies with assistance from C.C. B.Z. and X.-J.S. performed the XRD investigations. J.F.O., L.C. and X.-J.S. performed SEM studies with discussions from G.D. about the measurements. A.S. performed the PDS characterizations. S.W. contributed to the electrostatic potential simulations. X.-J.S. interpreted the results and established the model. H.S. directed and supervised the project. H.S. and X.-J.S. wrote the manuscript. All authors discussed the results and revised the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Supplementary Information
Supplementary Figs. 1–31 and Discussion sections 1–17.
Rights and permissions
About this article
Cite this article
She, XJ., Chen, C., Divitini, G. et al. A solvent-based surface cleaning and passivation technique for suppressing ionic defects in high-mobility perovskite field-effect transistors. Nat Electron 3, 694–703 (2020). https://doi.org/10.1038/s41928-020-00486-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1038/s41928-020-00486-5
This article is cited by
-
Recent progress with one-dimensional metal halide perovskites: from rational synthesis to optoelectronic applications
NPG Asia Materials (2023)
-
Laser printed microelectronics
Nature Communications (2023)
-
Charge transport in mixed metal halide perovskite semiconductors
Nature Materials (2023)
-
High-performance metal halide perovskite transistors
Nature Electronics (2023)
-
Stabilization of photoactive phases for perovskite photovoltaics
Nature Reviews Chemistry (2023)