Silsesquioxane-Polythiophene Hybrid Copolymer as an Efficient Modifier for Single-Walled Carbon Nanotubes

Gao, Shuxi; Hu, Xiaoyong; Zhang, Lei; Mai, Yuliang; Pang, Hao; Dai, Yongqiang; Liao, Bing

doi:https://doi.org/10.1155/2020/7659405

International Journal of Polymer Science

On this page

Abstract Introduction Results and Discussion Conclusion Data Availability Conflicts of Interest Authors’ Contributions Acknowledgments Supplementary Materials References Copyright Related Articles

Special Issue

Preparation and Application of Conducting Polymer-Based Nanocomposites

View this Special Issue

Research Article | Open Access

Volume 2020 | Article ID 7659405 | https://doi.org/10.1155/2020/7659405

Silsesquioxane-Polythiophene Hybrid Copolymer as an Efficient Modifier for Single-Walled Carbon Nanotubes

Shuxi Gao,¹Xiaoyong Hu,¹Lei Zhang,¹Yuliang Mai,¹Hao Pang,¹Yongqiang Dai,¹and Bing Liao¹

Guest Editor: Feng Wu

Received08 Oct 2019

Accepted30 Dec 2019

Published11 Mar 2020

Abstract

One silsesquioxane-polythiophene hybrid copolymer, with combined star-like structure and intramolecular heterogeneity, was synthesized and sufficiently characterized via various methods, including FTIR, NMR, and SEC measurements. According to the exploration and characterization results, it was much more efficient at modifying SWNTs than its linear analogs in aqueous solution. The hydrophobic silsesquioxane core and PEDOT chains could locally anchor to the surface of the nanotubes, while the soluble flexible copolymer chains extended into the solution and rigid conjugated chains provided some - stacking effect to enhance adhesive force with the conjugated structure of the carbon nanotube, imparting steric stabilization to nanotube dispersion. The noncovalent interaction with SWNTs and solubility in aqueous solution improved the electrochemical characteristics of the modified-SWNT composite and availed for the preparation of a flexible and transparent electroactive film. Accordingly, this kind of silsesquioxane-polythiophene hybrid copolymer will be forwarded to apply to the assembling of flexible optoelectronic devices.

1. Introduction

Carbon nanotubes (CNTs) classified as multiwalled nanotubes (MWNTs) and single-walled nanotubes (SWNTs), upon the wrapped amount of a graphite sheet, have been used in multiple fields, such as composites, optoelectronic devices, field emission display, and energy storage, due to their unique physical, chemical, and structural properties [1–3]. However, the poor solubility and dispersibility of CNTs in both aqueous and organic media are major barriers for CNT applications, especially for SWNTs, as a result of the strong Van der Waals interaction between CNTs [4–8].

In order to obtain fine dispersion of CNTs in aqueous solution, various approaches that primarily paid attention on dispersion and dissolution properties have been developed, including covalent surface and noncovalent surface functionalization strategies [9–14]. Noncovalent modification has received considerable attraction for the modification of surface properties with no damage to the sp2 structure of the nanotube surface, involving - interaction, hydrogen bonds, and ionic interaction by employing micromolecule surfactants or amphiphilic copolymers as modifiers.

In previously published works [15–17], copolymeric structures have the advantages of promoting CNTs’ dispersibility in a wide range of solvents depending on the great affinity of hydrophobicity of the copolymers for the nanotube, and it has been demonstrated in several literatures that various polymers have effectively enhanced the long-term dispersion stability of CNTs through different types of interactions. Furthermore, the versatile chemistry of copolymer modifiers allows for tailoring and functionalizing polymer/nanotube composites with finely various properties, enhancing the application of CNTs, especially in fabricating carbon-based flexible transparent electrodes [18–21].

Herein, a novel star-shaped copolymer is reported to stabilize single-walled carbon nanotubes (SWNTs) in aqueous solution through noncovalent interactions. In the previous work of our team [4], we had adequately demonstrated that an octopus-shaped amphiphilic copolymer could generate a stable and uniform physical adsorption layer on a nanotube, yielding much better efficiencies toward functionalization and dispersion, and multiple binding sites could assemble larger polymer aggregation that locally anchored onto the nanotube surface compared to its linear analogs that sequentially reduced the hydrophobicity of the sidewall surface for minimizing the connection with water and other tubes.

Therefore, we were motivated to extend SWNT modification to a silsesquioxane- (SQ-) cored star-like conjugated copolymer. Firstly, SQ would be convenient to constitute the core of star polymers. Secondly, the hydrophobic silsesquioxane cage could impart to amphiphilic copolymers’ hydrophobic-hydrophobic interactions with CNTs [4]. Finally, the conjugated segments could generate - interaction between conjugated chains and the hybridized CNT surface [22–24].

Herein, we report a star-like conjugated copolymer T₁₀-(PDMA-b-PMA)-PEDOT (P5-5) standing on hydrophobic cage-like decakis(methacryloxypropyl) silsesquioxane (T₁₀) and the linear analog PDMA-b-PMA-b-PEDOT, to explore the mechanism of SQ-based star configuration and conjugated system generating the efficient dispersion of SWNTs.

2. Experimental Section

2.1. Materials

N,N-(Dimethylamine)ethyl methacrylate (DMA, Aladdin, 99%) and methyl acrylate (MA, Aladdin, 99%) were purified through passing over the basic aluminum oxide column. 2,2-Azobisisobutyronitrile (AIBN, Aladdin, 98%) was recrystallized twice in ethanol before use. Cage-like decakis(methacryloxypropyl) silsesquioxane (T₁₀) was prepared in our laboratory [25]. Single-walled carbon nanotubes (SWNTs) were purchased from Aladdin (carbon , : ).

2.2. Synthesis Processes

As described in Scheme 1, the experiments began from the precise synthesis of a T₁₀-(PDMA-b-PMA)-Th polymer precursor (M5-5) that contained five thiophene groups. The polymer precursor was subsequently copolymerized with the EDOT monomer to form PEDOT branches grafted from the hydrophobic T₁₀ core, and the extension of the conjugated system was realized at the interface between the immiscible organic and aqueous phases by a modified interfacial synthesis protocol (MIP) [24]. For comparative purposes and to further explore the dispersing efficiency, the linear analog was prepared by the RAFT method and subsequently grafted the EDOT monomer from the thiophene group (denoted as PDMA-b-PMA-b-PEDOT) in the MIP process.

The specific experimental procedures were described in supporting information with structural characterization information for all polymers and reaction intermediates.

2.3. Characterization

Size exclusion chromatography (SEC) was conducted at 35°C by a Waters 1515 series system equipped with Styragel HR4 and HR3 columns and a Waters 2414 refractive index detector. The system was calibrated by narrowly dispersed polystyrene standards, and HPLC-grade DMF was used for the mobile phase at 0.60 mL/min. Nuclear Magnetic Resonance (¹H NMR) spectra were characterized in deuterated chloroform by using a Bruker DMX-400 spectrometer with a Varian probe. Infrared spectra were obtained with a Fourier transform infrared spectrometer using the KBr method (FTIR, Bruker Tensor 27, Germany). The UV-vis spectra of samples were measured in THF solution (UV-1800, Shimadzu Co., Japan). Weight loss temperatures of the products were determined by using a thermogravimetric analyzer (TGA, Netzsch TG209F3) at 10°C/min under the nitrogen flow rate of 40 mL/min from 50–700°C. Transmission electron microscopy was performed on a high-resolution transmission electron microscope (HR-TEM, Tecnai G2 F20 S-TWIN). The electrochemical performance was determined with CHI660E employing a standard three-electrode electrochemical cell that consisted of a glassy carbon electrode as the working electrode, a saturated calomel electrode (SCE) as the reference electrode, and a platinum wire as the counter electrode. Cyclic voltammetry was carried out relative to an SCE reference electrode at different scan rates (20–100 mV/s), and the potential window of cycling was confined between -1 and 1 V. The electrochemical impedance spectroscopy (EIS) was performed in the frequency range of 10⁵ to 10⁻² Hz with the signal amplitude of 5 mV against the open-circuit potential. The electrical conductivity was subjected to the standard four-point probe method at ambient temperature (RTS-8, Four Probes Tech).

3. Results and Discussion

3.1. Chemical Structural Characterization

Decafunctionalized SQ (T₁₀) was selected to construct the star-shaped copolymer because this viscous amorphous liquid cluster compound was synthesized with high yield, which could be afforded in large-scale use. In addition, T₁₀ offers more available functionalities for multiple grafting of the polymer chains to the core, and it also effectively interferes in strong - interactions between neighboring conjugated chains, resulting in solution processability for the hybrid polymer [24].

In order to form the star-shaped copolymer precursor M5-5, a one-pot continuous reaction sequence was used to prepare the asymmetric T₁₀ with five thiophene groups (T₁₀(5-5)), including a nucleophilic opening of the thiolactone by aminolysis and then a radical thiol-ene conjugation. Due to the extremely high reactivity of thiyl radical addition toward the carbon-carbon double bond, excess thiolactone could promote the conversion rate of amine and ensure complete conversion [26]; PDMA-b-PMA obtained by reversible addition-fragmentation transfer (RAFT) polymerization was linked to T₁₀(5-5) by thiol-ene conjugation after nucleophilic cleavage of the thiocarbonyl group.

The linear copolymer precursor was obtained by a typical RAFT polymerization procedure under the regulation of DTTC-Th as an efficient RAFT agent with an end-capped thiophene group.

Our particular synthetic approach (MIP) for the growth of conjugated chains relied on the reaction of the precursors and monomer by multicomponent oxidative coupling at the interface, which suppresses the interdiffusion of a monomer and an oxidant in the confined region to avoid uncontrolled homopolymerization, and also on the diffusion of the resulting copolymer down to the bottom phase due to the highly hydrophilic nature of the flexible arms and instability enhancement at the interface as the extension of the conjugated system, while being convenient for the rearrangement of unreacted precursors at the interface (Scheme 2).

¹H NMR, FTIR, UV-vis, and GPC analyses confirmed that the star-shaped conjugated copolymer and linear analogs were obtained with precise structure and low narrow molecular weight distribution, and the supporting information described the detailed experimental process and results (Figures S1–S8). All chemical structures are illustrated in Scheme 1, and the structural data are listed in Table 1.

3.2. Functionalized CNTs with the Silsesquioxane-Polythiophene Hybrid Copolymer and Its Linear Analog

Multiple modifier-functionalized SWNTs were obtained while avoiding inclusion of dissociative copolymers through multiple centrifugation and washing steps, yielding PDMA-b-PMA-Th with SWNTs (M1) and PDMA-b-PMA-b-PEDOT with SWNTs (M2) and P5-5 with SWNTs. As we know, - stacking interactions are strong interfacial noncovalent interactions between modifiers and CNTs, as it was indicated that conjugation groups located at the flexible chains of the copolymer resulted in higher adhesion [8]. For the copolymer/CNT composites, the employed thiophene moieties in the flexible PDMAEMA could endow the copolymer strong - interactions with CNT, functioning as interfacial linkers between the modifiers and SWNTs. Thus, the anchor groups at the flexible chains of modifiers could be adhered tightly along the CNT surface to form stronger interfacial interaction in the modifier-CNT complex.

3.2.1. Transmission Electron Microscopy (TEM)

For the purpose to confirm the strong and stable interfacial interactions between SWNTs and modifiers, we conducted transmission electron microscopy (TEM) analysis. As observed in Figure 1, all nanotubes retained their structural integrity, revealing that no damage was evident to the nanotube walls in the experiment; the modified SWNTs apparently tended to exist as individuals or small bundles, especially for P5-5/SWNTs, despite well-known property that the pristine SWNTs would aggregate and be entangled to form large ropes without any modification. In addition, these star-shaped copolymer-modified SWNTs had more individually dispersed nanotubes and less bundles, compared to linear copolymer-modified SWNTs; moreover, the star-shaped copolymer aggregates homogeneously adhered to the surface of the nanotube without large agglomeration. From the figures of individual SWNTs (Figure 1, insets), many arc-like bulges were observed on the surface of P5-5 modified nanotubes, attributed commonly to regions of irregular copolymer coating along the lengths; however, many linear copolymer-modified nanotubes were still bounded together, which might be due to the disorderly stacking of a large copolymer and resulting in the lack of relatively strong noncovalent forces to stabilize individual tubes. Of the two linear copolymer-modified nanotubes, PDMA-b-PMA-b-PEDOT-modified SWNTs had less entanglement (Figure 1(b)).

(a)

(b)

(c)

3.2.2. Fourier Transform Infrared Spectroscopy (FTIR)

Direct evidences of modifier-nanotube interactions could also be obtained using Fourier transform infrared spectroscopy (FTIR) after dispersion and centrifugation. As displayed in FTIR spectra of pristine SWNTs and modified SWNTs (Figure 2), the IR absorption bands occurred with maxima around 3450 cm^-1, which correspond to the –OH stretching vibration of surface hydroxyl groups on CNTs and the adsorbed water molecules. An intense band at 1636 cm^-1 appeared in all samples was assigned to the stretching vibration of carbonyl groups (C=O) present in carboxylic acids and conjugated C=C groups on the nanotubes. Besides, in the spectra of modified SWNTs, an obvious C=O stretching vibration of ester groups in polymer chains (ca. 1718 cm^-1) and C–O stretching vibrations (ca. 1233 and 1149 cm^-1) were observed; the observation suggested that the modifiers were still effectively wrapped onto the nanotube surface by noncovalent interactions after rinsing. Compared to the spectra of modifiers (Figure S9), the characteristic peak of PEDOT chains (ca. 850 and 988 cm^–1) shifted toward higher wavenumbers due to the electron-deficient defects of the nanotube surface and might confirm the -conjugated stacking between the PEDOT segment and the nanotube surface, revealing the adherence of copolymers to the nanotube surface.

3.3. Dispersion Properties

3.3.1. UV-vis Spectrogram

For the assessment of the variation of dispersion efficiency of SWNTs modified by the star-like copolymer and its linear analogs in aqueous solution, three modified-SWNT (m-SWNT) dispersions (M1, M2, and M3) were prepared and investigated by using a UV-vis spectrogram. Figure S10 shows the absorption profiles of SWNT dispersions in a modifier THF/water solution; nearly no obvious signal peaks could be detected for SWNT dispersion modified by linear copolymers (M1, M2) in the UV-vis region. Moreover, there were no evident changes in the absorption spectra with or without the modifiers, causing us to tentatively suppose that the nanotube structure had not been destroyed in the solubilization process. In the absorption profiles for PDMA-b-PMA-b-PEDOT solution and P5-5 solution (Figure 3), a wide absorption band from 450 to 550 nm was observed in the spectra, which could be attributed to the characteristic - transition in conjugated polythiophene backbones [27].

Furthermore, we presumed that the amount of the nanotube stabilized by modifiers in dispersion would be reduced after centrifugal separation, and the UV absorption intensity of supernatants could represent the amount of well-stable nanotube suspension. As indicated from Figure 3, the absorption intensity of the supernatants for both PEDOT-grafted modifiers (M2 and M3) was enhanced significantly in comparison with the original polymer solutions diluted in the same ratio, despite the fact that it was not obvious in comparison with the M1 supernatant with PDMA-b-PMA-Th solution; in addition, the M3 supernatant had the maximum enhancement of absorption intensity. The variation of dispersion efficiency resulted from the noncovalent modification, which was probably relevant to the configuration, the silsesquioxane cage, and the PEDOT segments.

3.3.2. Visual Sedimentation

It was well known that pristine SWNTs could not be stabilized in aqueous solution without the help of a modifier, despite the vigorous ultrasonication, due to the highly specific surface area and hydrophobic sidewall surface. For the modified SWNTs, the modification ability of polymers on SWNTs could be visually assessed by conducting a sedimentation experiment to compare the stability of modified-SWNT dispersions (Figure S11). All modifiers had the ability to enhance the dispersity of SWNTs, especially PEDOT-grafted copolymers. In particular, it seemed that the star-shaped copolymer/SWNT dispersion had more stability than linear ones, which was observed in a vial over 10 days without any precipitation. Therefore, we inferred that the SQ cage and PEDOT segments played key roles for noncovalent functionalization of nanotubes: Firstly, due to the hydrophobic nature of SQ cores and PEDOT segments, they should be gathered close to the surface of the carbon tube. Secondly, the poor solubility and conjugated nature of PEDOT imparted effective physisorption between the stabilizer and the conjugated structure of the nanotube. Thirdly, thanks to the tentacles of multiarm SQ-based copolymers with rigid arms, the solvation segments would produce more opportunities to generate a great affinity for solvent, which primarily decreased the interfacial tension of nanotubes by minimizing their contacts with water [28], and more hydrophobic segments could provide more opportunities to interact with the nanotube surface. This speculation can be strongly supported by the fact that the SQ-based star copolymer employing multi-PEDOT chains compared to its linear analogs resulted in an improved functional capability to stabilize SWNTs.

3.3.3. Thermogravimetric Analysis (TGA)

For the purpose of obtaining a more quantitative picture of the extent of nanotube functionalization, thermogravimetric analysis (TGA) was conducted to evaluate the thermodynamic property of copolymer/SWNT complexes and further estimate the well-adhered polymers on the nanotube surface under an N₂ atmosphere after centrifugation; all thermal property data are listed in Table 2. The copolymers (PDMA-b-PMA-Th, PDMA-b-PMA-b-PEDOT, and P5-5) and copolymer/SWNTs complexes (M1 residue, M2 residue, and M3 residue) (Figure 4) both indicated a distinct two-step thermal degradation, which might be caused by the loss of ester bonds and the decomposition of the backbone in the temperature range of 200–500°C, while no mass loss of the SWNTs was observed in the same temperature range.

Table 2: Thermogravimetric analysis data of various copolymers and modified-SWNT residues.

The highest decomposition temperature at the maximum degradation rate in the second stage for thermal degradation of the framework structure of P5-5 indicated that the star-shaped configuration and the presence of T₁₀ contributed to the increase in thermostability (Figure S12) [29]. The lower decomposition temperature of the PEDOT homopolymer might result in the lower decomposition temperature in the second stage of the PDMA-b-PMA-b-PEDOT trace (Figure S13), and the successful grafting of PEDOT segments from the thiophene group of PDMA-b-PMA-Th was further verified.

In addition, the values of PDMA-b-PMA-Th, PDMA-b-PMA-b-PEDOT, and P5-5 were 5.5, 5.1, and 12.6%, and the values of M1 residue, M2 residue, and M3 residue were 72.2, 60.4, and 56.1, respectively. As indicated in Figure 3 (TGA traces), the copolymers would be completely decomposed over 500°C; the mass loss from the residues of copolymer/SWNT complexes during thermal degradation could be used to estimate the amount of well-wrapped copolymers on the nanotubes in dispersion, and it was, respectively, about 25%, 35%, and 44% corresponding to the loss of PDMA-b-PMA-Th, PDMA-b-PMA-b-PEDOT, and P5-5 between 200°C and 500°C deducing that the mass loss of SWNTs, further combined with UV spectra, could be used to evaluate the functional capability of modifiers to stabilize SWNTs.

M1 residue had the least mass loss with the lowest dispersion efficiency of M1; that is, most of PDMA-b-PMA-Th was washed out due to the unstable physisorption on SWNTs; it implied that the grafting of PEDOT segments played an important role to form stable interactions with nanotubes in solution, which endowed more stacking interaction and hydrophobicity between modifiers and the surface of the nanotube. As expected, M3 residue had the largest mass loss compared with the linear ones with the best dispersion efficiency of M3, indicating that more P5-5 was well wrapped on the surface of nanotubes resulting in the largest polymer content in residue, thus providing strong support for the previous proposal: more possibilities would be obtained by introducing more solvation segments to generate a great affinity for solvent, and more hydrophobic segments and conjugated segments could provide more opportunities and -stacking to interact with the nanotube, which powerfully enhanced adhesion on the surface to avoid dissolving even during several washing steps.

3.3.4. Mechanism

On the basis of the above results, the possible mechanism for elucidating the interaction between SWNTs and copolymers in Figure 5 was put forward. Thanks to the hydrophobic interaction and - stacking system between star-shaped copolymers and the sidewall, originating from the hydrophobic CSQ cores and conjugated PEDOT segments, the modifiers were readily adsorbed onto the surface of nanotubes by forming relatively strong noncovalent forces, and the other flexible solvable tentacles on the opposite side of the carbon tube had to stretch to the solvent as linear “buoys” due to the steric hindrance endowed by silsesquioxane cages. Thereby, a mass of spherical modifiers was inclined to absorb onto the sidewall to form arc-shaped copolymer aggregation which could decrease the hydrophobicity of the sidewall for minimizing the direct contact with water and other tubes. Meanwhile, these “buoys” tremendously enhanced the solubility of SWNTs in aqueous solution, thus causing well-dispersed SWNTs. In contrast, linear modifiers would be irregularly distributed in solvent due to lack of restrictions from the CSQ cage; therefore, the solvable copolymer chains would wrap the nanotube by generating hydrogen bond interactions. Although the PEDOT chains in PDMA-b-PMA-b-PEDOT could provide some - stacking effect to enhance adhesive force with the graphite structure of the surface, but the linear copolymers were difficult to form well-organized aggregations to prevent bundling of tubes.

(a)

(b)

3.4. Electrochemical Property

The electrochemical characteristics of thin films prepared by spin coating from copolymer solutions and the supernatant of modified-SWNT dispersions were determined to provide information about the structure of copolymers and dispersion efficiency. The quasi-rectangle-shaped cyclic voltammetry (CV) curves of PDMA-PMA-b-PEDOT P5-5 in Figure S14 were similar to those of soluble PEDOT analogs [30], the curves indicated similar chemically reversible signals during the process of positive and negative scans, and low potentials of the current onsets verified the highly electron-rich nature of the polymer films. As shown in the CV curves, a negative shift was observed in the oxidation potential () values for PDMA-b-PMA-b-PEDOT (0.84 V) and P5-5 (0.75 V), possibly due to the larger conjugation system in P5-5. In addition, the larger curve area in the P5-5 film indicated that it had a higher specific capacitance that was imparted by the more PEDOT chains for facilitating ion motion.

In order to further study the stabilizing effect endowed by the conjugation and configuration of modifiers, which could be reflected by the electrochemical variation of modified-SWNT composite films, cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS) measurements were conducted on the composite films. From Figure 6(a), CV curves of the P5-5/SWNT composite film and PDMA-b-PMA-b-PEDOT/SWNT composite film showed a quasirectangle shape with a couple of peaks, indicating an electrical double-layer capacitance originated from the redox reactions of PEDOT chains [31]. As we know, a large surface area and good electrical conductivity may enhance capacity properties, and the curve area of the P5-5/SWNT composite film was greater than that of the PDMA-b-PMA-b-PEDOT/SWNT composite film and PDMA-b-PMA-Th/SWNT composite film; it was clearly indicated that the hybrid copolymer, P5-5, possesses maximum PEDOT segments and star configuration, which was beneficial to facilitating ion motion to increase the specific capacitance of the composite film.

(a)

(b)

Furthermore, the internal resistance of modified-SWNT films, arising from the physical contact between components and the electron transfer resistance between the active materials and the substrate, could reflect the adhesion and - stacking system between copolymers and the nanotube [32–34]. Therefore, electrochemical impedance spectroscopy (EIS) measurements were performed from 10⁵ Hz to 0.01 Hz. As shown in Figure 6(b), the resistance of the electrolyte () corresponded to the intercept of the Nyquist diagrams on the real axis; the charge transfer resistance () on the electrode was represented on the diameter of the semicircle in the Nyquist plots; the Warburg resistance () was associated with the slope of the straight line portion in the Nyquist plots at low frequency, correlating with the frequency dependence of ion diffusion to the electrode interface in the electrolyte. Obviously, values for the P5-5/SWNT composite film (12.7 Ω), PDMA-b-PMA-b-PEDOT/SWNT composite film (12.9 Ω), and PDMA-b-PMA-Th/SWNT composite film (13.4 Ω) were quite similar for the same electrochemical system. Predictable results, in which values were in the order of the P5-5/SWNT composite film (76 Ω) < PDMA-b-PMA-b-PEDOT/SWNT composite film (116 Ω) < PDMA-b-PMA-Th/SWNT composite film (>186 Ω), indicated that PEDOT chains and silsesquioxane cages tended to assist the charge migration, while further implying that the star-shaped copolymer could stabilize more nanotubes via more - interaction and hydrophobic-hydrophobic interaction. The value for the P5-5/SWNT composite film was larger than that of PDMA-b-PMA-b-PEDOT/SWNTs and PDMA-b-PMA-Th/SWNTs, which demonstrated good accessibility of the electrolyte ions to the P5-5/SWNT electrode in the participation of robust silsesquioxane cages on the surface. These EIS results supported the CV analyses of the enhanced electrochemical performance of the P5-5/SWNT composite film and also echoed the analyses of UV spectra and TEM; that is, the SQ-based star-shaped copolymer with PEDOT segments could tightly adhere on the surface to stabilize more nanotubes in aqueous solution.

4. Conclusion

In summary, one star-shaped silsesquioxane-polythiophene hybrid modifier (P5-5) for SWNTs was successfully synthesized via a modified interfacial synthesis protocol. The visual sedimentation indicated that the P5-5 showed excellent ability to stabilize SWNTs in aqueous solution, and direct evidences of modifier/SWNT interactions were verified by UV-vis, FTIR, TEM, and TGA, which demonstrated that the amphiphilic hybrid copolymer was much more efficient at modifying SWNTs than its linear analogs. The possible mechanism for elucidating the noncovalent interaction between SWNTs and the star-shaped copolymer was that the silsesquioxane core and conjugated PEDOT chains locally anchored onto the nanotube surface due to their hydrophobicity nature, while the flexible copolymer chains stretched into aqueous solution; in addition, the formation of amphiphilic copolymer aggregations, which is convex over the sidewall surface, sequentially reduced the hydrophobic area for minimizing their contact with water and other tubes and thus provided hydrophilic “buoys” to enhance the solubility of SWNTs in aqueous solution. The electrochemical properties indicated that PEDOT chains and silsesquioxane cages tended to facilitate the charge migration due to the electrochemical activity and functional capability of P5-5.

Data Availability

The data used to support the findings of this study are included within the article.

Conflicts of Interest

The authors declare that they have no conflicts of interest.

Authors’ Contributions

Shuxi Gao and Xiaoyong Hu contributed equally to this work.

Acknowledgments

The authors gratefully acknowledge the financial support from the China Postdoctoral Science Foundation (2019M662819) and the Guangdong Academy of Sciences Project of Science and Technology Development (2018GDASCX-1011) and the material support from Professor Kai Xu’s group (Guangzhou Institute of Chemistry, Chinese Academy of Sciences).

Supplementary Materials

The only supplied supporting information consists of 14 pages (single column) including 14 figures. It contained the detailed description of the experimental process and some additional results for accurate argument. (Supplementary Materials)

References

S. Iijima, “Helical microtubules of graphitic carbon,” Nature, vol. 354, no. 6348, pp. 56–58, 1991.
View at: Publisher Site | Google Scholar
R. H. Baughman, A. A. Zakhidov, and W. A. de Heer, “Carbon nanotubes−the route toward applications,” Science, vol. 297, no. 5582, pp. 787–792, 2002.
View at: Publisher Site | Google Scholar
M. Yang, V. Koutsos, and M. Zaiser, “Interactions between polymers and carbon nanotubes: a molecular dynamics study,” The Journal of Physical Chemistry B, vol. 109, no. 20, pp. 10009–10014, 2005.
View at: Publisher Site | Google Scholar
S. Gao, Z. Yu, K. Xu et al., “Silsesquioxane-cored star amphiphilic polymer as an efficient dispersant for multi-walled carbon nanotubes,” RSC Advances, vol. 6, no. 36, pp. 30401–30404, 2016.
View at: Publisher Site | Google Scholar
A. Di Crescenzo, M. Aschi, and A. Fontana, “Toward a better understanding of steric stabilization when using block copolymers as stabilizers of single-walled carbon nanotubes (SWCNTs) aqueous dispersions,” Macromolecules, vol. 45, no. 19, pp. 8043–8050, 2012.
View at: Publisher Site | Google Scholar
N. A. Rice and A. Adronov, “Supramolecular interactions of high molecular weight poly (2,7-carbazole) s with single-walled carbon nanotubes,” Macromolecules, vol. 46, no. 10, pp. 3850–3860, 2013.
View at: Publisher Site | Google Scholar
A. Habibnejad Korayem, M. R. Barati, G. P. Simon et al., “Transition and stability of copolymer adsorption morphologies on the surface of carbon nanotubes and implications on their dispersion,” Langmuir, vol. 30, no. 33, pp. 10035–10042, 2014.
View at: Publisher Site | Google Scholar
K. Y. Cho, Y. S. Yeom, H. Y. Seo et al., “Rational design of multiamphiphilic polymer compatibilizers: versatile solubility and hybridization of noncovalently functionalized CNT nanocomposites,” ACS Applied Materials & Interfaces, vol. 7, no. 18, pp. 9841–9850, 2015.
View at: Publisher Site | Google Scholar
P.-C. Ma, N. A. Siddiqui, G. Marom, and J.-K. Kim, “Dispersion and functionalization of carbon nanotubes for polymer-based nanocomposites: a review,” Composites Part A: Applied Science and Manufacturing, vol. 41, no. 10, pp. 1345–1367, 2010.
View at: Publisher Site | Google Scholar
H. Abbasi, M. Antunes, and J. I. Velasco, “Recent advances in carbon-based polymer nanocomposites for electromagnetic interference shielding,” Progress in Materials Science, vol. 103, pp. 319–373, 2019.
View at: Publisher Site | Google Scholar
A. S. R. Bati, L. Yu, M. Batmunkh, and J. G. Shapter, “Recent Advances in Applications of Sorted Single‐Walled Carbon Nanotubes,” Advanced Functional Materials, vol. 29, no. 30, p. 1902273, 2019.
View at: Publisher Site | Google Scholar
M. W. Chik, Z. Hussain, M. Zulkefeli et al., “Polymer-wrapped single-walled carbon nanotubes: a transformation toward better applications in healthcare,” Drug Delivery and Translational Research, vol. 9, no. 2, pp. 578–594, 2019.
View at: Publisher Site | Google Scholar
K.-t. Lau, C. Gu, and D. Hui, “A critical review on nanotube and nanotube/nanoclay related polymer composite materials,” Composites Part B: Engineering, vol. 37, no. 6, pp. 425–436, 2006.
View at: Publisher Site | Google Scholar
A. S. Christensen, T. Kubař, Q. Cui, and M. Elstner, “Semiempirical quantum mechanical methods for noncovalent interactions for chemical and biochemical applications,” Chemical Reviews, vol. 116, no. 9, pp. 5301–5337, 2016.
View at: Publisher Site | Google Scholar
Y. Zhou, R. Azumi, and S. Shimada, “A highly durable, stretchable, transparent and conductive carbon nanotube–polymeric acid hybrid film,” Nanoscale, vol. 11, no. 9, pp. 3804–3813, 2019.
View at: Publisher Site | Google Scholar
Y.-L. Zhao, N. Ullah, S. Chen, and R.-Q. Zhang, “n → π interaction promoted charge carrier transfer between helical SWNTs and a 4-(1-pyrenyl) phenyl group,” The Journal of Physical Chemistry C, vol. 123, no. 22, pp. 13976–13982, 2019.
View at: Publisher Site | Google Scholar
P. Bilalis, D. Katsigiannopoulos, A. Avgeropoulos, and G. Sakellariou, “Non-covalent functionalization of carbon nanotubes with polymers,” RSC Advances, vol. 4, no. 6, pp. 2911–2934, 2014.
View at: Publisher Site | Google Scholar
L. V. Sigolaeva, T. V. Bulko, M. S. Kozin et al., “Long-term stable poly(ionic liquid)/MWCNTs inks enable enhanced surface modification for electrooxidative detection and quantification of dsDNA,” Polymer, vol. 168, pp. 95–103, 2019.
View at: Publisher Site | Google Scholar
G. Zhang, M. McBride, N. Persson et al., “Versatile interpenetrating polymer network approach to robust stretchable electronic devices,” Chemistry of Materials, vol. 29, no. 18, pp. 7645–7652, 2017.
View at: Publisher Site | Google Scholar
Z.-H. Jin, Y.-L. Liu, J.-J. Chen, S.-L. Cai, J.-Q. Xu, and W.-H. Huang, “Conductive polymer-coated carbon nanotubes to construct stretchable and transparent electrochemical sensors,” Analytical Chemistry, vol. 89, no. 3, pp. 2032–2038, 2017.
View at: Publisher Site | Google Scholar
Y. Huang, Y. Wang, L. Gao, X. He, P. Liu, and C. Liu, “Characterization of stretchable SWCNTs/Lycra fabric electrode with dyeing process,” Journal of Materials Science: Materials in Electronics, vol. 28, no. 5, pp. 4279–4287, 2017.
View at: Publisher Site | Google Scholar
L. Yu, C. Shearer, and J. Shapter, “Recent development of carbon nanotube transparent conductive films,” Chemical Reviews, vol. 116, no. 22, pp. 13413–13453, 2016.
View at: Publisher Site | Google Scholar
I. A. Kinloch, J. Suhr, J. Lou, R. J. Young, and P. M. Ajayan, “Composites with carbon nanotubes and graphene: an outlook,” Science, vol. 362, no. 6414, pp. 547–553, 2018.
View at: Publisher Site | Google Scholar
S. Gao, K. Xu, X. Gui, L. Sun, and L. Liu, “Synthesis of soluble silsesquioxane–polythiophene hybrid copolymers with a controlled morphology,” ACS Applied Polymer Materials, vol. 1, no. 3, pp. 437–451, 2019.
View at: Publisher Site | Google Scholar
J. Peng, K. Xu, H. Cai et al., “Can an intact and crystalline octakis(methacryloxypropyl) silsesquioxane be prepared by hydrolysis-condensation of a trimethoxysilane precursor?” RSC Advances, vol. 4, no. 14, pp. 7124–7131, 2014.
View at: Publisher Site | Google Scholar
H. Willcock and R. K. O'Reilly, “End group removal and modification of RAFT polymers,” Polymer Chemistry, vol. 1, no. 2, pp. 149–157, 2010.
View at: Publisher Site | Google Scholar
J. F. Ponder Jr., A. M. Österholm, and J. R. Reynolds, “Designing a soluble PEDOT analogue without surfactants or dispersants,” Macromolecules, vol. 49, no. 6, pp. 2106–2111, 2016.
View at: Publisher Site | Google Scholar
Z. Iatridi and C. Tsitsilianis, “pH responsive MWCNT–star terpolymer nanohybrids,” Soft Matter, vol. 9, no. 1, pp. 185–193, 2013.
View at: Publisher Site | Google Scholar
S. Majeed, V. Filiz, S. Shishatskiy, J. Wind, C. Abetz, and V. Abetz, “Pyrene-POSS nanohybrid as a dispersant for carbon nanotubes in solvents of various polarities: its synthesis and application in the preparation of a composite membrane,” Nanoscale Research Letters, vol. 7, no. 1, p. 296, 2012.
View at: Publisher Site | Google Scholar
H. Zhang, T.-T. Lu, W.-Y. Lai et al., “Pyrene-cored starburst oligofluorenes with diphenylamine end-cappers: design, synthesis, stabilized optical gain, and lasing properties,” The Journal of Physical Chemistry C, vol. 121, no. 49, pp. 27569–27579, 2017.
View at: Publisher Site | Google Scholar
T. Goda, M. Toya, A. Matsumoto, and Y. Miyahara, “Poly(3,4-ethylenedioxythiophene) bearing phosphorylcholine groups for metal-free, antibody-free, and low-impedance biosensors specific for C-reactive protein,” ACS Applied Materials & Interfaces, vol. 7, no. 49, pp. 27440–27448, 2015.
View at: Publisher Site | Google Scholar
C. Wei, W. Zhang, Y. Zhou et al., “High-performance ternary π-conjugated copolymers containing diarylethylene units: synthesis, properties, and study of substituent effects on molecular aggregation and charge transport characteristics,” Journal of Materials Chemistry C, vol. 7, no. 2, pp. 362–370, 2019.
View at: Publisher Site | Google Scholar
Z. Zhou, C. Gu, C. Chen, P. Zhao, Y. Xie, and J. Fei, “An ultrasensitive electrochemical sensor for quercetin based on 1-pyrenebutyrate functionalized reduced oxide graphene /mercapto-β- cyclodextrin /Au nanoparticles composite film,” Sensors and Actuators B: Chemical, vol. 288, pp. 88–95, 2019.
View at: Publisher Site | Google Scholar
P. Zhao, M. Ni, C. Chen et al., “Stimuli-enabled switch-like paracetamol electrochemical sensor based on thermosensitive polymer and MWCNTs-GQDs composite nanomaterial,” Nanoscale, vol. 11, no. 15, pp. 7394–7403, 2019.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2020 Shuxi Gao et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

349

Downloads

954

Citations