Effect of spheroidization of cementite in ductile cast iron

  • Published:
International Journal of Minerals, Metallurgy and Materials Aims and scope Submit manuscript

Abstract

The research aims to provide an alternative to austempering treatment of ductile cast iron with a simple and cost-effective heat-treatment process. This goal was accomplished by applying a simple one-step spheroidization heat treatment to the as-cast ductile iron, which would normally possess a coarse pearlitic microstructure to a significant extent. Spheroidization experiments involving isothermal holding below the lower critical temperature (A1) were conducted followed by standard mechanical testing and microstructural characterization for an experimental ductile iron. After improving the spheroidization holding time at a given temperature, the work shows that the ductility and toughness of an as-cast ductile iron can be improved by 90% and 40%, respectively, at the cost of reducing the tensile strength by 8%. Controlled discretization of the continuous cementite network in pearlitic matrix of the ductile iron is deemed responsible for the improved properties. The work also shows that prolonged holding time during spheroidization heat treatment leads to degradation of mechanical properties due to the inhomogenous microstructure formation caused by heterogeneous decomposition and cementite clustering in the material. The main outcome of this work is the demonstration of ductile cast iron’s necking behavior due to spheroidization heat treatment.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. D.M. Stefanescu, A history of cast iron, [in] D.M. Stefanescu, ed., Cast Iron Science and Technology, ASM Handbook, Vol. 1A, ASM International, Materials Park, OH, 2017, p. 3.

    Chapter  Google Scholar 

  2. M. de Bouw, I. Wouters, J. Vereecken, and L. Lauriks, Iron and steel varieties in building industry between 1860 and 1914 — A complex and confusing situation resolved, Constr. Build. Mater., 23(2009), No. 8, p. 2775.

    Article  Google Scholar 

  3. F. Iacoviello, V.D. Cocco, and G. Favaro, Pearlitic ductile cast iron: Mechanical properties gradient analysis in graphite elements, Procedia Struct. Integrity, 9(2018), p. 9.

    Article  Google Scholar 

  4. C.R. Gagg and P.R. Lewis, The rise and fall of cast iron in Victorian structures — A case study review, Eng. Fail. Anal., 18(2011), No. 8, p. 1963.

    Article  CAS  Google Scholar 

  5. C. Labrecque and M. Gagné, Ductile iron: Fifty years of continuous development, Can. Metall. Q., 37(1998), No. 5, p. 343.

    CAS  Google Scholar 

  6. J.J. Cui and L.Q. Chen, Microstructure and abrasive wear resistance of an alloyed ductile iron subjected to deep cryogenic and austempering treatments, J. Mater. Sci. Technol., 33(2017), No. 12, p. 1549.

    Article  CAS  Google Scholar 

  7. J.J. Cui and L.Q. Chen, Microstructures and mechanical properties of a wear-resistant alloyed ductile iron austempered at various temperatures, Metall. Mater. Trans. A, 46(2015), No. 8, p. 3627.

    Article  CAS  Google Scholar 

  8. C.H. Hsu and T.L. Chuang, Influence of stepped austempering process on the fracture toughness of austempered ductile iron, Metall. Mater. Trans. A, 32(2001), No. 10, p. 2509.

    Article  Google Scholar 

  9. R.C. Voigt and Y.H. Lee, Properties and application of austempered ductile irons, [in] Y.H. Kabil and M.E. Said, eds., Current Advances in Mechanical Design and Production IV, Pergamon Press, Oxford, 1989, p. 29.

    Chapter  Google Scholar 

  10. A. Trudel and M. Gagné, Effect of composition and heat treatment parameters on the characteristics of austempered ductile irons, Can. Metall. Q., 36(1997), No. 5, p. 289.

    Article  CAS  Google Scholar 

  11. B. Stouģhton and R.D. Billinger, The spheroidizing of cementite, Ind. Eng. Chem., 18(1926), No. 8, p. 785.

    Article  Google Scholar 

  12. D.H. Shin, S.Y. Han, K.T. Park, Y.S. Kim, and Y.N. Paik, Spheroidization of low carbon steel processed by equal channel angular pressing, Mater. Trans., 44(2003), No. 8, p. 1630.

    Article  CAS  Google Scholar 

  13. Z.Q. Lv, B. Wang, Z.H. Wang, S.H. Sun, and W.T. Fu, Effect of cyclic heat treatments on spheroidizing behavior of cementite in high carbon steel, Mater. Sci. Eng. A, 574(2013), p. 143.

    Article  CAS  Google Scholar 

  14. K. Tokaji, T. Horie, and Y. Enomoto, Effects of microstructure and carbide spheroidization on fatigue behaviour in high V-Cr-Ni cast irons, Int. J. Fatigue, 28(2006), No. 3, p. 281.

    Article  CAS  Google Scholar 

  15. L.C. Casteletti, P.E.B. Kinap, and P.A.P. Nascente, Heat treatments for obtaining spheroidal cementite in ductile cast iron, Int. J. Mater. Prod. Technol., 24(2005), No. 1–4, p. 375.

    Article  CAS  Google Scholar 

Download references

Acknowledgement

Authors thank the Department of Metallurgical and Materials Engineering, NITK, India, for providing experimental facilities to complete this work.

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to Basavaraj.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Basavaraj, Sondar, P.R. & Hegde, S.R. Effect of spheroidization of cementite in ductile cast iron. Int J Miner Metall Mater 28, 404–411 (2021). https://doi.org/10.1007/s12613-020-2041-0

Download citation

  • Received:

  • Revised:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s12613-020-2041-0

Keywords

Navigation