Abstract
Growing concerns over the hazardous impact of mineral oil-based industrial quench media on human health and the environment have forced researchers to seek renewable and non-hazardous alternatives. Non-edible vegetable oil-based quench media are perceived to be a potential replacement for mineral-based industrial quench media. The present work focuses on assessing the cooling performance of neem oil as compared to commercial hot oil quench media. Inconel and steel probes were used to characterize the cooling performance of these quench media maintained at bath temperatures 100 °C, 150 °C and 200 °C. The heat extraction rates and uniformity of heat extraction in Inconel probes quenched in neem oil were observed to be substantially higher at all bath temperatures. The hardness of AISI 52100 steel probe quenched in neem oil at all bath temperatures was observed to be higher. The pearlitic microstructure was observed in the steel probe quenched in hot oil maintained at 200 °C bath temperature. In contrast to this, a mixture of bainite, martensite and carbide was observed in case of steel probes quenched in neem oil maintained at 200 °C. Oxidation experiments revealed that neem oil is susceptible to an increase in viscosity due to oxidation. An increase in the viscosity by about 15% was observed in the case of neem oil as compared to only 4% increase in viscosity of hot oil. However, after an initial increase, the viscosity of neem oil stabilized and further no significant change in viscosity due to oxidation were observed. Oxidation had no significant effect on the cooling performance hot neem oil quench medium, and thus, it can be considered as an effective replacement for hot oil.
References
E.C. de Souza, M.R. Fernandes, S.C.M. Augustinho, L.C.F. Canale, and G.E. Totten, Comparison of Structure and Quenching Performance of Vegetable Oils, J. ASTM Int., 2009, 6(9), p 102188. https://doi.org/10.1520/jai102188
G. Ramesh and K.N. Prabhu, Wetting and Cooling Performance of Mineral Oils for Quench Heat Treatment of Steels, ISIJ Int., 2014, 54(6), p 1426–1435. https://doi.org/10.2355/isijinternational.54.1426
D.S. MacKenzie, Advances in quenching, in Proceedings of the 22nd Heat Treating Society Conference and the 2nd International Surface Engineering Congress, 2003 (Stage C), p. 228–239, https://doi.org/https://www.houghtonintl.com/sites/default/files/resources/article_-_advances_in_quenching.pdf.
F. Salawa, R. Napierala, and C. Suarez, “Best Practices for the Application of Quenching Oils,” n.d.
E. Rowland and D.S. MacKenzie, “Proper Care of Quench Oil Leading to Consistent Part Quality,” Thermal Processing in Motion, ASM International, 2018, p 98–105.
G. Graham and D.S. Mackenzie, Understanding the Quenchant Report, 2018.
N.J. Fox and G.W. Stachowiak, Vegetable Oil-Based Lubricants—A Review of Oxidation, Tribol. Int., 2007, 40(7), p 1035–1046
L.C.F. Canale, M.R. Fernandes, S.C.M. Agustinho, G.E. Totten, and A.F. Farah, Oxidation of Vegetable Oils and Its Impact on Quenching Performance, Int. J. Mater. Prod. Technol., 2005, 24(1/2/3/4), p 101. https://doi.org/10.1504/ijmpt.2005.007943
G.E. Totten, H.M. Tensi, and K. Lainer, Performance of Vegetable Oils as a Cooling Medium in Comparison to a Standard Mineral Oil, J. Mater. Eng. Perform., 1999, 8(4), p 409–416
K.M. Pranesh Rao and K.N. Prabhu, Assessment of Wetting Kinematics and Cooling Performance of Select Vegetable Oils and Mineral-Vegetable Oil Blend Quench Media, Mater. Sci. Forum, 2015, 830–831, p 160–163. https://doi.org/10.4028/www.scientific.net/MSF.830-831.160
S.W. Dean, K.N. Prabhu, and P. Fernandes, Heat Transfer During Quenching and Assessment of Quench Severity—A Review, J. ASTM Int., 2009, 6(1), p 101784. https://doi.org/10.1520/jai101784
U.V. Nayak and K.N. Prabhu, Effect of Section Thickness on Heat Transfer during Quenching in Vegetable Oils, Mater. Perform. Charact., 2018, 7(1), p 20180084. https://doi.org/10.1520/mpc20180084
S.B. Hassan, J.B. Agboola, V.S. Aigbodion, and E.J. Williams, Hardening Characteristics of Plain Carbon Steel and Ductile Cast Iron Using Neem Oil as Quenchant, J. Miner. Mater. Charact. Eng., 2011, 10(2), p 161–172
H.K. Kim and S.I. Oh, Evaluation of Heat Transfer Coefficient during Heat Treatment by Inverse Analysis, J. Mater. Process. Technol., 2001, 112(2), p 157–165. https://doi.org/10.1016/S0924-0136(00)00877-3
Z. Nie, G. Wang, Y. Lin, and Y.K. Rong, Precision Measurement and Modeling of Quenching- Tempering Distortion in Low-Alloy Steel Components with Internal Threads, J. Mater. Eng. Perform., 2015, 24(12), p 4878–4889
K.M. Pranesh Rao and K.N. Prabhu, Effect of Bath Temperature on Cooling Performance of Molten Eutectic NaNO3-KNO3 Quench Medium for Martempering of Steels, Metall. Mater. Trans. A, 2017, 48(10), p 4895–4904. https://doi.org/10.1007/s11661-017-4267-7
G. Ramesh and K.N. Prabhu, Assessment of Axial and Radial Heat Transfer during Immersion Quenching of Inconel 600 Probe, Exp. Therm. Fluid Sci., 2014, 54, p 158–170. https://doi.org/10.1016/j.expthermflusci.2014.01.016
S.R. Elmi Hosseini, A. Zabett, and Z. Li, Cooling Curve Analysis of Heat Treating Oils and Correlation with Hardness and Microstructure of a Low Carbon Steel, Mater. Perform. Charact., 2015, 3(4), p 20130067. https://doi.org/10.1520/mpc20130067
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Pranesh Rao, K.M., Prabhu, K.N. Assessment of Cooling Performance of Neem Oil for Distortion Control in Heat Treatment of Steel. J. of Materi Eng and Perform 29, 6033–6043 (2020). https://doi.org/10.1007/s11665-020-05082-4
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11665-020-05082-4