Impact of hydrogen on rupture behaviour of Zircaloy-4 nuclear fuel cladding during loss-of-coolant accident: a novel observation of failure at multiple locations☆
To establish the exclusive role of hydrogen on burst behaviour of Zircaloy-4 during loss-of-coolant accident transients, an extensive single-rod burst tests were conducted on both unirradiated as-received and hydrogenated Zircaloy-4 cladding tubes at different heating rates and internal overpressures. The visual observations of cladding tubes during bursting as well as post-burst are presented in detail to understand the effect of hydrogen concentration, heating rate, and internal pressure. Impact of hydrogen on burst parameters—burst stress, burst strain, burst temperature—during loss-of-coolant accident transients are compared and discussed. Rupture at multiple locations for hydrogenated cladding at lower internal pressure and higher heating rate is reported for the very first time. A novel burst criterion accounting hydrogen concentration in nuclear fuel cladding is proposed.