1 Introduction

Lignite is an abundant fossil fuel resource and will continue to be an important energy source in the foreseeable future. Because of its high moisture content (25 wt%–60 wt%), the drying/dewatering is an integral step for lignite applications that require high efficiency. Hydrothermal treatment (Butler et al. 2007; Sakaguchi et al. 2008; Katalambula and Gupta 2009; Ullah et al. 2018), a non-evaporative technique, is considered an effective method for dewatering and upgrading lignite. The process enables an improvement in the slurry properties of coal (Yu et al. 2012; Fu and Wang 2014; Zhang et al. 2018) and can reduce the viscosity of the coal-water slurry. Moreover, hydrothermal treatment not only promotes the hydro-liquefaction activity during coal liquefaction (Li et al. 2020) but also increases the coal concentration of the coal-solvent slurry (Inoue et al. 2012a, b), which is because of the lower porosity for the treated coal. Furthermore, hydrothermally treated lignite has a greater calorific value (Yu et al. 2014; Ullah et al. 2018) compared with raw lignite. Furthermore, contaminant elements in lignite, such as sulfur, nitrogen, and chlorine (Wang et al. 2016a, b; Zhao et al. 2020), can be fixed during hydrotreatment.

The improvement of low-grade coal via hydrothermal treatment could benefit from a better understanding of the evolution of the structural properties of lignite during hydrothermal treatment. This would aid in predicting the behavior of coal subsequently during the pyrolysis, liquefaction, and gasification processes (Sun et al. 2004; Safarova et al. 2005 Wang et al. 2013a, b). Intensive research on the structure of coal has been undertaken using X-ray diffraction (XRD) (Sonibare et al. 2010; Wu et al. 2013; Yan et al. 2020), Fourier transform infrared spectroscopy (FTIR) (Ibarra et al. 1996; Wang et al. 2013a, b; Wu et al. 2013, 2014; Jiang et al. 2019), and Raman spectroscopy (Jiang et al. 2019; Liu et al. 2014). XRD spectroscopy is commonly used to study the crystal structure of carbonaceous materials. However, exploring the non-crystalline part of coal is difficult. Raman spectroscopy is a major technique used to evaluate the degree of ordering and crystallinity in carbonaceous materials. FTIR is very useful in probing the functional groups in coal and thus widely used for studying the chemical structure of coal. Combined with curve-fitting analysis (Ibarra et al. 1996; Wang et al. 2011, 2013a; Wu et al. 2013; Jiang et al. 2019), these methods can provide additional insight into the structure of coal and their structural parameters can be quantitatively analyzed. To better understand the carbon skeleton structure of coal, solid 13C nuclear magnetic resonance (13C-NMR) spectroscopy (Wei et al. 2005; Erdenetsogt et al. 2010; Xiang et al. 2013; Yan et al. 2014) has been used to determine the chemical structure, which could be used to quantitatively characterize different existing types of carbon in coal.

The raw and hydrothermally-treated Inner Mongolia lignite (IM) structures were compared via their 13C-NMR spectra (Zhang et al. 2016). Hydrothermal treatment can break the cross-linked structure in lignite (Liu et al. 2016, 2017; Ge et al. 2018) to change the conversion pathway during pyrolysis. The water in the reaction can participate in one or more roles with the presence of oxygen functional groups (Siskina and Katritzky 2000; Feng et al. 2008) at the treatment temperature. The hydrogen from water was determined to be transferred to IM via analysis of pyrolysis tar using the isotopic tracer method (Wang et al. 2016a). As discussed above, previous studies focused on the correlation of the hydrothermal treatment of lignite with the pyrolysis product, while the structural evolution of lignite during hydrothermal treatment has largely been ignored. To the best of our knowledge, an in-depth investigation of the structural evolution of lignite during hydrothermal treatment has yet to be carried out.

In this work, the structural evolution of IM during hydrothermal treatment was studied. The curve-fitting method was used to quantify the accurate chemical shift values of different structural carbons via 13C-NMR spectroscopy and the wavenumbers of the oxygen functional groups in lignite were determined using FTIR spectroscopy. Finally, changes in the lignite structure during hydrothermal treatment were determined.

2 Experimental

2.1 Materials

Inner Mongolia lignite (IM) from the Inner Mongolia province, China was ground to < 0.2 mm and stored under a cryogenic environment. The proximate and ultimate analyses of the lignite are shown in Table 1. The raw lignite was dried under vacuum at 323 K for 8 h before characterization.

Table 1 Proximate and ultimate analyses of lignites
Full size table

2.2 Methods

2.2.1 Hydrothermal treatment

Hydrothermal treatment of lignite was carried out in a 500 mL autoclave. The water content of raw lignite is about 25%–60%; for the experiments a value of about 40% was used and the original lignite state was simulated in the laboratory. For this, 80 g lignite and 48 mL deionized water were placed in the reactor and heated at a rate of 4 K/min to a certain temperature (473, 493, 513, 533, 573 K); then, stirred using a stirrer and maintained for 30 min under saturated vapor pressure. The treated lignite was then cooled to room temperature and removed from the reactor. The products were filtered to remove excess water, and then dried under vacuum at 323 K for 8 h. The lignite hydrothermally treated at different temperatures is referred to as IM-473, IM-493, IM-513, IM-533, and IM-573.

The gas composition was analyzed via gas chromatography (GC) with a GC 126 instrument (INESA instrument, China), equipped with two detectors, i.e., a thermal conductivity detector (TCD) and a flame ionization detector (FID). The gas sampling bags were put under vacuum and purged several times before the experiments.

2.2.2 Analysis of the raw and treated lignite

  1. (1)

    Proximate and ultimate analyses


The proximate analyses of the lignites were carried out using standard methods (ISO1171and ISO562). The elements C, H, N, and S were analyzed using an elemental analyzer (Elementar Vario Micro Cube, Germany), and the percentage of oxygen was calculated using the difference.

  1. (2)

    13C-NMR


The carbon structure was determined via solid 13C-NMR using a Bruker Avance 500 NMR spectrometer (Germany) at a frequency of 125.77 MHz for carbon and a frequency of 500.12 MHz for the proton. Dry and powdered coals were packed into a 4 mm rotor. The solid 13C NMR spectra were obtained at a spinning speed of 5.7 kHz using a solid cross polarization/magic angle spinning (CP/MAS) probe and the total suppression of sidebands sequence (TOSS). The measurement conditions were as follows: the contact time was 1 ms, with a recycle delay of 3 s and a scan number > 2000. The corresponding chemical shifts for different carbon types have been investigated in numerous studies (Xiang et al. 2013; Yan et al. 2014; Erdenetsogt et al. 2010). Using data from other studies along with the 13C-NMR spectra of the raw and treated IM, the chemical shifts for different types of carbon were determined in our previously reported study (Liu et al. 2016). The characteristics of the carbons located in lignite are shown in Fig. 1.

Fig. 1
figure 1

Character of the carbon located in lignite

Full size image
  1. (3)

    FTIR analyses


The oxygen functional groups were analyzed via FTIR spectroscopy. Quantitative FTIR transmission spectra of the lignites were obtained with a Nicolet 6700 Fourier Transform infrared spectrometer (USA) using finely ground samples pressed in KBr pellets. A mixture of lignite and KBr (ratio of 1:100) was ground together and pressed into a pellet and then dried in a vacuum oven at 323 K for 24 h. The spectra were recorded with various indexes between 4000 and 400 cm−1 by co-adding 32 scans at a resolution of 4 cm−1. The bands of the corresponding oxygen functional groups (region of 1000–1800 cm−1) for the FTIR spectra of the raw and treated IM were determined based on our previously reported study (Liu et al. 2016).

  1. (4)

    Curve-fitting method


A range of functional groups in lignite clusters were marked by peak clusters in the spectra, rather than distinct sharp peaks with specific positions. To interpret the data, the peak separation and quantitative calculations were performed using a curve-fitting program in the Origin 8.0 software. The positions and number of bands were initially established from the second derivative of the spectrum, and a coefficient of determination (R2) of 0.998 for the desired fit of the experimental spectrum was obtained. The number of peaks in a given region was determined, and the frequency and intensity of each peak were estimated. Subsequently, each simulated peak was integrated to obtain the peak area, and the corresponding fraction relative to the total carbon integration of the spectrum was calculated to obtain the relative content of each unit.

3 Results and discussion

3.1 Effect of hydrothermal treatment on preliminary evaluation of lignite composition

The proximate and ultimate analyses of raw and treated IM are shown in Table 1.

The data in Table 1 indicates that the fixed carbon content of treated IM increased and the oxygen contents decreased with increasing temperature, especially above a temperature of 493 K. The carbon contents of IM-533 and IM-573 were close to those of bituminous coal (Zhang 2014). The changes in the elemental composition led to an increase in the calorific value of treated IM. This indicated that the treated IM could be a better solid fuel than raw IM. The variation of H/C and O/C during hydrothermal treatment is shown in Fig. 2.

Fig. 2
figure 2

Variation of H/C and O/C during hydrothermal treatment

Full size image

The O/C ratio decreased from 0.203 in raw IM to 0.185 for IM-493 and to 0.132 for IM-573. The change in the O/C ratio indicates that oxygen functional groups decreased during hydrothermal treatment with increasing treatment temperature. The IM improved during hydrothermal treatment, especially with treatment above a temperature of 493 K. The ratio of H/C increased with increasing temperature below 513 K. The data showed that hydrothermal treatment promotes the removal of oxygen functional groups, and hydrogen is exchanged and transferred between water and lignite. The hydrogen bonds in lignite were rearranged during hydrothermal treatment. When the treatment temperature subsequently increased, the H/C ratio decreased.

3.2 Evolution of different types of carbon in IM during hydrothermal treatment

To investigate the change of the IM structure during hydrothermal treatment in detail, the structure of the carbon skeleton of the raw and treated IM was analyzed via solid 13C-NMR spectroscopy, and the spectra are shown in Fig. 3.

Fig. 3
figure 3

13C NMR spectra of raw and treated IM

Full size image

Two peak clusters containing various functional groups of structural carbons, rather than unique sharp peaks with specific chemical shifts were observed. They were visible in the spectrum as: aliphatic units (0–90 ppm), aromatic units (100–165 ppm), and carbonyl units were observed at a chemical shift of 170–220 ppm. The spectra were fitted to quantify the relative proportions of different carbon types in the raw and treated IM, as shown in Fig. 4.

Fig. 4
figure 4

Fitted 13C NMR spectra of the raw and treated IM (Black line is measured spectrum, red line is fitting spectrum, green line is simulated peak)

Full size image

The relative contents of each carbon unit to the total carbon content are calculated by their individual areas from the fitted 13C NMR spectra and listed in Table 2.

Table 2 Carbon structure distributions of the raw and treated IM on the basis of the raw lignite
Full size table

The data in Table 2 indicate the difference between the structural characteristics of raw and treated IM can be given as: an increase of aliphatic carbons, a decrease of ether and changes of carboxyl, quinone, and carbonyl carbons after treatment.

3.2.1 Oxygen-linked carbon species (fOal , fOa , and fCCa )

The functional groups of oxygen were abundant in the raw IM (oxygen-linked carbon is 27.40%), as characterized by oxygen aliphatic carbon (fOal ), oxygen aromatic carbon (fOa ), and carboxyl, quinone, and carbonyl carbon (fCCa ). There was a decrease in fOal with increasing treatment temperature. The fOa decreased from 12.89% of raw IM to 4.26% in IM-493, and then increased to 8.16% for IM-533. The change of fCCa had the same trend as for fOa . The results indicate that hydrothermal treatment promotes the cleavage of ether, and steam could also depolymerize the lignite macromolecular network via cleavage of weak covalent bonds, such as ether linkages that are thermally stable but hydrothermally unstable at elevated temperatures (Zeng et al. 2006). Water with the presence of oxygen functional groups in lignite can participate in one or more roles: as a catalyst, reactant, and solvent in aquathermolysis chemistry at a high temperature (~ 523 K) (Siskina and Katritzky 2000). Therefore, the O/C ratio and fOal and fOa decreased and fCCa changed. Hydrothermal treatment can be divided into three stages. (1) At a temperature < 493 K, thermal decomposition of carboxyl acid, breaking of the alkyl ether, and the slight cleavage of the aryl ether are thought to be the main reactions (Li et al. 2013). In this stage, fOal , fOa , and fCCa decrease, and then the hydrogen bond is weakened. (2) The stage between 493 and 533 K, here, the hydrogen bond between lignite and water is broken (Li et al. 2011), and the interaction of lignite and water tends to occur. The free H+ and OH− are possibly cross-linked to the benzene or phenoxy groups to generate phenolic groups via electrophilic substitution, and fOa increases. Because of the mineral matter present in lignite, lignite was enclosed in an acidic environment after the addition of water (Shui et al. 2006). The weak covalent bonds were catalyzed for cleavage, hence, fOal continued to decrease. Furthermore, water was adsorbed around the oxygen functional groups (Xiang et al. 2014) to produce a new hydrogen bond, and the raw IM hydrogen bond between the hydroxyl was broken to obtain a free hydroxyl (Miura et al. 1991), which resulted in a rearrangement of the hydrogen bond. The free hydroxyl condensed to obtain quinone, so fCCa increased and the H/C ratio decreased. (3) At temperatures > 533 K, a cleavage of the covalent bond may occur (Shi et al. 2013), the ether bond is broken further, and the carboxyl, quinone, and carbonyl groups begin to break under the steam pressure. When the temperature was increased to 573 K, fOal decreased from 0.69% in IM-533 to 0.13% in IM-573, fOa decreased from 8.16% in IM-533 to 5.88% in IM-573 m, and fCCa decreased from 9.91% in IM-533 to 5.74% in IM-573.

3.2.2 Aromatic carbon species (fHa , fBa , fSa , and fOa )

The aromatic carbon species comprises ~ 50% at the treated temperature below 533 K. While the main lignite structure displays minimal change with hydrothermal treatment below 533 K, the protonated aromatic carbon and side chains markedly changed. The ratios of the protonated aromatic carbon, bridging ring junction aromatic carbon, and aliphatic substituted aromatic carbon to the total aromatic carbon are shown in Fig. 5.

Fig. 5
figure 5

Variation of the ratio of protonated aromatic carbon, bridging ring junction aromatic carbon, and aliphatic substituted aromatic carbon to the aromatic carbon

Full size image

From Fig. 5, it can be seen that the decomposition of the carboxyl is a primary reaction during the first stage of hydrothermal treatment. The fHa increased, while fBa and fSa had only a small change. The H/C increased in the first stage according to Fig. 1, which is consistent with the analysis for oxygen-linked carbon. In the second and third stages, the free radical in lignite increased because of the hydrolysis of the oxygen functional groups. A cross-linking reaction occurred between the free radicals under aqueous conditions. The aliphatic hydrocarbon radical may be linked with the aryl radical at elevated temperature and the ratio of fSa to aromatic carbon increased from 0.176 in IM-493 to 0.214 in IM-573, and the ratio of fHa to aromatic carbon decreased from 0.196 in IM-493 to 0.109 in IM-573.

3.2.3 Aliphatic carbon species (f3al , faal , f2al , f1al , and f*al )

From the data in Table 2, it can be seen that the total aliphatic carbon changes a little (~ 35%). However, the ratio of CH2/CH3 (f2al /(f3al  + faal )) increased from 0.727 in IM to 1.241 in IM-533 (Fig. 6) in the second stage, and it decreased from 1.241 in IM-533 to 0.256 in IM-573 in the third stage.

Fig. 6
figure 6

Variation of the CH2/CH3 ratio

Full size image

The CH2/CH3 ratio can be considered to be an estimate of the length of the aliphatic chains of lignite and a branching index (Ibarra et al. 1996). In the first stage, the increase of methylene is due to the decomposition of oxygen functional groups, hence, H/C increases; however, the increasing trend is not obvious. The CH2/CH3 ratio clearly increases in the second stage because hydrolysis of the oxygen functional groups (such as carboxyl, esters, and ethers) plays an important role in this stage. The hydrogen of the functional groups in lignite can exchange with water via electrophilic substitution on addition of water at this temperature (Ishihara et al. 1993, 2002), and then transfer in lignite or the methyl hydroaromatic structures opposite to the branched aliphatic structures. The H radicals produced by the condensation of free phenol also participate in the hydrogen transfer. However, a portion of the covalent bonds of C–C begin to break in the third stage and the length of the aliphatic carbon decreases. The length of the aliphatic chain is smaller when the treatment temperature rises to 573 K. The composition of the gas produced during hydrothermal treatment was analyzed via GC and the results are presented in Table 3.

Table 3 Composition of the gas produced during the hydrothermal treatment
Full size table

The decomposition and hydrolysis of the oxygen functional group is the primary reaction occurring below 533 K during the hydrothermal treatment. The largest gas components are CO2 and CO. Hydrogen transfer reaction occurs in the second stage, here, the production of H2 during hydrothermal treatment increases from 0.18% at 493 K to 0.83% at 533 K. The cleavage of covalent bonds leads to an increase in the CO and CH4 components of the gas in the third stage, which indicates that the length of the aliphatic carbon decreased. These results are consistent with the previously discussed analyses.

3.3 FTIR analysis of the evolution of oxygen functional groups during hydrothermal treatment

To verify the objectives discussed above, the functional groups of IM-Raw and IM-533 were monitored via FTIR. The 3000–3500 cm−1 region of the IM-Raw and IM-533 spectra were compared using the absorption of the C=C bond stretching of the aromatic ring at 1588 cm−1 as a standard peak, and the obtained spectra are shown in Fig. 7.

Fig. 7
figure 7

Comparison of IM-Raw and IM-533 spectra in the region 3000–3500 cm−1

Full size image

A decrease in the intensity of the band near 3300 cm−1 can be seen in the spectrum in Fig. 7. This indicates that the hydrogen bond decreased during the hydrothermal treatment of lignite because of hydrolysis of the oxygen functional group. While water absorbed in KBr may obscure this band, the results agree with Ishihara et al. (2002) and Yan et al. (2020) and the discussion above.

The oxygen functional groups (region of 1000–1750 cm−1) were analyzed via curve-fitting and the results are shown in Fig. 8.

Fig. 8
figure 8

Fitted FTIR spectra of the oxygen functional group in IM-Raw and IM-533 (Black line is measured spectrum, red line is fitting spectrum, green line is simulated peak)

Full size image

The content of each oxygen functional group unit relative to the total simulated peak area in the region of 1000–1750 cm−1 was determined from the fitted spectra; the results for IM-533 were calculated based on the raw lignite listed in Table 4.

Table 4 Relative contents of each oxygen functional group
Full size table

The main oxygen functional groups in IM are aryl ether, phenol, and carbonyl or quinone conjugated with aromatic rings. Hydrothermal treatment promotes the cleavage of weak bonds such as the ether and carboxyl, resulting in a decrease in the amount of ether and carboxyl groups. With the addition of water, the free H and OH possibly cross-link with the benzene or phenoxy groups to generate phenol via electrophilic substitution in the second stage. Hence, the area percentage in 1269 cm−1, assigned to phenolic groups, clearly increases from 9.60% in IM to 18.51% in IM-533. With decreasing hydrogen bonds and increasing free phenol, quinone is produced and takes part in hydrogen transfer between water and lignite. Therefore, the conjugated C=O increases according to the stretching band at 1656 cm−1. The results of the FTIR characterization were in good agreement with the NMR analysis.

From these results, it can be concluded that the hydrothermal treatment proceeds in three stages: the first stage is the reaction involving the decomposition of the carboxyl, non-covalent bond and weak covalent bond; the second stage is hydrolysis of the oxygen functional groups and hydrogen transfer between water and lignite; and the third stage is the breakage of covalent bonds. The evolution of the lignite structure is described in Fig. 9.

Fig. 9
figure 9

Schematic of the structural evolution of IM lignite during hydrothermal treatment

Full size image

4 Conclusions

In this work, the evolution of the IM lignite structure during hydrothermal treatment was investigated via solid 13C NMR and FTIR spectroscopies. The carbon content increased from 72.99 wt% in IM to 78.16 wt% in IM-573. The atomic ratio of O/C decreased from 0.203 in IM to 0.132 in IM-573. The hydrothermal treatment resulted in improvement of the IM. The structural evolution of IM during hydrothermal treatment can be divided into three stages depending on the treatment temperature:

  1. (1)

    In the first stage (< 493 K), oxygen functional groups decompose and are substituted by hydrogen with increasing temperature. The atomic ratio of H/C increased from 0.764 in IM to 0.920 in IM-493, and oxygen-linked carbon decreased from 27.40% in IM to 9.10% in IM-493. The main components of the escaping gas were CO2 with a small amount of CO;

  2. (2)

    In the second stage (493–533 K), the hydrolysis of functional groups promoted cleavage of weak bonds. H+ and OH− were linked by lignite via an ionic pathway under hydrothermal conditions. The oxygen-linked aromatic carbon increased from 4.26% in IM-493 to 8.16% in IM-533, and the phenolic groups increased, as indicated by the FTIR spectra. Hydrogen transfer took place between the water and lignite or within the intra-molecular structure. The hydroaromatic methyl structure converted to a branched aliphatic structure, resulting in an increase of the CH2/CH3 ratio from 0.871 in IM-493 to 1.241 in IM-533. The free phenolic group was condensed to generate quinonyl and the carbonyl carbon increased from 3.31% in IM-493 to 9.91% in IM-533; the H/C ratio had a small decrease. H2 and CH4 were eliminated in this stage.

  3. (3)

    In the third stage (> 533 K), a portion of the covalent bonds begin to break. The CH2/CH3 ratio decreased and the hydroaromatic methyl structure content increased. The conjugated C=O in lignite also decomposed to produce CO and the carbonyl carbon decreased from 9.91% in IM-533 to 5.74% in IM-573. The content of CO and CH4 in the escaping gas also increased. The bridge ring junction carbon content increased from 24.24% in IM-533 to 29.71% in IM-573. At this stage, the changes in the lignite structure were clear.