A novel post-processing method for 316L steel specimen generated by SLM using TiN/TiAlN multilayer coating

Selective laser melting (SLM) is an important advanced additive manufacturing technology. The existing SLM printing technology cannot manufacture the mechanical parts that fully meet the requirements of high precision and strength. This paper aims to explore a new post-processing method for SLM 316L specimen, namely, using of the TiN/TiAlN multilayer coating fabricated by multi-arc ion plating on the surface of SLM specimens, for improving the performance of SLM specimens. The other purpose of this paper is compared the performances of the TiAlN/TiN multilayer coating machined specimen and the TiN/TiAlN multilayer coating SLM specimen.

The TiN/TiAlN multilayer coating is fabricated by multi-arc ion plating on the surface of 316L specimens. The surface morphology and selected mechanical properties of TiN/TiAlN multilayer coating plating on the SLM substrate specimen and the machined substrate specimen were studied in this paper. The analyzed properties included surface topography, micro hardness, the adhesion, the thickness and the wear resistance of TiN/TiAlN multilayer coating plating on the SLM substrate specimen and the machined substrate specimen.

The electron microscope images reveal that surface morphology of TiN/TiAlN multilayer coating plating on the SLM specimens is relatively flat, and there are some micro-particles in different sizes and pin holes dispersed on them. After TiN/TiAlN multilayer coating, the performances of SLM samples, such as micro hardness, the thickness and the wear resistance, were significantly improved. The micro hardness of TiN/TiAlN multilayer coating machined specimen is higher than that of TiN/TiAlN multilayer coating SLM specimen. However, the adhesion of TiN/TiAlN multilayer coating machined specimen is less than that of TiN/TiAlN multilayer coating SLM specimen.

The study provides a new post-processing method for SLM 316L specimen to improve the performance of SLM specimens and to enable SLM specimens to be applied in the field of precision mechanical transmission.