Microstructure and mechanical properties of maraging 18Ni-300 steel obtained by powder bed based selective laser melting process

The purpose of this paper is to maraging 18Ni-300 steel fabricate by powder bed based selective laser melting (SLM) process. Microstructure and mechanical properties of the maraging steel part before and after heat treatment at a slow cooling rate were investigated.

The microstructure of the printed part was observed by optical microscopy and scanning electron microscopy. The phases were determined by X-ray diffraction. The surface roughness of the part was recorded by a profilometer. The tensile properties and microhardness of the parts before and after heat treatment were characterized by an electronic universal tensile testing machine and a Vickers hardness tester, respectively.

Maraging 18Ni-300 steel part comprised of the martensitic phase and a small fraction of austenite phase. After heat treatment, the volume fraction of austenite slightly increased. The surface roughness of the part was about 96 µm. The printed part was dense, but irregular pores were present. The yield strength, ultimate tensile strength (UTS), elongation and Young’s modulus of as-fabricated parts were 554.7 MPa, 1173.1 MPa, 10.9% and 128.9 GPa, respectively. The yield strength, UTS, elongation and Young’s modulus of as-treated parts were 2065 MPa, 2225 MPa, 4.2% and 142.5 GPa, respectively. The microhardness values of surface and cross-section of the as-fabricated part were 407.1 HV and 443.0 HV, respectively. After short-time heat treatment, the microhardness values of the surface and cross-section of the part were 542.7 HV and 567.3 HV, respectively. After long-time heat treatment, the microhardness values of the surface and cross-section of the part were 524.4 HV and 454.8 HV, respectively. The microhardness and tensile strength increased significantly with decreasing elongation due to the changes in phases and microstructure of the parts after heat treatment.

This work studied the effect of heat treatment at 550°C combined with a subsequent slow cooling rate on microstructure and mechanical properties of maraging 18Ni-300 steel obtained by the powder bed based SLM process.