Liquation cracking in the heat-affected zone of IN939 superalloy tungsten inert gas weldments

International Journal of Minerals, Metallurgy and Materials Aims and scope Submit manuscript

Abstract

The main aim of this study was to investigate liquation cracking in the heat-affected zone (HAZ) of the IN939 superalloy upon tungsten inert gas welding. A solid solution and age-hardenable filler metals were further studied. On the pre-weld heat-treated samples, upon solving the secondary γ′ particles in the matrix, primary γ′ particles in the base metal grew to “ogdoadically diced cubes” of about 2 µm in side lengths. The pre-weld heat treatment reduced the hardness of the base metal to about HV 310. Microstructural studies using optical and field-emission scanning electron microscopy revealed that the IN939 alloy was susceptible to liquation cracking in the HAZ. The constitutional melting of the secondary, eutectic, and Zr-rich phases promoted the liquation cracking in the HAZ. The microstructure of the weld fusion zones showed the presence of fine spheroidal γ′ particles with sizes of about 0.2 µm after the post-weld heat treatment, which increased the hardness of the weld pools to about HV 350 and 380 for the Hastelloy X and IN718 filler metals, respectively. Application of a suitable solid solution filler metal could partially reduce the liquation cracking in the HAZ of IN939 alloy.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. T.Á. Tejedor, R. Singh, and P. Pilidis, Advanced gas turbine asset and performance management, [in] P. Jansohn, ed., Modern Gas Turbine Systems: High Efficiency, Low Emission, Fuel Flexible Power Generation, Woodhead Publishing Series in Energy, Woodhead Publishing India Private Limited, New Delhi, 2013, p. 515.

    Chapter  Google Scholar 

  2. O.A. Ojo, N.L. Richards, and M.C. Chaturvedi, Microstructural study of weld fusion zone of TIG welded IN 738LC nickel-based superalloy, Scripta Mater., 51(2004), No. 7, p. 683.

    Article  CAS  Google Scholar 

  3. R.K. Sidhu, O.A. Ojo, N.L. Richards, and M.C. Chaturvedi, Metallographic and OIM study of weld cracking in GTA weld build-up of polycrystalline, directionally solidified and single crystal Ni based superalloys, Sci. Technol. Weld. Joining, 14(2009), No. 2, p. 125.

    Article  CAS  Google Scholar 

  4. R.K. Sidhu, O.A. Ojo, and M.C. Chaturvedi, Microstructural response of directionally solidified René 80 superalloy to gastungsten arc welding, Metall. Mater. Trans. A, 40(2009), No. 1, p. 150.

    Article  Google Scholar 

  5. K.C. Chen, T.C. Chen, R.K. Shiue, and L.W. Tsay, Liquation cracking in the heat-affected zone of IN738 superalloy weld, Metals, 8(2018), No. 6, p. 387.

    Article  Google Scholar 

  6. T.B. Gibbons and R. Stickler, IN939: Metallurgy, properties and performance, [in] R. Brunetaud, D. Coutsouradis, T.B. Gibbons, Y. Lindblom, D.B. Meadowcroft, and R. Stickler, eds., High Temperature Alloys for Gas Turbines 1982, D. Reidel Publishing Co., Dordrecht, 1982, p. 369.

    Chapter  Google Scholar 

  7. C.P. Cutler and S.W.K. Shaw, The interrelationship of γ′ size, grain size and mechanical properties in IN-939, a cast nickelbase superalloy, [in] Strength of Metals and Alloys, Proceedings of the 5th International Conference, Aachen, 1979, p. 1357.

  8. J.N. DuPont, J.C. Lippold, and S.D. Kiser, Welding Metallurgy and Weldability of Nickel-Base Alloys, John Wiley & Sons, New Jersey, 2009.

    Book  Google Scholar 

  9. O.A. Ojo, N.L. Richards, and M.C. Chaturvedi, Study of the fusion zone and heat-affected zone microstructures in tungsten inert gas-welded INCONEL 738LC superalloy, Metall. Mater. Trans. A, 37(2006), No. 2, p. 421.

    Article  Google Scholar 

  10. Q.G. Li, X. Lin, X.H. Wang, H.O. Yang, M.H. Song, and W.D. Huang, Research on the grain boundary liquation mechanism in heat affected zones of laser forming repaired K465 nickel-based superalloy, Metals, 6(2016), No. 3, p. 64.

    Article  CAS  Google Scholar 

  11. O.A. Ojo, Y.L. Wang, and M.C. Chaturvedi, Heat affected zone liquation cracking in electron beam welded third generation nickel base superalloys, Mater. Sci. Eng. A, 476(2008), No. 1–2, p. 217.

    Article  Google Scholar 

  12. M. Montazeri and F.M. Ghaini, The liquation cracking behavior of IN738LC superalloy during low power Nd: YAG pulsed laser welding, Mater. Charact., 67(2012), p. 65.

    Article  CAS  Google Scholar 

  13. M. Montazeri, F.M. Ghaini, and O.A. Ojo, Heat input and the liquation cracking of laser welded IN738LC superalloy, Weld. J., 92(2013), p. 258.

    Google Scholar 

  14. O.A. Ojo, Intergranular liquation cracking in heat affected zone of a welded nickel based superalloy in as cast condition, Mater. Sci. Technol., 23(2007), No. 10, p. 1149.

    Article  CAS  Google Scholar 

  15. O.A. Ojo and M.C. Chaturvedi, Liquation microfissuring in the weld heat-affected zone of an overaged precipitation-hardened nickel-base superalloy, Metall. Mater. Trans. A, 38(2007), p. 356.

    Article  Google Scholar 

  16. M.A. González Albarrán, D.I. Martínez, E. Díaz, J.C. Diaz, I. Guzman, E. Saucedo, and A.M. Guzman, Effect of preweld heat treatment on the microstructure of heat-affected zone (HAZ) and weldability of Inconel 939 superalloy, J. Mater. Eng. Perform., 23(2014), No. 4, p. 1125.

    Article  Google Scholar 

  17. M.A. González, D.I. Martínez, A. Pérez, H. Guajardo, and A. Garza, Microstructural response to heat affected zone cracking of prewelding heat-treated Inconel 939 superalloy, Mater. Charact., 62(2011), No. 12, p. 1116.

    Article  Google Scholar 

  18. A. Thakur, Microstructural Responses of a Nickel-Base Cast IN-738 Superalloy to a Variety of Pre-Weld Heat-Treatments [Dissertation], University of Manitoba, Winnipeg, 1997.

    Google Scholar 

  19. A. Thakur, N.L. Richards, and M.C. Chaturvedi, On crack-free welding of cast Inconel 738, Int. J. Joining Mater., 15(2003), No. 4, p. 21.

    Google Scholar 

  20. S. Kou, Welding Metallurgy, 2nd ed., John Wiley & Sons, New Jersey, 2003.

    Google Scholar 

  21. R.A. Ricks, A.J. Porter, and R.C. Ecob, The growth of β′ precipitates in nickel-base superalloys, Acta Metall., 31(1983), No. 1, p. 43.

    Article  CAS  Google Scholar 

  22. M. Doi, T. Miyazaki, and T. Wakatsuki, The effect of elastic interaction energy on the morphology of γ′ precipitates in nickel-based alloys, Mater. Sci. Eng., 67(1984), No. 2, p. 247.

    Article  CAS  Google Scholar 

  23. O.T. Ola, O.A. Ojo, and M.C. Chaturvedi, On the development of a new pre-weld thermal treatment procedure for preventing heat-affected zone (HAZ) liquation cracking in nickel-base IN 738 superalloy, Philos. Mag., 94(2014), No. 29, p. 3295.

    Article  CAS  Google Scholar 

  24. H.X. Li and T.K. Chaki, Grain boundary melting and hot cracking in weld HAZ of a two-phase Ni3Al alloy containing Zr, [in] Materials Research Society Symposium-Proceedings, Vol. 364, Boston, 1995, p375.

    Article  Google Scholar 

  25. S.A. David, J.M. Vitek, S.S. Babu, L.A. Boatner, and R.W. Reed, Welding of nickel base superalloy single crystals, Sci. Technol. Weld. Joining, 2(1997), No. 2, p. 79.

    Article  CAS  Google Scholar 

  26. P. Petrzak, K. Kowalski, and M. Blicharski, Analysis of phase transformations in Inconel 625 alloy during annealing, Acta Phys. Pol. A, 130(2016), No. 4, p. 1041.

    Article  CAS  Google Scholar 

  27. S.S. Babu, S.A. David, J.M. Vitek, and M.K. Miller, Atomprobe field-ion microscopy investigation of CMSX-4 Ni-base superalloy laser beam welds, J. Phys. IV, 6(1996), p. C5–253.

    Google Scholar 

  28. R. Nakkalil, N.L. Richards, and M.C. Chaturvedi, Fusion zone microstructure of electron beam welded incoloy 903, Scripta Metall. Mater., 26(1992), No. 4, p. 545.

    Article  CAS  Google Scholar 

  29. M.V. Nathal, R.A. Mackay, and R.G. Garlick, Temperature dependence of γ-γ′ lattice mismatch in nickel-base superalloys, Mater. Sci. Eng., 75(1985), No. 1–2, p. 195.

    Article  CAS  Google Scholar 

  30. B. Geddes, H. Leon, and X. Huang, Superalloys: Alloying and Performance, ASM International, OH, 2010.

    Google Scholar 

Download references

Acknowledgement

The authors would like to acknowledge the assistance from the Niroo Research Institute, Iran for providing the required research facilities.

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to Mohammad Tajally.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Kazempour-Liasi, H., Tajally, M. & Abdollah-Pour, H. Liquation cracking in the heat-affected zone of IN939 superalloy tungsten inert gas weldments. Int J Miner Metall Mater 27, 764–773 (2020). https://doi.org/10.1007/s12613-019-1954-y

Download citation

  • Received:

  • Revised:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s12613-019-1954-y

Keywords

Navigation