Correction to: JOM, Vol. 71, No. 10, 2019 https://doi.org/10.1007/s11837-019-03715-1
The authors regret that the following mistakes were made.
-
1.
Caption of Fig. 2. The caption should read: Fig. 2. EBSD IPF (a, c) and PF (b, d) maps taken from as-built FCC Al0.3CoCrFeNi prepared using SLM, highlighting the <110> fiber texture towards the sample build direction: (a, b) the plane of the map is perpendicular to the build direction and (c, d) parallel. IPF color-codes with respect to build-up direction (a) and tensile testing direction (c).
-
2.
Caption of Fig. 3. The caption should read: Fig. 3. (a) Optical image showing the columnar cells and the traces of the melt pools observed in a plane parallel to the build direction. (b) Low-magnification EBSD IPF map showing random crystal orientation along tensile testing direction. The black frame indicates the size of the optical micrograph shown in (a).
-
3.
Table S1. 13 µm should be replaced by 12 µm. Table S1. should appear as below:
As-cast | Recrystallized | As-built LBM | |
---|---|---|---|
\( \sigma_{y}^{\exp } \) (MPa) | 275 | 149 | 730 |
σ0 (MPa) | 172 | 172 | 172 |
ky (MPa/m1/2) | 0.73 | 0.73 | 0.73 |
D (μm) | 50 | 100 | 12 |
σgb (MPa) | 103 | 73 | 211 |
σ0 + σgb (MPa) | 275 | 245 | 383 |
M | 3.3 | ||
alpha | 0.2 | ||
G (GPa) | 83-88 | ||
b (nm) | 0.254 | ||
rho (m/m3) | 3–7.1014 | ||
σd (MPa) | 241–392 | ||
\( \sigma_{y}^{\text{estimate}} \,\left( {\text{MPa}} \right) \) | 275 | 245 | 624–775 |
We apologize to the readers for any inconvenience.
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Peyrouzet, F., Hachet, D., Soulas, R. et al. Correction to: Selective Laser Melting of Al0.3CoCrFeNi High Entropy Alloy: Printability, Microstructure, and Mechanical Properties. JOM 72, 3705 (2020). https://doi.org/10.1007/s11837-020-04149-w
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11837-020-04149-w