Abstract
Laser beam offset welding of GH3128 and molybdenum (Mo) dissimilar joints was studied with an emphasis on the role of laser beam offset (LBO). It was found that the change of LBO significantly affected the properties of GH3128/Mo dissimilar joints. When the LBO increased from − 0.1 mm (i.e., laser spot was centered on Mo surface) to + 0.3 mm (i.e., laser spot was centered on GH3128 surface) at the step size of 0.1 mm, the amount of melted Mo gradually declined; the welding mode gradually changed from fusion welding to welding–brazing; macro-segregation of Mo-rich phases in fusion zone (FZ) gradually disappeared; the average microhardness of FZ significantly decreased, and therefore, microhardness distribution in FZ became more uniformly; the quantity of grain boundary liquation observed in heat-affected zone (HAZ) of GH3128 side gradually decreased; and recrystallization of grains in the HAZ of Mo was gradually suppressed. Joints with the optimal LBO of + 0.2 mm reached the maximum tensile strength of about 560 MPa. When using a small LBO, i.e., LBOs were + 0.1, 0, − 0.1 mm, the HAZ of Mo was greatly softened and embrittled. When adopting a large LBO, i.e., LBO was + 0.3 mm, the melt near Mo-FZ interface might fail to moisten Mo surface and spread on Mo surface, thus resulting in the reduction in tensile strength.
Similar content being viewed by others
References
X. Qu, X. Yang, J. Wang et al., Combined Cycle Schemes Coupled with a Very High Temperature Gas-Cooled Reactor, Prog. Nucl. Energy, 2018, 108, p 1–10
W. Kim, S. Yin, Y. Kim et al., Creep Behaviour and Long-Term Creep Life Extrapolation of Alloy 617 for a Very High Temperature Gas-Cooled Reactor, Trans. Indian Inst. Met., 2010, 63, p 145–150
H. Shah-Hosseini, M. Shamanian, and A. Kermanpur, Microstructural and Weldability Analysis of Inconel 617/AISI, 310 Stainless Steel Dissimilar Welds, Int. J. Press. Vessel. Pip., 2016, 144, p 18–24
X. Wang, A. Dallemagne, Y. Hou et al., Influence of Thermomechanical Processing on Grain Boundary Character Distribution of Hastelloy X Alloy, Mater. Sci. Eng., A, 2016, 669, p 95–102
K. Yuan, X. Zhao, P. Ye et al., Methodology for Determining High Temperature Tensile Design Allowable Strengths of Alloy GH3128, Journal of Tsinghua University, 2014, 54, p 1236–1239
G. Liu, G.J. Zhang, F. Jiang et al., Nanostructured High-Strength Molybdenum Alloys with Unprecedented Tensile Ductility, Nat. Mater., 2013, 12, p 344–350
L.J. Zhang, J.Y. Pei, L.L. Zhang et al., Laser Seal Welding of End Plug to Thin-Walled Nanostructured High-Strength Molybdenum Alloy Cladding with a Zirconium Interlayer, J. Mater. Process. Technol., 2019, 267, p 338–347
J.K. Hong, J.H. Park, N.K. Park et al., Microstructures and Mechanical Properties of Inconel 718 Welds by CO2 Laser Welding, J. Mater. Process. Technol., 2008, 201, p 515–520
H. Zhang et al., Effects of the Electron Beam Welding Process on the Microstructure, Tensile, Fatigue and Fracture Properties of Nickel Alloy Nimonic 80A, J. Mater. Eng. Perform., 2018, 27, p 89–98
K.H. Song, W.Y. Kim, and K. Nakata, Evaluation of Microstructures and Mechanical Properties of Friction Stir Welded Lap Joints of Inconel 600/SS 400, Mater. Des., 2012, 35, p 126–132
L. Hsuan-Liang et al., Effects of Flux Precoating and Process Parameter on Welding Performance of Inconel 718 Alloy TIG Welds, J. Mater. Eng. Perform., 2014, 23, p 125–132
G. Yan, B. Nagarajan, A. Bhowmik et al., Induction Transient Liquid Phase Bonding of Inconel 718 with the Nickel-Based Sintered Brazing Preform, Appl. Surf. Sci., 2018, 473, p 1024–1037
G. Chen, J. Liu, X. Shu et al., Study on Microstructure and Performance of Molybdenum Joint Welded by Electron Beam, Vacuum, 2018, 154, p 1–5
P. Liu, K.Y. Feng, and G.M. Zhang, A Novel Study on Laser Lap Welding of Refractory Alloy 50Mo–50Re of Small-Scale Thin Sheet, Vacuum, 2017, 136, p 10–13
T. Wang, N. Li, Y. Zhang et al., Influence of Welding Speed on Microstructures and Mechanical Properties of Vacuum Electron beam Welded TZM Alloy Joints, Vacuum, 2018, 149, p 29–35
L.J. Zhang, J.Z. Liu, Q.L. Bai et al., Effect of Preheating on the Microstructure and Properties of Fiber Laser Welded Girth Joint of Thin-Walled Nanostructured Mo Alloy, Int. J. Refract. Met. Hard Mater., 2019, 78, p 219–227
J. Ning, K.M. Hong, G.V. Inamke et al., Analysis of Microstructure and Mechanical Strength of Lap Joints of TZM Alloy Welded by a Fiber Laser, J. Manuf. Process., 2019, 39, p 146–159
L.L. Zhang, L.J. Zhang, J. Long et al., Effects of Titanium on Grain Boundary Strength in Molybdenum Laser Weld Bead and Formation and Strengthening Mechanisms of Brazing Layer, Mater. Des., 2019, 169, p 107681
Z. Sun and J.C. Ion, Laser Welding of Dissimilar Metal Combinations, J. Mater. Sci., 1995, 30, p 4205–4214
Y. Zhang et al., Microstructure and Mechanical Property Improvement in Laser-Welded TC4 Titanium Alloy and 301L Stainless Steel Joints Without Filler Metal, J. Mater. Eng. Perform., 2018, 28, p 140–153
M.J. Torkamany, F. Malek Ghaini, and R. Poursalehi, An Insight to the Mechanism of Weld Penetration in Dissimilar Pulsed Laser Welding of Niobium and Ti–6Al–4V, Opt. Laser Technol., 2016, 79, p 100–107
G. Casalino, P. Guglielmi, V.D. Lorusso et al., Laser Offset Welding of AZ31B Magnesium Alloy to 316 Stainless Steel, J. Mater. Process. Technol., 2017, 242, p 49–59
L.J. Zhang, G.F. Lu, J. Ning et al., Effects of Minor Zr Addition on the Microstructure and Mechanical Properties of Laser Welded Dissimilar Joint of Titanium and Molybdenum, Mater. Sci. Eng., A, 2019, 742, p 788–797
G. Chen, Q. Yin et al., Beam Deflection Effects on the Microstructure and Defect Creation on Electron Beam Welding of Molybdenum to Kovar, J. Mater. Process. Technol., 2019, 267, p 280–288
X. Gao, L. Li, J. Liu et al., Effect of Laser Offset on Microstructure and Mechanical Properties of Laser Welding of Pure Molybdenum to Stainless Steel, Int. J. Refract Metal Hard Mater., 2020, 88, p 105186
L.J. Zhang, C.H. Wang, Y.B. Zhang et al., The Mechanical Properties and Interface Bonding Mechanism of Molybdenum/SUS304L by Laser Beam Welding with Nickel Interlayer, Mater. Des., 2019, 182, p 108002
J.P. Oliveira, Z. Zeng, C. Andrei et al., Dissimilar Laser Welding of Superelastic NiTi and CuAlMn Shape Memory Alloys, Mater. Des., 2017, 128, p 166–175
S. Chen, J. Huang, J. Xia et al., Influence of Processing Parameters on the Characteristics of Stainless Steel/Copper Laser Welding, J. Mater. Process. Technol., 2015, 222, p 43–51
S. Chen, J. Huang, J. Xia et al., Microstructural Characteristics of a Stainless Steel/Copper Dissimilar Joint Made by Laser Welding, Metall. Mater. Trans. A, 2013, 44, p 3690–3696
T. Soysal, S. Kou, D. Tat et al., Macrosegregation in Dissimilar-Metal Fusion Welding, Acta Mater., 2016, 110, p 149–160
I. Tomashchuk, P. Sallamand, and J.M. Jouvard, The Modeling of Dissimilar Welding of Immiscible Materials by Using a Phase Field Method, Appl. Math. Comput., 2013, 219, p 7103–7114
A. Duan, and C. Li. Characteristics of keyhole and molten pool during laser welding of TC4 Ti-alloy. Proceedings of the 36th International MATADOR Conference. Springer, London, 2010.
P. Paradis, T. Ishikawa, and S. Yoda, Surface Tension and Viscosity of Liquid and Undercooled Tantalum Measured by a Containerless Method, J. Appl. Phys., 2005, 97, p 1010
P. Paradis, T. Ishikawa, and S. Yoda, Viscosity of Liquid Undercooled Tungsten, J. Appl. Phys., 2005, 97, p 565
W.I. Cho et al., Numerical Simulation of Molten Pool Dynamics in High Power Disk Laser Welding, J. Mater. Process. Technol., 2012, 212(1), p 262–275
A. Duan, and C. Li . Characteristics of keyhole and molten pool during laser welding of TC4 Ti-alloy, Proceedings of the 36th International MATADOR Conference. Springer, London, 2010, p 591–594
F. Yan, S. Liu, C. Hu et al., Liquation Cracking Behavior and Control in the Heat Affected Zone of GH909 Alloy During Nd: YAG Laser Welding, J. Mater. Process. Technol., 2017, 244, p 44–50
X.L. Chen, H.G. Yan, J.H. Chen et al., Effects of Grain Size and Precipitation on Liquation Cracking of AZ61 Magnesium Alloy Laser Welding Joints, Sci. Technol. Weld. Join., 2013, 18, p 458–465
F. Yan, C. Hu, X. Zhang et al., Influence of Heat Input on HAZ Liquation Cracking in Laser Welded GH909 Alloy, Opt. Laser Technol., 2017, 92, p 44–51
J. Sabbaghzadeh, M. Azizi, and M.J. Torkamany, Numerical and Experimental Investigation of Seam Welding with a Pulsed Laser, Opt. Laser Technol., 2008, 40, p 289–296
Acknowledgment
This work was supported by the National Natural Science Foundation of China (Grant No. 51775416) and National Thousand Talents Program of China (Grant No. WQ2017610446). The authors would thank teachers at Instrument Analysis Center of Xi’an Jiaotong University for their assistance with SEM and EBSD analysis. Jinduicheng Molybdenum Group Co., Ltd., is thanked for providing the materials.
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Zhang, LJ., Guo, Q., Zhang, YB. et al. Microstructure and Performance of Laser-Welded GH3128/Mo Dissimilar Joints. J. of Materi Eng and Perform 29, 1792–1809 (2020). https://doi.org/10.1007/s11665-020-04721-0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11665-020-04721-0