Destructive and Nondestructive Evaluation of Dry Spots in Thick Glass Fiber Reinforced Composites

  • Published:
Applied Composite Materials Aims and scope Submit manuscript

Abstract

This article reports on the destructive and nondestructive evaluation of dry spots or patches in thick unidirectional glass/epoxy laminates. Dry spots in composites can act as weak regions potentially resulting in catastrophic failure if undetected. Composite samples with dry spots were fabricated and nondestructive evaluation was first carried out using non-contact air coupled ultrasonics. Two types of dryness were investigated: surface and mid-plane dryness. Both types were tested using two ultrasonic testing methods. The ultrasonic velocity was used to determine stiffness and dryness fraction maps. The results showed that the dryness could be detected and characterized using the ultrasonic nondestructive evaluation. To validate the results, a destructive analysis was carried out by cutting the sample into small pieces and burning them to obtain the weight of matrix and fibers. This was further used in micromechanics models to obtain void and dryness fractions. Both model and ultrasonic results show that dry spots result in spatial gradient of mechanical properties around the dry spot. Nondestructive characterization of dryness helps in deciding if the part must be scrapped or repaired based on the severity in terms of loss of stiffness.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10

Similar content being viewed by others

References

  1. Scott, I.G., Scala, C.M.: A review of non-destructive testing of composite materials. NDT Int. 15, 75–86 (1982)

    Article  Google Scholar 

  2. Jolly, M.R., Prabhakar, A., Sturzu, B., Hollstein, K., Singh, R., Thomas, S., Foote, P., Shaw, A.: Review of non-destructive testing (NDT) techniques and their applicability to thick walled composites. Procedia CIRP. 38, 129–136 (2015)

    Article  Google Scholar 

  3. Birt, E.A., Smith, R.A.: A review of NDE methods for porosity measurement in fibre-reinforced polymer composites. Insight-Non-Destruct. Test. Cond. Monitor. 46, 681–686 (2004)

    Article  Google Scholar 

  4. Kumar, A., Shukla, M.: Race tracking and related issues in liquid composite Moulding process. J. Manuf. Sc. Prod. 14, 209–217 (2014)

    Google Scholar 

  5. Kueh, S.R.M., Parnas, R.S., Advani, S.G.: A methodology for using long-period gratings and mold-filling simulations to minimize the intrusiveness of flow sensors in liquid composite molding. Compos. Sci. Technol. 62, 311–327 (2002)

    Article  Google Scholar 

  6. Minaie, B., Chen, Y.F.: Adaptive control of filling pattern in resin transfer molding process. J. Compos. Mater. 39, 1497–1513 (2005)

    Article  Google Scholar 

  7. Hegg, M.C., Ogale, A., Mescher, A., Mamishev, A.V., Minaie, B.: Remote monitoring of resin transfer molding processes by distributed dielectric sensors. J. Compos. Mater. 39, 1519–1539 (2005)

    Article  Google Scholar 

  8. Yildiz, M., Ozdemir, N.G., Bektas, G., Keulen, C.J., Boz, T., Sengun, E.F., Ozturk, C., Menceloglu, Y.Z., Suleman, A.: An experimental study on the process monitoring of resin transfer molded composite structures using fiber optic sensors. J. Manuf. Sci. Eng. 134, 044502 (2012)

    Article  Google Scholar 

  9. Dominauskas, A., Heider, D., Gillespie, J.W.: Electric time-domain reflectometry sensor for online flow sensing in liquid composite molding processing. Compos. A: Appl. Sci. Manuf. 34, 67–74 (2003)

    Article  Google Scholar 

  10. Konstantopoulos, S., Fauster, E., Schledjewski, R.: Monitoring the production of FRP composites: a review of in-line sensing methods. Express Polym Lett. 8, (2014)

  11. Martin, B.G.: Ultrasonic attenuation due to voids in fibre-reinforced plastics. NDT Int. 9, 242–246 (1976)

    Article  Google Scholar 

  12. Martin, B.G.: Ultrasonic wave propagation in fiber-reinforced solids containing voids. J. Appl. Phys. 48, 3368–3373 (1977)

    Article  Google Scholar 

  13. Jeong, H., Hsu, D.K.: Experimental analysis of porosity-induced ultrasonic attenuation and velocity change in carbon composites. Ultrasonics. 33, 195–203 (1995)

    Article  Google Scholar 

  14. Lin, L., Zhang, X., Chen, J., Mu, Y., Li, X.: A novel random void model and its application in predicting void content of composites based on ultrasonic attenuation coefficient. Appl. Phys. A Mater. Sci. Process. 103, 1153–1157 (2011)

    Article  Google Scholar 

  15. Karabutov, A., Podymova, N.: Quantitative analysis of the influence of voids and delaminations on acoustic attenuation in CFRP composites by the laser-ultrasonic spectroscopy method. Compos. Part B. 56, 238–244 (2014)

    Article  Google Scholar 

  16. Rafiee-Dehkharghani, R., Aref, A., Dargush, G.: Planar stress wave attenuation in plates with circular voids and inclusions. Compos. Part B. 75, 307–318 (2015)

    Article  Google Scholar 

  17. Alvarez-Arenas, T.E.G.: Acoustic impedance matching of piezoelectric transducers to the air. IEEE Trans. Ultrason. Ferroelectr. Freq. Control. 51, 624–633 (2004)

    Article  Google Scholar 

  18. W. A. Grandia and C. M. Fortunko, "NDE applications of air-coupled ultrasonic transducers," in Ultrasonics Symposium, 1995. Proceedings., 1995 IEEE, 1995

  19. Chimenti, D.E.: Review of air-coupled ultrasonic materials characterization. Ultrasonics. 54, 1804–1816 (2014)

    Article  Google Scholar 

  20. Castaings, M., Cawley, P., Farlow, R., Hayward, G.: Single sided inspection of composite materials using air coupled ultrasound. J. Nondestruct. Eval. 17, 37–45 (1998)

    Article  Google Scholar 

  21. Castaings, M., Cawley, P.: The generation, propagation, and detection of lamb waves in plates using air-coupled ultrasonic transducers. J. Acoust. Soc. Am. 100, 3070–3077 (1996)

    Article  Google Scholar 

  22. Chakrapani, S.K., Dayal, V., Barnard, D.: Detection and characterization of waviness in unidirectional GFRP using Rayleigh wave air coupled ultrasonic testing (RAC-UT). Res. Nondestruct. Eval. 24, 191–201 (2013)

    Article  Google Scholar 

  23. Chakrapani, S.K., Padiyar, M.J., Balasubramaniam, K.: Crack detection in full size Cz-silicon wafers using lamb wave air coupled ultrasonic testing (LAC-UT). J. Nondestruct. Eval. 31, 46–55 (2012)

    Article  Google Scholar 

  24. Hudson, T.B., Hou, T.-H., Grimsley, B.W., Yuan, F.-G.: Imaging of local porosity/voids using a fully non-contact air-coupled transducer and laser Doppler vibrometer system. Struct. Health Monit. 16, 164–173 (2017)

    Article  Google Scholar 

  25. Huang, H., Talreja, R.: Effects of void geometry on elastic properties of unidirectional fiber reinforced composites. Compos. Sci. Technol. 65, 1964–1981 (2005)

    Article  Google Scholar 

  26. A. K. Kaw, Mechanics of composite materials, CRC press, 2005

  27. E. A. Ash and E. G. S. Paige, Rayleigh-Wave Theory and Application: Proceedings of an International Symposium Organised by The Rank Prize Funds at The Royal Institution, London, 15--17 July, 1985, vol. 2, Springer Science & Business Media, 2012

  28. A. H. Nayfeh, Wave propagation in layered anisotropic media: With application to composites, vol. 39, Elsevier, 1995

  29. Chakrapani, S.K., Dayal, V.: The interaction of Rayleigh waves with delaminations in composite laminates. J. Acoust. Soc. Am. 135(5), 2646–2653 (2014)

    Article  Google Scholar 

  30. Musgrave, M.J.P.: Crystal Acoustics. Holden-Day, San Francisco (1970)

    Google Scholar 

  31. Hagstrand, P.-O., Bonjour, F., Månson, J.-A.E.: The influence of void content on the structural flexural performance of unidirectional glass fibre reinforced polypropylene composites. Compos. A: Appl. Sci. Manuf. 36, 705–714 (2005)

    Article  Google Scholar 

  32. Madsen, B., Lilholt, H.: Physical and mechanical properties of unidirectional plant fibre composites—an evaluation of the influence of porosity. Compos. Sci. Technol. 63, 1265–1272 (2003)

    Article  Google Scholar 

Download references

Acknowledgements

The authors would like to thank Ryan Krafka and Aaron Eldal from Iowa State University for their help in sample preparation, and Ajith Subramaniam for his help with micrographs. The authors would also like to acknowledge the generous support by Momentive Specialty, Stafford, Texas, for providing the epoxy and hardener used in the preparation of samples for this research.

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to Sunil Kishore Chakrapani.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Chakrapani, S.K., Dayal, V. Destructive and Nondestructive Evaluation of Dry Spots in Thick Glass Fiber Reinforced Composites. Appl Compos Mater 26, 693–708 (2019). https://doi.org/10.1007/s10443-018-9744-7

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s10443-018-9744-7

Keywords

Navigation