Crystallographic Orientation Sensitive Measurement of Strain Rate Sensitivity in Zircaloy-2 Via Synchrotron X-ray Diffraction
International Journal of Plasticity ( IF 5.800 ) Pub Date : 2018-09-07 , DOI: 10.1016/j.ijplas.2018.09.003
Travis Skippon, Chris Cochrane, Mark R. Daymond

A series of stress relaxation experiments were performed on samples of rolled Zircaloy-2 plate. In situ synchrotron x-ray diffraction was used to observe changes in interatomic lattice spacing during both deformation and relaxation. The concepts of strain rate sensitivity and activation volume are extended from the macroscopic to the microscopic scale using the results of the diffraction analysis. The technique outlined in this paper allows for the precise measurement of thermally activated properties at the level of subsets of grains sharing similar crystal orientations relative to the loading direction. Self-consistent modelling results are used to connect the observed strain rate sensitivity of these grain families with the rate sensitivities of the various active slip systems in zirconium alloys. The results show that the dependence of strain rate sensitivity on crystal orientation occurs primarily due to the differing strain rate sensitivities of the individual slip systems, which ultimately determines the macroscopic value.
更新日期:2018-09-07

 

全部期刊列表>>
Springer Nature 2019高下载量文章和章节
化学/材料学中国作者研究精选
《科学报告》最新环境科学研究
ACS材料视界
自然科研论文编辑服务
中南大学国家杰青杨华明
剑桥大学-
中南大学
材料化学和生物传感方向博士后招聘
课题组网站
X-MOL
北京大学分子工程苏南研究院
华东师范大学分子机器及功能材料
中山大学化学工程与技术学院
试剂库存
天合科研
down
wechat
bug