Nanocrystalline NiWO 4 -WO 3 -WO 2.9 Composite Strings: Fabrication, Characterization and their Electrocatalytic Performance for Hydrogen Evolution Reaction
Metallurgical and Materials Transactions A ( IF 2.050 ) Pub Date : 2019-12-19 , DOI: 10.1007/s11661-019-05596-0
Shaheen Fatima Anis, Ahmad O. Mostafa, Nidal Hilal, Raed Hashaikeh

In this study, novel nano crystalline composite strings made from mixed nickel-tungsten oxides (NiWO4-WO3-WO2.9) have been fabricated. The NiWO4-WO3 fibers produced by the electrospinning method were post treated in an argon atmosphere at 800 °C which yielded NiWO4-WO3-WO2.9 nanocrystals attached together forming a string-like structure. The presence of WO2.9 phase was confirmed by both the XRD and TEM diffraction pattern analysis. String morphology and structure were found to change with different post treatment conditions such as by changing the calcination temperature from 550 °C under oxygen to 800 °C under pure argon atmosphere. This material was investigated for electrocatalytic hydrogen evolution reaction (HER) in 0.5 M H2SO4 and 0.1 M KOH electrolytes. These composite strings showed good electrocatalytic activity compared to the NiWO4-WO3 fibers reported previously (Anis et al. in J. Mater. Sci. 52:7269–7281, 2017). It was concluded that the presence of WO2.9 phase increases the electrocatalytic activity of the catalyst as compared to the NiWO4-WO3 fibers with overpotentials as low as 40 and 50 mV in 0.5 M H2SO4 and 0.1 M KOH, respectively.
更新日期:2019-12-19

 

全部期刊列表>>
物理学研究前沿热点精选期刊推荐
chemistry
自然职位线上招聘会
欢迎报名注册2020量子在线大会
化学领域亟待解决的问题
材料学研究精选新
GIANT
ACS ES&T Engineering
ACS ES&T Water
ACS Publications填问卷
屿渡论文,编辑服务
阿拉丁试剂right
南昌大学
王辉
南方科技大学
彭小水
隐藏1h前已浏览文章
课题组网站
新版X-MOL期刊搜索和高级搜索功能介绍
ACS材料视界
天合科研
x-mol收录
赵延川
李霄羽
廖矿标
朱守非
试剂库存
down
wechat
bug