An investigation into the effects of HIP after sintering of WC-ZrC-Co-Cr3C2 cemented carbides
International Journal of Refractory Metals & Hard Materials ( IF 2.794 ) Pub Date : 2019-11-28 , DOI: 10.1016/j.ijrmhm.2019.105164
Tomas Soria, Belen Lopez, Lorena Lozada, Steven Moseley, Patricia Alveen, Marc Elsen, Andrea Müller-Grunz, Michael Magin, Ralph Useldinger, Jose M. Sánchez

The sintering behaviour of cemented carbides based on WC-ZrC-Co-Cr3C2 powder mixtures have been analyzed by dilatometric and calorimetric methods for different cobalt contents and WC/ZrC ratios. As expected, powder oxide reduction in these compositions is mainly of carbothermic nature. However, depending on the milling conditions, some highly stable Zr-rich oxides are retained in the binder phase after sintering. Hot isostatic pressing (HIP) cycles have been successfully applied for closing residual porosity after vacuum sintering. For a fixed amount of binder phase and a WC/ZrC ratio, the hardness of these materials depends on the amount of residual porosity and WC grain growth control. The best combination of hardness and toughness is found for alloys with 8 wt%Co and WC/ZrC wt. ratios of 6.46. HIP treatments induce the formation of a compact and well adhered layer mainly comprised of Zr oxides and WC grains. The cobalt binder phase migrates from this layer towards the sample bulk likely due to the loss of wettability on these Zr rich oxides. Hot hardness is higher for the alloy with higher WC/ZrC ratio suggesting that this property depends on both the volume fraction of (ZrxW1-x)C and WC phases and their degree of contiguity.
更新日期:2019-12-11

 

全部期刊列表>>
宅家赢大奖
向世界展示您的会议墙报和演示文稿
全球疫情及响应:BMC Medicine专题征稿
新版X-MOL期刊搜索和高级搜索功能介绍
化学材料学全球高引用
ACS材料视界
x-mol收录
自然科研论文编辑服务
南方科技大学
南方科技大学
西湖大学
中国科学院长春应化所于聪-4-8
复旦大学
课题组网站
X-MOL
深圳大学二维材料实验室张晗
中山大学化学工程与技术学院
试剂库存
天合科研
down
wechat
bug