The Journal of Supercritical Fluids ( IF 3.9 ) Pub Date : 2021-11-12 , DOI: 10.1016/j.supflu.2021.105469 Yaoxin Fan 1 , Shuangming Li 1, 2 , Yongwei Liu 1 , Yiwen Wang 1 , Yujiao Wang 1 , Yanan Chen 1 , Sansan Yu 1, 2
A series of MoVTeNbOx-mixed metal oxides were synthesized by high-pressure hydrothermal method. The effects of temperature and time during the preparation process on the structure and catalytic performance of MoVTeNbOx were investigated. It was demonstrated that high content of M1 phase (94.5%) MoVTeNbOx with typical needle-shape morphology and high surface abundance of V5+ (68.9%) could be fabricated by high-pressure hydrothermal method in a short time (30–60 min) without hydrogen peroxide post-treatment. The catalytic results of propane selective oxidation showed that the MoVTeNbOx sample synthesized at 200 °C for 30 min possessed the highest surface V5+ abundance and largest proportion of terminating (001) plane, displaying the highest selectivity (74.1%) for acrylic acid. Moreover, the prepared MoVTeNbOx showed excellent stability in high temperature continuous reaction.
中文翻译:
高压水热合成具有高表面 V5+ 丰度的 MoVTeNbOx 用于丙烷氧化转化为丙烯酸
采用高压水热法合成了一系列MoVTeNbO x混合金属氧化物。研究了制备过程中温度和时间对MoVTeNbO x结构和催化性能的影响。已经证实,M1相(94.5%)的高含量MoVTeNbO X与典型针状形态学和V的高丰度表面5+(68.9%)可通过高压水热法在短时间内制造(30-60 min) 没有过氧化氢后处理。丙烷选择性氧化的催化结果表明,在 200 °C 下合成 30 min的 MoVTeNbO x样品具有最高的表面 V 5+端(001)平面的丰度和最大比例,对丙烯酸显示出最高的选择性(74.1%)。此外,制备的MoVTeNbO x在高温连续反应中表现出优异的稳定性。