Abstract

Adsorption of conditioning films on a solid surface is the first step in the development of biofilms. With the goal of understanding the preliminary adhesion mechanisms of cyanobacteria on photobioreactor (PBR) materials to prevent biofouling, the physical changes occurring on PBR materials were investigated during the initial adhesion and biofilm formation by Anabaena sp. PCC 7120, a cyanobacterium that is genetically modified to produce linalool. Atomic force microscopy (AFM) revealed that the conditioning film deposition was in the form of spike-like structures on all the materials except PVC. The average heights (in the range 9 − 16 nm) of the conditioning films deposited on glass, PMMA, PC and HDPE were 11 to 20 times higher than on PVC at 96 h. The time dependent change in thickness of conditioning films correlated well with Anabaena cell attachment to the PBR materials. The rapid and significant colonization of Anabaena on glass within 48 h was consistent with the increase in thickness of the conditioning film within this time period. Lack of the conditioning film spike structures and no change in thickness of the conditioning films with time on the PVC together with comparatively delayed cell attachment and conditioning-film protein deposition on this material, indicated that the nanoscale spike structures on the other PBR materials may be accelerating the cell attachment process but are not a prerequisite for cell attachment. These results suggest that PVC should be explored further as an antifouling material for photobioreactors. The thickness of the conditioning films on glass measured by a scratch and scan method was in good agreement with the thickness values measured by an adhesive tape method, indicating that both these methods can be used for fast and reliable AFM thickness determination of bacterial conditioning films.

摘要

Adsorption of conditioning films on a solid surface is the first step in the development of biofilms. With the goal of understanding the preliminary adhesion mechanisms of cyanobacteria on photobioreactor (PBR) materials to prevent biofouling, the physical changes occurring on PBR materials were investigated during the initial adhesion and biofilm formation by Anabaena sp. PCC 7120, a cyanobacterium that is genetically modified to produce linalool. Atomic force microscopy (AFM) revealed that the conditioning film deposition was in the form of spike-like structures on all the materials except PVC. The average heights (in the range 9 − 16 nm) of the conditioning films deposited on glass, PMMA, PC and HDPE were 11 to 20 times higher than on PVC at 96 h. The time dependent change in thickness of conditioning films correlated well with Anabaena cell attachment to the PBR materials. The rapid and significant colonization of Anabaena on glass within 48 h was consistent with the increase in thickness of the conditioning film within this time period. Lack of the conditioning film spike structures and no change in thickness of the conditioning films with time on the PVC together with comparatively delayed cell attachment and conditioning-film protein deposition on this material, indicated that the nanoscale spike structures on the other PBR materials may be accelerating the cell attachment process but are not a prerequisite for cell attachment. These results suggest that PVC should be explored further as an antifouling material for photobioreactors. The thickness of the conditioning films on glass measured by a scratch and scan method was in good agreement with the thickness values measured by an adhesive tape method, indicating that both these methods can be used for fast and reliable AFM thickness determination of bacterial conditioning films.