• A binder-free and freestanding all-climate cathode FeS₂@C/CNT in aluminum-ion batteries working from −25 to 50 °C with exceptional flexibility, enhanced capacity retention (above 117 mAh g⁻¹) and rate capacity even at a low temperature of −25 °C.

• High rate capacity (above 151 mAh g⁻¹ at 2 A g⁻¹) and robust long-term stability (above 80 mAh g⁻¹ after 2,000 cycles at 1 A g⁻¹) at room temperature.

• DFT simulation verifies that the well-designed structure restricts FeS₂ pulverization and facilitates the kinetic process of active ion.

中文翻译：

---

基于无粘合剂 MOF 衍生 FeS2@C/CNT 阴极的全气候铝离子电池

• 铝离子电池中的无粘合剂且独立的全气候正极 FeS _{2 @C/CNT，工作温度范围为 -25 至 50 °C，具有出色的柔韧性、增强的容量保持率（高于 117 mAh g} ^-1）和倍率容量，即使在-25°C的低温。

• 室温下的高倍率容量（在 2 A g ^{-1 下超过 151 mAh g -1 ）}和稳健的长期稳定性（在 1 A g -1 下 2,000 次循环后超过 80 mAh g ^-1）^。

• DFT模拟验证了精心设计的结构限制了FeS ₂的粉碎，促进了活性离子的动力学过程。