Fire Resistance Tests on Prestressed Concrete Box Girder with Intumescent Fire-Retardant Coatings
Fire Technology ( IF 3.4 ) Pub Date : 2021-06-03 , DOI: 10.1007/s10694-021-01145-7
Wei Hou , Gang Zhang , Shuanhai He

The fire resistance of prestressed concrete (PC) structures is seriously affected due to the sensitivity of these structures and significant damage to high temperature. With the continuous improvement of the fire resistance rating of the structures, the fire resistance of PC structures has attracted much attention. According to the relevant research, the reasonable fire protection and heat insulation measures can effectively improve the fire resistance of the PC structures and meet requirements of the fire resistance rating. However, very limited research has been conducted on the effect of intumescent fire-retardant coating (IFC) on the fire resistance of PC structures. Hence, the fire resistance of PC box girder coated with IFC is studied in this paper. Under the combined thermal load and external load, the appearance, thermal response, deflection, prestress variation and fire resistance of the structures under high temperature are measured and compared. The effect of IFC on the fire resistance of PC box girder is preliminarily studied. The test results showed that the IFC can effectively reduce the spalling, bursting and cracking of concrete, effectively prevent concrete structure of reaching very high temperature, significantly reduce the deflection of PC structure at high temperature, and effectively protect the structural prestress. The fire resistance of PC structures can be effectively improved by adopting IFC. In addition, it is found that the fire resistance of PC box girder with high flexural rigidity may be determined by its ultimate bearing capacity rather than its ultimate deflection to high temperature.



中文翻译:

膨胀型防火涂料预应力混凝土箱梁的耐火试验

由于预应力混凝土(PC)结构的敏感性和对高温的显着破坏,这些结构的耐火性受到严重影响。随着结构耐火等级的不断提高,PC结构的耐火性备受关注。根据相关研究,合理的防火隔热措施可以有效提高PC结构的耐火性能,满足耐火等级要求。然而,关于膨胀型防火涂料 (IFC) 对 PC 结构耐火性的影响的研究非常有限。因此,本文对涂有 IFC 的 PC 箱梁的耐火性能进行了研究。在热负荷和外负荷联合作用下,外观、热响应、对结构在高温下的挠度、预应力变化和耐火性能进行了测量和比较。初步研究了IFC对PC箱梁耐火性能的影响。试验结果表明,IFC能有效减少混凝土的剥落、爆裂和开裂,有效防止混凝土结构达到极高温度,显着降低PC结构在高温下的挠度,有效保护结构预应力。采用IFC可以有效提高PC结构的耐火性能。此外,研究还发现,高抗弯刚度PC箱梁的耐火性能可能取决于其极限承载力,而不是其对高温的极限挠度。对结构在高温下的预应力变化和耐火性能进行了测量和比较。初步研究了IFC对PC箱梁耐火性能的影响。试验结果表明,IFC能有效减少混凝土的剥落、爆裂和开裂,有效防止混凝土结构达到极高温度,显着降低PC结构在高温下的挠度,有效保护结构预应力。采用IFC可以有效提高PC结构的耐火性能。此外,研究还发现,高抗弯刚度PC箱梁的耐火性能可能取决于其极限承载力,而不是其对高温的极限挠度。对结构在高温下的预应力变化和耐火性能进行了测量和比较。初步研究了IFC对PC箱梁耐火性能的影响。试验结果表明,IFC能有效减少混凝土的剥落、爆裂和开裂,有效防止混凝土结构达到极高温度,显着降低PC结构在高温下的挠度,有效保护结构预应力。采用IFC可以有效提高PC结构的耐火性能。此外,研究还发现,高抗弯刚度PC箱梁的耐火性能可能取决于其极限承载力,而不是其对高温的极限挠度。初步研究了IFC对PC箱梁耐火性能的影响。试验结果表明,IFC能有效减少混凝土的剥落、爆裂和开裂,有效防止混凝土结构达到极高温度,显着降低PC结构在高温下的挠度,有效保护结构预应力。采用IFC可以有效提高PC结构的耐火性能。此外,研究还发现,高抗弯刚度PC箱梁的耐火性能可能取决于其极限承载力,而不是其高温极限挠度。初步研究了IFC对PC箱梁耐火性能的影响。试验结果表明,IFC能有效减少混凝土的剥落、爆裂和开裂,有效防止混凝土结构达到极高温度,显着降低PC结构在高温下的挠度,有效保护结构预应力。采用IFC可以有效提高PC结构的耐火性能。此外,研究还发现,高抗弯刚度PC箱梁的耐火性能可能取决于其极限承载力,而不是其对高温的极限挠度。有效防止混凝土结构达到极高温度,显着降低PC结构高温挠度,有效保护结构预应力。采用IFC可以有效提高PC结构的耐火性能。此外,研究还发现,高抗弯刚度PC箱梁的耐火性能可能取决于其极限承载力,而不是其对高温的极限挠度。有效防止混凝土结构达到极高温度,显着降低PC结构高温挠度,有效保护结构预应力。采用IFC可以有效提高PC结构的耐火性能。此外,研究还发现,高抗弯刚度PC箱梁的耐火性能可能取决于其极限承载力,而不是其对高温的极限挠度。

更新日期:2021-06-03
down
wechat
bug