This paper reports the results of the investigation of second order optical nonlinearity, as well as the polarization nonlinear behavior of Zn4B6O13. For experiments samples were prepared by thermal treatment of glass tapes and solid state synthesis. The tapes were obtained by a rapid melt quenching technique. The thermal processes in the glass tapes were investigated by differential thermal analysis. The synthesized materials were studied by X-ray diffraction. For the sample thermally treated at 710°C for 18 h, the remnant polarization up to 0.04 μC/cm2 was measured under an electric field of 49 kV/cm. It was shown that the second harmonic generation intensity of Zn4B6O13 is 1.9 times higher than that of the well-known optical material KH2PO4.
中文翻译:
Zn 4 B 6 O 13的合成及非线性光电特性
摘要
本文报告了Zn 4 B 6 O 13的二阶光学非线性以及偏振非线性行为的研究结果。对于实验,通过玻璃带的热处理和固态合成来制备样品。通过快速熔体淬火技术获得带。通过差热分析研究了玻璃带中的热过程。通过X射线衍射研究合成的材料。对于在710°C下热处理18小时的样品,在49 kV / cm的电场下测量了高达0.04μC/ cm 2的残余极化。结果表明,Zn 4 B 6 O的二次谐波产生强度图13的结构比公知的光学材料KH 2 PO 4高1.9倍。