Life-Extending Benefit of Chip Sealing for Pavement Preservation
Transportation Research Record: Journal of the Transportation Research Board ( IF 1.7 ) Pub Date : 2021-01-29 , DOI: 10.1177/0361198121989721
Farhang Jalali 1 , Adriana Vargas-Nordcbeck 2
Affiliation  

Chip seals are effective pavement preservation treatments that are usually applied to address non-fatigue cracking, weathering, and raveling, to seal the surface, to delay oxidation, and, finally, to improve skid resistance. This study used field performance data of test sections from the Pavement Preservation Group Study being conducted by the National Center for Asphalt Technology and the Minnesota DOT’s Road Research Facility. Data from test sections located in a low-traffic-volume road with a hot, wet, no-freeze climate collected over a period of 7 years were used to evaluate the effect of several chip seal treatments. Treatments range from single layer to multilayer systems, and include different construction techniques such as rejuvenating scrub seal and fiber membrane. Also, a section was crack sealed before the application of a single layer chip seal to assess the benefits. A semi-parametric survival analysis was performed to determine the differences in median time to failure (MTTF) for different chip seal sections versus a controlled section—representing a “do-nothing” scenario. The results showed that the MTTF for a single layer chip seal ranges from 6.8 to 9.1 years depending on the pretreatment condition. Crack sealing before chip seal could extend the MTTF by an additional 1–3 years, depending on initial conditions. Double and triple layer chip seals extend the MTTF beyond 10 years. Finally, the scrub seal provided the highest benefits, with survival rates close to 100% after 10 years of performance.



中文翻译:

碎屑密封剂在延长路面寿命方面的优势

切屑密封是有效的路面养护处理方法,通常用于解决非疲劳开裂,风化和撕裂,密封表面,延缓氧化并最终改善防滑性。这项研究使用了由国家沥青技术中心和明尼苏达州交通部的道路研究设施进行的“路面养护小组研究”的测试部分的现场性能数据。来自位于低流量的道路上的测试部分的数据,在7年的时间内收集了炎热,潮湿,无冻结的气候,用于评估几种芯片密封处理的效果。处理范围从单层到多层系统,并包括不同的构造技术,例如使磨砂密封和纤维膜恢复活力。也,在应用单层芯片密封以评估其益处之前,先将一个部分进行裂缝密封。进行了半参数生存分析,以确定不同芯片密封部分与受控部分的平均失效时间(MTTF)的差异,这代表“无所作为”。结果表明,根据预处理条件,单层芯片密封的MTTF为6.8至9.1年。根据初始条件,在芯片密封之前进行裂纹密封可能会使MTTF再延长1-3年。双层和三层芯片密封将MTTF延长了10年以上。最后,磨砂密封件具有最高的效益,在使用10年后,其存活率接近100%。进行了半参数生存分析,以确定不同芯片密封部分与受控部分的平均失效时间(MTTF)的差异,这代表“无所作为”。结果表明,根据预处理条件,单层芯片密封的MTTF为6.8至9.1年。根据初始条件,在芯片密封之前进行裂纹密封可能会使MTTF再延长1-3年。双层和三层芯片密封将MTTF延长了10年以上。最后,磨砂密封件具有最高的效益,在使用10年后,其存活率接近100%。进行了半参数生存分析,以确定不同芯片密封部分与受控部分的平均失效时间(MTTF)的差异,这代表“无所作为”。结果表明,根据预处理条件,单层芯片密封的MTTF为6.8至9.1年。根据初始条件,在芯片密封之前进行裂纹密封可能会使MTTF再延长1-3年。双层和三层芯片密封将MTTF延长了10年以上。最后,磨砂密封件具有最高的效益,在使用10年后,其存活率接近100%。8至9.1年,具体取决于预处理条件。根据初始条件,在芯片密封之前进行裂纹密封可能会使MTTF再延长1-3年。双层和三层芯片密封将MTTF延长了10年以上。最后,磨砂密封件具有最高的效益,在使用10年后,其存活率接近100%。8至9.1年,具体取决于预处理条件。根据初始条件,在芯片密封之前进行裂纹密封可能会使MTTF再延长1-3年。双层和三层芯片密封将MTTF延长了10年以上。最后,磨砂密封件具有最高的效益,在使用10年后,其存活率接近100%。