Evaluation of residual creep life of steels using macro-pillar creep testing and Omega method
Measurement ( IF 3.364 ) Pub Date : 2021-01-10 , DOI: 10.1016/j.measurement.2021.108991
Xiaocheng Zhang; Guoyao Chen; Wulin Wang; Jiru Zhong; Qiongqi Wang; Tong Xu; Kaishu Guan

Residual creep life evaluation is an essential part of Fitness-For-Service (FFS) assessment for engineering components operating at elevated temperatures. This paper elaborates a new evaluation approach based on macro-pillar compression testing (MPCT) and Omega method. The MPCT creep test was performed at the same stress level as the tensile creep test by adjusting the testing load using an algorithm, which is also provided in this paper. The barreling effect of MPCT creep test was corrected by two proposed parameters, which were calibrated using finite element method with 6 types of Cr-Mo alloys from API 579. Finally, a 1.25Cr-0.5Mo-Si steel was prepared for both MPCT and round bar tensile creep tests at 550 ℃ and different initial stress levels. The predicted residual creep life by MPCT has an error of 2.2% at 140 MPa, 6.4% at 160 MPa and 13.5% at 180 MPa.



中文翻译:

使用宏观柱蠕变测试和Omega方法评估钢的残余蠕变寿命

残余蠕变寿命评估是针对在高温下运行的工程组件进行的适航性(FFS)评估的重要组成部分。本文阐述了一种基于宏柱压缩测试(MPCT)和Omega方法的新评估方法。MPCT蠕变测试是在与拉伸蠕变测试相同的应力水平下进行的,方法是使用算法调整测试负载,该算法也在本文中提供。通过建议的两个参数校正了MPCT蠕变试验的桶装效果,并使用有限元方法对API 579中的6种Cr-Mo合金进行了标定。最后,为MPCT和1.25制备了1.25Cr-0.5Mo-Si钢。圆棒在550℃和不同初始应力水平下的拉伸蠕变试验。MPCT预测的残余蠕变寿命在140 MPa时的误差为2.2%,在160 MPa和13时的误差为6.4%。

更新日期:2021-01-13
全部期刊列表>>
微生物研究
亚洲大洋洲地球科学
NPJ欢迎投稿
自然科研论文编辑
ERIS期刊投稿
欢迎阅读创刊号
自然职场,为您触达千万科研人才
spring&清华大学出版社
城市可持续发展前沿研究专辑
Springer 纳米技术权威期刊征稿
全球视野覆盖
施普林格·自然新
chemistry
物理学研究前沿热点精选期刊推荐
自然职位线上招聘会
欢迎报名注册2020量子在线大会
化学领域亟待解决的问题
材料学研究精选新
GIANT
ACS ES&T Engineering
ACS ES&T Water
屿渡论文,编辑服务
阿拉丁试剂right
上海中医药大学
清华大学
复旦大学
南科大
北京理工大学
上海交通大学
隐藏1h前已浏览文章
课题组网站
新版X-MOL期刊搜索和高级搜索功能介绍
ACS材料视界
王鹏
武汉大学
浙江大学
天合科研
x-mol收录
试剂库存
down
wechat
bug