SOLID PARTICLE EROSIVE WEAR BEHAVIOR OF Sol–Gel-DERIVED AA2024 THERMAL BARRIER COATINGS
Surface Review and Letters ( IF 1.1 ) Pub Date : 2020-10-17 , DOI: 10.1142/s0218625x20500511
DIPAK KUMAR 1 , K. N. PANDEY 2
Affiliation  

Solid particle erosion behavior of non-conventional thermal barrier coatings prepared by dip coating of sol–gel 7[Formula: see text]wt.% yttria-stabilized zirconia (7YSZ) has been studied in the present paper. The purpose was to show its applicability to protect aeronautic bodies vulnerable under solid particle impact, e.g. the leading edges of the wings, the radome or the leading edges of rotor blades. The effect of operational variables on erosion rate is studied both for uncoated AA2024-T351 substrate and sol–gel-derived 7YSZ top-coat on AA2024-T351 substrate. The interactive influence of variables on erosive wear behavior is also systematically studied using an air-jet erosion tester under four different parameters such as temperature (25, 150, 275 and [Formula: see text]C), impact angle ([Formula: see text], [Formula: see text], [Formula: see text] and [Formula: see text]), impact particle velocity (40, 60, 80 and 100[Formula: see text]m/s) and erodent flow rate (2, 3, 4 and 5[Formula: see text]g/min) using L[Formula: see text] Taguchi design of experiments. The optimal experimental parameters were obtained by orthogonal arrays, signal-to-noise ratio (SNR) and analysis of variance (ANOVA) for uncoated and coated aluminum alloys AA2024-T351. The temperature was found to be the most influencing parameter followed by impact angle, impact velocity and erodent flow rate for uncoated samples. For 7YSZ sol–gel coated samples, temperature was the most influencing parameter followed by impact angle, erodent flow rate and impact velocity.

中文翻译:

溶胶-凝胶衍生 AA2024 隔热涂层的固体颗粒侵蚀磨损行为

本文研究了溶胶-凝胶7[公式:见正文]wt.%氧化钇稳定氧化锆(7YSZ)浸涂制备的非常规热障涂层的固体颗粒侵蚀行为。目的是展示其适用于保护易受固体颗粒撞击的航空体,例如机翼前缘、天线罩或转子叶片前缘。对于未涂层的 AA2024-T351 基材和溶胶-凝胶衍生的 7YSZ 面漆在 AA2024-T351 基材上都研究了操作变量对侵蚀速率的影响。在温度(25、150、275 和 [公式:见正文]C)、冲击角([公式:见文本]、[公式:见文本]、[公式:见文]和[公式:见文]),冲击粒子速度(40、60、80和100[公式:见文]m/s)和侵蚀流速(2、3、4和5[公式:见文) ]g/min) 使用 L[公式:见正文] 田口实验设计。通过正交阵列、信噪比 (SNR) 和方差分析 (ANOVA) 获得最佳实验参数,用于未涂层和涂层铝合金 AA2024-T351。发现温度是影响最大的参数,其次是未涂层样品的冲击角、冲击速度和侵蚀流速。对于 7YSZ 溶胶-凝胶涂层样品,温度是影响最大的参数,其次是冲击角、侵蚀流速和冲击速度。见文本]g/min) 使用 L[公式:见文本] 田口实验设计。通过正交阵列、信噪比 (SNR) 和方差分析 (ANOVA) 获得最佳实验参数,用于未涂层和涂层铝合金 AA2024-T351。发现温度是影响最大的参数,其次是未涂层样品的冲击角、冲击速度和侵蚀流速。对于 7YSZ 溶胶-凝胶涂层样品,温度是影响最大的参数,其次是冲击角、侵蚀流速和冲击速度。见文本]g/min) 使用 L[公式:见文本] 田口实验设计。通过正交阵列、信噪比 (SNR) 和方差分析 (ANOVA) 获得最佳实验参数,用于未涂层和涂层铝合金 AA2024-T351。发现温度是影响最大的参数,其次是未涂层样品的冲击角、冲击速度和侵蚀流速。对于 7YSZ 溶胶-凝胶涂层样品,温度是影响最大的参数,其次是冲击角、侵蚀流速和冲击速度。发现温度是影响最大的参数,其次是未涂层样品的冲击角、冲击速度和侵蚀流速。对于 7YSZ 溶胶-凝胶涂层样品,温度是影响最大的参数,其次是冲击角、侵蚀流速和冲击速度。发现温度是影响最大的参数,其次是未涂层样品的冲击角、冲击速度和侵蚀流速。对于 7YSZ 溶胶-凝胶涂层样品,温度是影响最大的参数,其次是冲击角、侵蚀流速和冲击速度。