Russian Journal of Inorganic Chemistry ( IF 2.1 ) Pub Date : 2020-11-17 , DOI: 10.1134/s003602362011008x A. V. Kertman , A. V. Ruseikina
Abstract
A confined region of solid solution exists in BaS−In2S3 system of eutectic type with incongruent melting compounds of BaIn2S4 and Ba2In2S5 composition based on the α modification of In2S3. Compounds BaIn2S4 and Ba2In2S5 melt incongruently at 1330 and 1497 K, crystallize in rhombic syngony with unit cell parameters а = 2.181 nm, b = 2.165 nm, с = 1.311 nm (space group Fddd) and а = 1.317 nm, b = 1.272 nm, с = 1.178 nm (space group Pbca), respectively. Microhardness H = 2470 MPa for BaIn2S4 and 2250 MPa for Ba2In2S5. Coordinates of BaIn2S4–In2S3 eutectics is 76 mol % In2S3, Tm = 1190 K. Solubility of BaS in α-In2S3 at 1070 K reaches 2 mol % BaS. Solubility of BaS in α-In2S3 decreases with temperature and becomes 1 mol % BaS at 870 K.
中文翻译:
BaS–In 2 S 3系统中的相平衡
摘要
在共晶类型的BaS-In 2 S 3系统中存在固溶的受限区域,且基于In 2 S 3的α修饰,BaIn 2 S 4和Ba 2 In 2 S 5组成的熔融化合物不一致。化合物BaIn 2 S 4和Ba 2 In 2 S 5在1330和1497 K时熔融不均匀,在菱形同构中结晶,晶胞参数а= 2.181 nm,b = 2.165 nm,с = 1.311 nm(空间群Fddd)和а= 1.317 nm,b = 1.272 nm,с = 1.178 nm(空间群Pbca)。BaIn 2 S 4的显微硬度H = 2470 MPa,Ba 2 In 2 S 5的显微硬度H = 2250 MPa 。贝恩的坐标2小号4 -In 2小号3个共晶体是76%(摩尔)在2 s ^ 3,Ť米的α-在BAS中的= 1190 K.溶解度2小号3在1070 k达到2周%(摩尔)的BaS。在α-在BAS中的溶解度2小号3随温度降低而在870 K下变为1 mol%BaS。