Russian Journal of Inorganic Chemistry ( IF 2.1 ) Pub Date : 2020-10-30 , DOI: 10.1134/s0036023620100101 I. V. Ivanova , N. A. Zaitseva , R. F. Samigullina , I. V. Baklanova , M. V. Rotermel
Abstract
It has been found that the isomorphic capacity of the Zn2 – 2xNi2xSiO4 solid solution with a willemite structure is 15 mol % Ni. The unit cell parameters of Zn2 – 2xNi2xSiO4 samples in the homogeneity range of the solid solution are nearly independent of the content of dopant х and are close to those of undoped Zn2SiO4. It has been shown that the melting point of Zn2 – 2xNi2xSiO4 decreases with an increase in х from 1512°С for х = 0 to 1455°С for х = 0.15. The UV-Vis absorption spectrum and color coordinates of Zn2 – 2xNi2xSiO4 correspond to the blue range, and the color intensity of the pigment increases with increasing nickel content.
中文翻译:
具有硅锌矿结构的Zn 2 – 2x Ni 2x SiO 4固溶体的合成及晶体化学,热学和光谱化学性质
摘要
已经发现,具有硅锌矿结构的Zn 2 – 2 x Ni 2 x SiO 4固溶体的同晶容量为15 mol%Ni。在固溶体均质性范围内的Zn 2 – 2 x Ni 2 x SiO 4样品的晶胞参数几乎与掺杂剂х的含量无关,并且与未掺杂的Zn 2 SiO 4接近。结果表明,从1512°С开始,Zn 2 – 2 x Ni 2 x SiO 4的熔点随着х的增加而降低。对于х = 0.15,х = 0至1455°С 。Zn 2 – 2 x Ni 2 x SiO 4的紫外可见吸收光谱和色坐标对应于蓝色范围,并且颜料的色强度随镍含量的增加而增加。