Reaction Kinetics, Mechanisms and Catalysis ( IF 1.8 ) Pub Date : 2020-09-10 , DOI: 10.1007/s11144-020-01862-0 Afaf Brik , Sabrina Naama , Toufik Hadjersi , Mohamed El Amine Benamar , Sihem Bouanik , Amar Manseri
In this paper, we report on the photodegradation of methylene blue (MB) using Er2O3-coated silicon nanowires as photocatalyst under UV and visible light irradiation. The silicon nanowires (SiNWs) were synthesized by Ag-assisted electroless etching on which Er was electrodeposited by Chronoamperometric method. The samples were analyzed by scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX) and X-ray diffraction (XRD). The results showed that Er2O3 was uniformly formed on silicon nanowires. The samples showed a high efficiency for the MB photodegradation especially, under UV light irradiation where a degradation rate of 100% was obtained after 90 min.
中文翻译:
Er 2 O 3包覆的硅纳米线作为光催化剂在紫外和可见光照射下对亚甲基蓝的光降解
在本文中,我们报道了使用Er 2 O 3包覆的硅纳米线作为光催化剂在紫外和可见光照射下对亚甲基蓝(MB)的光降解。硅纳米线(SiNWs)是通过银辅助化学蚀刻法合成的,其上通过计时安培法电沉积了Er。通过扫描电子显微镜(SEM),能量色散X射线光谱(EDX)和X射线衍射(XRD)分析样品。结果表明,Er 2 O 3均匀地形成在硅纳米线上。样品表现出较高的MB光降解效率,尤其是在90分钟后紫外线降解率达到100%的UV光照射下。