Investigation of the microstructure evolution and properties of A1050 aluminum alloy during radial-shear rolling using FEM analysis
The International Journal of Advanced Manufacturing Technology ( IF 2.496 ) Pub Date : 2020-05-20 , DOI: 10.1007/s00170-020-05227-8
Yury Gamin, Torgom Akopyan, Alexander Koshmin, Alexander Dolbachev, Alexander Aleshchenko, Sergey Pavlovich Galkin, Boris Alexeyevich Romantsev

In this study, the analysis of influence temperature-velocity parameters of radial-shear rolling (RSR) on structure and properties of A1050 (Al99.5%) aluminum alloy using the finite element modeling was carried out. During RSR process, the nonuniform change in temperature-velocity parameters occurs in the volume of workpiece. The deformation temperature is one of the main influencing parameters. The gradient of temperature change over section is almost independent of the initial heating temperature of workpiece, and it increases with growth of rotary velocity. In the surface layer, the temperature and strain rate can vary over a wide range due to the deformation temperature and friction on the contact surface. With that, the change in temperature of the rod central zone occurs monotonically and, mainly, due to the energy of plastic deformation. The increasing in strain rate leads to the intense heating of surface layers of workpiece in deformation zone and the decreasing in temperature oscillations between deformation cycles. After RSR the rods with gradient structure and ultrafine surface layer with a microhardness of up to 43 HV were obtained. Depending on the selected temperature-velocity parameters, it is possible to obtain a different combination of mechanical properties (UTS~94…120 MPa; YS~88…110 MPa; δ~1…43.5%). The strength of obtained RSR rods in all regimes is significantly higher than the strength of industrial rods in a hot-pressed condition that shows the application prospect of RSR process as efficient method of controlled plastic deformation of aluminum alloys and obtaining long rods.
更新日期:2020-05-20

 

全部期刊列表>>
如何通过Nature平台传播科研成果
跟Nature、Science文章学绘图
隐藏1h前已浏览文章
课题组网站
新版X-MOL期刊搜索和高级搜索功能介绍
中洪博元
ACS材料视界
x-mol收录
南开大学
朱守非
廖良生
南方科技大学
西湖大学
伊利诺伊大学香槟分校
徐明华
中山大学化学工程与技术学院
试剂库存
天合科研
down
wechat
bug