Solid State Ionics ( IF 3.2 ) Pub Date : 2020-05-08 , DOI: 10.1016/j.ssi.2020.115324 Nguyen Huu Huy Phuc , Hikima Kazuhiro , Muto Hiroyuki , Matsuda Atsunori
Li3−2xMxPS4 (M = Ca or Mg) solid electrolytes were prepared by planetary ball-milling. Solid electrolytes that were amorphous in XRD were obtained with 0 ≤ x ≤ 0.115. A new crystalline phase was detected in samples with x ≥ 0.391. The addition of Ca2+ to the Li3PS4 matrix (x ≤ 0.115) resulted in reduction of the total conductivity at room temperature but conductivity enhancement was obtained at temperatures of 50 °C or higher. The sample Li2.88Ca0.06PS4 exhibited conductivity of about 9 mS cm−1 at 90 °C, which was much improved compared with the conductivity of intrinsic Li3PS4 (2 mS cm−1).