Ag deposited ZnO (Ag/ZnO) nano materials with different Ag molar content were prepared via chemical precipitation method. The morphology of nano ZnO was rod like, while the size was 170 nm in length and 30 nm in diameter. Silver nanoparticles were found to be spherical with the diameter about 15 nm. When it deposited on the surface of the nano ZnO, the size of the nano ZnO was almost unchanged when the doping amount is 2.5 %. All the samples were treated on cotton fabric, and the laden fabric had excellent performance on hydrophobicity, including UV resistance, antibacterial activity and anti-mildew. The contact angle of fabric loaded with 3 % Ag/ZnO was 139 compare to nano ZnO, which was 103°. The fabric loaded with Ag/ZnO had superior performance of UV resistance. With the increase of depositing amount, the antibacterial rates were promoted; the antibacterial rates against S. aureus, E. coil, and C. albicans of fabric with 3 % Ag/ZnO were promoted to 91 %, 96 % and 98 %. Moreover, Ag/ZnO gave cotton fabrics good anti-mildew performance, especially A. flavus, and its anti-mildew effect could reach 0 grade.

通过化学沉淀法制备了不同Ag摩尔含量的Ag沉积ZnO（Ag / ZnO）纳米材料。纳米ZnO的形态为棒状，尺寸为长170nm，直径30nm。发现银纳米颗粒是直径约15nm的球形。当其沉积在纳米ZnO的表面上时，当掺杂量为2.5％时，纳米ZnO的尺寸几乎不变。所有样品均在棉织物上进行处理，该满载织物具有优异的疏水性，包括抗紫外线性，抗菌活性和防霉性。负载3％Ag / ZnO的织物的接触角为139，而纳米ZnO的接触角为103°。负载有Ag / ZnO的织物具有优异的抗紫外线性能。随着沉积量的增加，抗菌率提高。含3％Ag / ZnO的金黄色葡萄球菌，卷曲大肠杆菌和白色念珠菌的活性分别提高到91％，96％和98％。而且，Ag / ZnO赋予棉织物良好的抗霉性能，尤其是黄曲霉，其抗霉效果达到0级。