Microstructural evolution and superplastic deformation behavior of fine grain 5083Al
Metallurgical and Materials Transactions A ( IF 1.985 ) Pub Date : 1996 , DOI: 10.1007/bf02595632
Peter A Friedman,Amit Kumar Ghosh

The microstructural evolution during superplastic deformation of a fine grain Al-4.7 pct Mg alloy (5083Al) has been studied quantitatively. Starting from an average grain size of 7 µm, grain growth was monitored in this alloy both under static annealing and with concurrent superplastic deformation at a high test temperature of 550°C. Grain size was averaged from measurements taken in longitudinal, transverse, and thickness directions and was found to grow faster during concurrent superplastic deformation than for static annealing. A grain growth law based on an additive nature between time-based and strain-based growth behavior was used to quantify the dynamics of concurrent grain growth. The extent of void formation during deformation was quantified as the area fraction of voids on L-S planes. This void fraction, referred to as the cavity area percent, was recorded at several levels of strain for specimens deformed at two different strain rates. A constitutive equation incorporating this grain growth data into the stress-strain rate data, determined during the early part of deformation, was generated and utilized to model the superplastic tensile behavior. This model was used in an effort to predict the stress-strain curves in uniaxial tension under constant and variable strain rate conditions. Particular attention was paid to the effects of a rapid prestrain rate on the overall superplastic response and hardening characteristics of this alloy.
更新日期:2020-01-01

 

全部期刊列表>>
宅家赢大奖
向世界展示您的会议墙报和演示文稿
全球疫情及响应:BMC Medicine专题征稿
新版X-MOL期刊搜索和高级搜索功能介绍
化学材料学全球高引用
ACS材料视界
x-mol收录
自然科研论文编辑服务
南方科技大学
南方科技大学
西湖大学
中国科学院长春应化所于聪-4-8
复旦大学
课题组网站
X-MOL
深圳大学二维材料实验室张晗
中山大学化学工程与技术学院
试剂库存
天合科研
down
wechat
bug