Effects of temperature and shot peening on S-N behavior of a PM Ni-base superalloy UDIMET 720
Metallurgical and Materials Transactions A ( IF 1.985 ) Pub Date : 2004 , DOI: 10.1007/s11661-004-0027-6
Jian-shu Luo,Paul Bowen

Fatigue S-N (stress vs life) curve behavior for a powder metallurgy (PM) Ni-base superalloy UDIMET 720 in both polished and shot-peened surface conditions was investigated at room temperature and 600 °C in air. Tests were carried out under four-point bending at a load ratio of 0.1 and a frequency of 10 Hz. At 600 °C, an offset S-N curve was found for both polished and shot-peened surface conditions. This offset S-N curve is deduced to be controlled by the location of crack nucleation sites. Observations and deductions of crack nucleation sites, crack nucleation life, crack closure, environmental attack, and cyclic softening and hardening have been used to explain the experimental results.
更新日期:2020-01-01

 

全部期刊列表>>
宅家赢大奖
向世界展示您的会议墙报和演示文稿
全球疫情及响应:BMC Medicine专题征稿
新版X-MOL期刊搜索和高级搜索功能介绍
化学材料学全球高引用
ACS材料视界
x-mol收录
自然科研论文编辑服务
南方科技大学
南方科技大学
西湖大学
中国科学院长春应化所于聪-4-8
复旦大学
课题组网站
X-MOL
深圳大学二维材料实验室张晗
中山大学化学工程与技术学院
试剂库存
天合科研
down
wechat
bug