Improvement of Drawability of Titanium-Stabilized Interstitial-Free Steel by Optimization of Process Parameters and Texture
Metallurgical and Materials Transactions A ( IF 1.985 ) Pub Date : 2008 , DOI: 10.1007/s11661-008-9484-7
Kumkum Banerjee,Anil K. Verma,T. Venugopalan

AbstractA detailed study on the effect of cold rolling and annealing temperature on the texture and drawability of Ti-stabilized interstitial-free (IF) steels have been made with a view to achieving high drawability. The presence of shear type and cold-deformation type of textures in the hot bands of 3.8-, 4.3- and 4.5-mm thickness has been attributed to finish rolling below the Ar3 temperature. The 4.5-mm hot band was selected for further studies as it showed a strong γ fiber. Cold rolling of the hot band was done in the range of 60 to 90 pct, followed by batch annealing in the range of 660 °C to 750 °C. For a particular annealing temperature, a maximum in the intensity of $$ {\left\{ {{\text{111}}} \right\}}{\left\langle {{\text{110}}} \right\rangle } $$ component, and in average normal anisotropy, an rm value was observed with the increase in cold reduction, followed by a drop with further cold reduction. The results are discussed in terms of orientation distribution function (ODF), recrystallization behavior, and precipitation of FeTiP, (Ti, Mn) S, and TiC particles. Fine FeTiP-type precipitates in the grains and at the grain boundaries in samples annealed at 660 °C, as well as samples associated with (Ti, Mn)S in samples annealed at 750 °C, were found to be detrimental for the development of beneficial γ fiber and improved drawability, while coarse FeTiP-type precipitates in 80 pct cold-reduced samples annealed at 680 °C and 710 °C resulted in maximum rm values of 2.29 and 2.25, respectively. The dissolution of TiC at an annealing temperature of 750 °C adversely affected drawability due to the solute drag effect of solute carbon. An optimized combination of cold reduction and annealing temperature has been established for achieving a uniform γ fiber along with high rm values.
更新日期:2020-01-01

 

全部期刊列表>>
宅家赢大奖
向世界展示您的会议墙报和演示文稿
全球疫情及响应:BMC Medicine专题征稿
新版X-MOL期刊搜索和高级搜索功能介绍
化学材料学全球高引用
ACS材料视界
x-mol收录
自然科研论文编辑服务
南方科技大学
南方科技大学
舒伟
中国科学院长春应化所于聪-4-8
复旦大学
课题组网站
X-MOL
香港大学化学系刘俊治
中山大学化学工程与技术学院
试剂库存
天合科研
down
wechat
bug