The effect of consolidation temperature on microstructure and mechanical properties in powder metallurgy-processed 2XXX aluminum alloy composites reinforced with SiC particulates
Metallurgical and Materials Transactions A ( IF 1.985 ) Pub Date : 1997 , DOI: 10.1007/s11661-997-0019-4
Keesam Shin,Dongsup Chung,Sunghak Lee

The effects of consolidation temperature on the development of microstructure and resulting mechanical properties of 2XXX aluminum composites were studied in an effort to fabricate composites with enhanced properties. Type 2009 and 2124 aluminum composites reinforced with 15 pct SiC particulates were produced at four different consolidation temperatures, i.e., 560 °C, 580 °C, 600 °C, and 620 °C, followed by extrusion at 450 °C. The 2124 Al-SiCp composites consolidated at 560 °C showed the most homogeneous and the finest microstructures with the best mechanical properties, which were even better than the whisker-reinforced counterparts. All the results of the tensile tests, hardness tests, in situ scanning electron microscope (SEM) observations of the fracture process, and the apparent fracture toughness indicated that the prominent mechanical property improvement observed in the 2124 Al-SiCp was associated largely with the reduction of volume fraction of the detrimental coarse and brittle manganese-containing particles, as well as grain refinement. The detrimental manganese-containing particles that were routinely observed in the 2124 Al-SiC composites were very effectively refined by the reduction of consolidation temperature, and they rather contributed to the overall mechanical properties of the composites through Orowan-type strengthening and grain growth inhibition.
更新日期:2020-01-01

 

全部期刊列表>>
宅家赢大奖
向世界展示您的会议墙报和演示文稿
全球疫情及响应:BMC Medicine专题征稿
新版X-MOL期刊搜索和高级搜索功能介绍
化学材料学全球高引用
ACS材料视界
x-mol收录
自然科研论文编辑服务
南方科技大学
南方科技大学
西湖大学
中国科学院长春应化所于聪-4-8
复旦大学
课题组网站
X-MOL
深圳大学二维材料实验室张晗
中山大学化学工程与技术学院
试剂库存
天合科研
down
wechat
bug