The present study reports the novel synthesis of Zinc nanoparticles (Zn NPs) by thermal decomposition method and its characterisation by Scanning Electron Microscope (SEM), Transmission Electron Microscope (TEM), and X-ray Diffraction Measurements (XRD). Synthesis of Zn NPs was achieved by using thermosetting polymer and zinc salts as precursor. Zn NPs were obtained on calcination at 850 °C for 30 min. SEM study reveals that synthesized nanoparticles are spherical in shape. XRD analysis shows that the Zn NPs formed are low crystalline in nature.

中文翻译：

---

热固性聚合物合成锌纳米粒子的显微研究

本研究报告了通过热分解法合成锌纳米粒子 (Zn NPs) 的新方法，并通过扫描电子显微镜 (SEM)、透射电子显微镜 (TEM) 和 X 射线衍射测量 (XRD) 对其进行表征。Zn NPs 的合成是通过使用热固性聚合物和锌盐作为前体来实现的。Zn NPs 是在 850 °C 下煅烧 30 分钟获得的。SEM 研究表明合成的纳米粒子是球形的。XRD 分析表明，形成的 Zn NPs 本质上是低结晶的。