Fatigue behavior of AW7075 aluminum alloy in ultra-high cycle fatigue region
Materials Science and Engineering: A ( IF 4.081 ) Pub Date : 2020-01-07 , DOI: 10.1016/j.msea.2020.138922
S. Fintová; I. Kuběna; L. Trško; V. Horník; L. Kunz

Advanced electron microscopy methods were used with the aim to explain the differences in the response of strengthened AW 7075 – T6511 aluminum alloy to fatigue loading at 5 Hz and 20 kHz. The shift of the S–N curve to higher number of cycles to fracture for the specimens tested at high frequency was experimentally determined. This effect is not connected with a change of the fatigue crack initiation mechanism and site from the surface to material interior. The absence of slip markings and cracking of primary intermetallic particles on the surface of cycled specimens were characteristic features. A difference in the dislocation density and dislocation arrangement in the vicinity of the fatigue crack initiation sites was shown to be the only observable effect. However, consistent with the strengthened structure of the alloy, no specific dislocation structure due to the cyclic loading was observed, regardless of the loading frequency and stress amplitude.
更新日期:2020-01-07

 

全部期刊列表>>
Springer Nature 2019高下载量文章和章节
化学/材料学中国作者研究精选
《科学报告》最新环境科学研究
ACS材料视界
自然科研论文编辑服务
中南大学国家杰青杨华明
剑桥大学-
中南大学
材料化学和生物传感方向博士后招聘
课题组网站
X-MOL
北京大学分子工程苏南研究院
华东师范大学分子机器及功能材料
中山大学化学工程与技术学院
试剂库存
天合科研
down
wechat
bug