Composition of the Mo-Mo3Si alloys obtained via various methods
International Journal of Refractory Metals & Hard Materials ( IF 2.794 ) Pub Date : 2020-01-07 , DOI: 10.1016/j.ijrmhm.2020.105188
Ivan Gnesin; Boris Gnesin

The phase and chemical composition of an MoSi system alloy with a silicon content of 25 at.% was investigated via scanning electron microscopy, X-ray microanalysis, and X-ray diffraction. The samples were obtained by both sintering and melting of the components. The synthesis of Mo3Si from elemental Mo and Si via a sintering process at ≤1480 °C was significantly less complete than the synthesis of MoSi2, Mo5Si3 silicides via same process. To increase the efficiency of the synthesis, the reaction sintering of Mo3Si should be carried out at significantly higher temperatures than in the cases of MoSi2 and Mo5Si3 silicides synthesis. This offers a sufficiently phase-pure Mo3Si via reaction sintering at temperatures below the solidus. X-ray microanalysis data on Mo3Si chemical composition indicated a Mo3Si exists in a small compositional range. The average silicon content in Mo3Si was <25 at.%. In addition, experimental data indicated that the solubility of silicon in molybdenum may be higher than previously thought. Furthermore, the composition of the melt-quenched samples suggests that the solidus line for a Si solution in Mo may be retrograde.
更新日期:2020-01-07

 

全部期刊列表>>
宅家赢大奖
向世界展示您的会议墙报和演示文稿
全球疫情及响应:BMC Medicine专题征稿
新版X-MOL期刊搜索和高级搜索功能介绍
化学材料学全球高引用
ACS材料视界
x-mol收录
自然科研论文编辑服务
南方科技大学
南方科技大学
西湖大学
中国科学院长春应化所于聪-4-8
复旦大学
课题组网站
X-MOL
深圳大学二维材料实验室张晗
中山大学化学工程与技术学院
试剂库存
天合科研
down
wechat
bug